A raspberry-like SiO2@TiO2 new material supported on functionalized graphene oxide was prepared to reduce titania's band gap value. The material was characterized through different analytical methods such as Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and high-resolution transmission electron microscopy (HR-TEM). The band gap value was studied via UV-Vis absorption spectra and determined through the Kubelka-Munk equation. A theoretical study was also carried out to analyze the interaction between the species.
RESUMO
Catalysts have been widely used in industries and can be optimized by tuning the composition and chemical ordering of the elements involved in the nano-alloy. Among bi-metallic alloys, the Au-Cu system is of particular interest because it exhibits ordered phases at low temperatures. Nevertheless, the temperature at which these ordered structures are formed is totally unknown at the nanoscale. Consequently, to speed up the development of these catalysts, this paper theoretically predicts the structural phase transitions between ordered and disordered phases for the Au-Cu system by using nano-thermodynamics. Following the predictions, the suggested annealing temperatures have been carefully chosen and consequently, Au-Cu ordered nanocubes have been successfully synthesized through a solventless protocol. The results are fully supported by electron microscopy observations.