Organometallic control at the nanoscale: a new, one-pot method to decorate a magnetic nanoparticle surface with noble metal atoms.

A novel cascade of reactions is designed to control in situ the deposition of noble metal islands (e.g. Rh) on top of nanoparticles of a 3d metal (e.g. Fe, Co).

Magnetic nanoparticles through organometallic synthesis: evolution of the magnetic properties from isolated nanoparticles to organised nanostructures.

Co and NiFe nanoparticles (2.7 to 3.3 nm mean diameter) of narrow size distribution have been obtained through the decomposition of organometallic precursors in organic solutions of long alkyl chain ligands, namely oleic acid and hexadecylamine. Materials of various volume fractions were produced. The particles have been structurally characterised by WAXS. Both adopt the bulk structure: HCP in the case of cobalt; a mixture of FCC and BCC for NiFe. Their aptitude to self-assemble either on flat supports or in bulk solid state has been investigated by means of TEM and SAXS. This study suggests the crystallisation of the nanoparticles upon solvent evaporation, especially a local FCC arrangement was observed for the NiFe material. Magnetic measurements (SQUID) confirm this tendency. The blocking temperature depends on the metal volume fraction, i.e. on the anisotropy generated by the dipolar couplings (Ki). We show that, for dense samples, the particles of high intrinsic anisotropy, Ku, (Co) still display an individual behaviour while the soft ones (NiFe) display a collective behaviour.

Structure of assemblies of metal nanowires in mesoporous alumina membranes studied by EXAFS, XANES, X-ray diffraction and SAXS.

Mesoporous alumina membranes ("anodic aluminium oxide", or "AAO") are made by anodic oxidation of aluminium metal. These membranes contain hexagonal arrays of parallel non-intersecting cylindrical pores perpendicular to the membrane surface. By varying the anodisation voltage, the pore diameters are controllable within the range 5-250 nm. We have used AAO membranes as templates for the electrochemical deposition of metals within the pores to produce nanowires. These represent assemblies of one-dimensional quantum wires with prospective applications in electronic, optoelectronic and magnetic devices. Detailed characterisation of the structures of these nanowire assemblies on a variety of length scales is essential to understand their physical properties and evaluate their possible applications. We have used EXAFS, XANES, WAXS, high energy X-ray diffraction and SAXS to study their structure and bonding. In this paper we report the results of our studies of four different nanowire systems supported in AAO membranes. These are the ferromagnetic metals iron and cobalt, the superconducting metal tin, and the semiconductor gallium nitride. Iron nanowires in pores of diameter over the range 12 nm-72 nm are structurally very similar to bcc bulk iron. They have a strong preferred orientation within the alumina pores. Their XANES shows significant differences from that of bulk iron, showing that the electronic structure of the iron nanowires depends systematically on their diameter. Cobalt nanowires are composed of a mixture of hcp and fcc phases, but the ratio of the two phases does not depend in a simple way on the pore diameter or preparation conditions. In bulk cobalt, the fcc beta-phase is normally stable only at high temperatures. Strong preferred orientation of the c-axis in the pores was found. Tin nanowires in alumina membranes with pores diameters between 12 nm and 72 nm have a tetragonal beta-structure at ambient temperature and also at 80 K. Magnetic susceptibility measurements show that they are diamagnetic, and become superconducting at the same temperature as bulk tin (3.7 K). Gallium nitride nanowires have been prepared in alumina membranes with pore diameter 24 nm by a novel method. Gallium nitrate was deposited in the pores from aqueous solution and thermolysed at 1000 degrees C to form Ga2O3, which was reacted with ammonia at 1000 degrees C. The GaN nanowires have the wurtzite structure. Preparation at 1150 degrees C led to the incorporation of aluminium in the GaN. The mesoscopic ordering of the pores in the AAO membranes and their filling by metal nanowires has been studied by SAXS, which shows patterns of Bragg peaks arising from the pore arrays. Additionally, the cobalt nanowires have been the subject of an initial ASAXS study.