Delignified porous wood as biofilm support for 1,4-dioxane-degrading bacterial consortium.

Delignified porous wood samples were used as carriers for biofilm formation of a bacterial consortium with the ability to degrade 1,4-dioxane (DX). The delignification treatment of the natural wood resulted in higher porosity, formation of macropores, increase in surface roughness and hydrophilicity of the treated wood pieces. These superior properties of two types of treated carriers (respectively, A and B) compared to the untreated wood resulted in 2.19 ± 0.52- and 2.66 ± 0.23-fold higher growth of biofilm. Moreover, analysis of the fatty acid profiles indicated an increase in proportion of the saturated fatty acids during the biofilm formation, characterising an enhancement in rigidity and hydrophobicity of the biofilms. DX initial concentration of 100 mg/L was completely degraded (detection limit 0.01 mg/L) in 24 and 32 h using the treated A and B woods, while only 25.84 ± 5.95% was removed after 32 h using the untreated wood. However, fitting the DX biodegradation data to the Monod model showed a lower maximum specific growth rate for biofilm (0.0276 ± 0.0018 1/h) versus planktonic (0.0382 ± 0.0024 1/h), because of gradual accumulation of inactive cells in the biofilm. Findings of this study can contribute to the knowledge of biofilm formation regarding the physical/chemical properties of biofilm carriers and be helpful to the ongoing research on bioremediation of DX.

Nanocrystalline cellulose derived from spruce wood: Influence of process parameters.

The cellulose nanocrystals (CNCs) were produced from spruce wood using less hazardous and toxic reagents with understanding of influence of process parameters on CNCs properties. This study employed acetosolv pulping followed by alkaline-peroxide bleaching, eliminating highly reactive chemicals such as Na-chlorites and Na-sulfite for cellulose pulp extraction from spruce wood. Cellulose pulp yield of 41.5 ± 0.7 wt% of dry wood was obtained from pulping followed by bleaching treatment. Cellulose pulp was hydrolyzed with 59.0-65.0 wt% sulfuric acid followed by ultrasonic treatment to produce CNCs. CNCs yield of 8.0 ± 3.2 wt% of dry wood was obtained at 65 wt% acid concentration and yield of 25.1 ± 0.7 wt% at 62 wt% acid concentration. The optimization of acid hydrolysis and ultrasonic treatment resulted in CNCs with high aspect ratios (length/width) up to 48.1. It was demonstrated that higher acid concentration requires lower intensity of ultrasonic treatment for CNCs dispersion, and that higher intensity could enhance aspect ratio without impacting the crystallinity index. However, ultrasonic treatment for longer than 5 min led to destruction of the whisker morphology of CNCs. The extracted CNCs possess high crystallinity index of 80.8 ± 1.7 %, low residual hemicellulose (<2.0 %) and lignin (<0.7 %), and high-char content of 26.7 wt% from thermal degradation.