Anion-Conducting Polymer Electrolyte without Ether Linkages and with Ionic Groups Grafted on Long Side Chains: Poly(Alkylene Biphenyl Butyltrimethyl Ammonium) (ABBA).

In this work we report the synthesis of the new ionomer poly(alkylene biphenyl butyltrimethyl ammonium) (ABBA) with a backbone devoid of alkaline-labile C-O-C bonds and with quaternary ammonium groups grafted on long side chains. The ionomer was achieved by metalation reaction with n-butyllithium of 2-bromobiphenyl, followed by the introduction of the long chain with 1,4-dibromobutane. The reaction steps were followed by 1H-NMR spectroscopy showing the characteristic signals of the Br-butyl chain and indicating the complete functionalization of the biphenyl moiety. The precursor was polycondensed with 1,1,1-trifluoroacetone and then quaternized using trimethylamine (TMA). After the acid catalyzed polycondensation, the stoichiometric ratio between the precursors was respected. The quaternization with TMA gave a final degree of amination of 0.83 in agreement with the thermogravimetric analysis and with the ion exchange capacity of 2.5 meq/g determined by acid-base titration. The new ionomer blended with poly(vinylalcohol) (PVA) or poly(vinylidene difluoride) (PVDF) was also characterized by water uptake (WU) and ionic conductivity measurements. The higher water uptake and ionic conductivity observed with the PVDF blend might be related to a better nanophase separation.

Aliphatic Anion Exchange Ionomers with Long Spacers and No Ether Links by Ziegler-Natta Polymerization: Properties and Alkaline Stability.

In this work we report the synthesis of poly(vinylbenzylchloride-co-hexene) copolymer grafted with N,N-dimethylhexylammonium groups to study the effect of an aliphatic backbone without ether linkage on the ionomer properties. The copolymerization was achieved by the Ziegler-Natta method, employing the complex ZrCl4 (THF)2 as a catalyst. A certain degree of crosslinking with N,N,N',N'-tetramethylethylenediamine (TEMED) was introduced with the aim of avoiding excessive swelling in water. The resulting anion exchange polymers were characterized by 1H-NMR, FTIR, TGA, and ion exchange capacity (IEC) measurements. The ionomers showed good alkaline stability; after 72 h of treatment in 2 M KOH at 80 °C the remaining IEC of 76% confirms that ionomers without ether bonds are less sensitive to a SN2 attack and suggests the possibility of their use as a binder in a fuel cell electrode formulation. The ionomers were also blended with polyvinyl alcohol (PVA) and crosslinked with glutaraldehyde. The water uptake of the blend membranes was around 110% at 25 °C. The ionic conductivity at 25 °C in the OH- form was 29.5 mS/cm.

"Intrinsic" Anion Exchange Polymers through the Dissociation of Strong Basic Groups: PPO with Grafted Bicyclic Guanidines.

We synthesized anion exchange polymers by a reaction of chloromethylated poly(2,6-dimethyl-1,4-phenylene)oxide (PPO) with strongly basic 1,5,7-triazabicyclo[4.4.0]dec-5-ene (TBD). TBD contains secondary and tertiary amine groups in the guanidine portion. To favor the functionalization with the secondary amine, TBD was activated with butyl lithium. The yield of amine formation via the reaction of the benzyl chloride moiety with TBD was 85%. Furthermore, we prepared polymers with quaternary ammonium groups by the reaction of PPO-TBD with CH3I. The synthesis pathways and ionomer structure were investigated by NMR spectroscopy. The thermal decomposition of both ionomers, studied by thermogravimetry, started above 200 °C, corresponding to the loss of the basic group. The ion exchange capacities, water uptake and volumetric swelling are also reported. The "intrinsic" anion conductivity of PPO-TBD due to the dissociation of grafted TBD was in the order of 1 mS/cm (Cl form). The quaternized ionomer (PPO-TBD-Me) showed an even larger ionic conductivity, above 10 mS/cm at 80 °C in fully humidified conditions.