Results of switching behavior of the improper ferroelectric LuFeO3 are presented. Using a model set of films prepared under controlled chemical and growth-rate conditions, it is shown that defects can reduce the quasi-static switching voltage by up to 40% in qualitative agreement with first-principles calculations. Switching studies show that the coercive field has a stronger frequency dispersion for the improper ferroelectrics compared to a proper ferroelectric such as PbTiO3 . It is concluded that the primary structural order parameter controls the switching dynamics of such improper ferroelectrics.
RESUMO
In this paper we studied the reversal magnetization of La1-x Sr x Fe0.5Cr0.5O3-δ (x = 0, 0.1 and 0.2) samples produced by combustion synthesis. The structural analysis was carried out by x-ray diffraction with Rietveld analysis. These analyses revealed that all samples have an orthorhombic structure with space group Pbnm (62) and that the Sr-doping induces a decrease of the lattice parameter. The x-ray photoelectron spectroscopy analysis indicates that the Sr-doping favor the change of the valence states of the Fe3+ to Fe4+. The magnetization as a function of the temperature reveals an unusual magnetic behavior with a reversal of magnetization. The increase of the Sr content induces a decrease of the temperature where occurs an inversion of the magnetization and do the value of the magnetization at 5 K more negative. This effect is attributed to the increase of the concentration of Fe4+ with increasing of the Sr content. The Fe and Cr with a valence of 4+ act as paramagnetic impurities in the antiferromagnetic lattice and are responsible for the changes in the magnetic behavior.