X-ray Absorption Spectroscopy Study of Thickness Effects on the Structural and Magnetic Properties of Pr2-δNi1-xMn1+xO6-y Double Perovskite Thin Films.

In this work, we report a systematic study of the influence of film thickness on the structural and magnetic properties of epitaxial thin films of Pr2-δNi1-xMn1+xO6-y (PNMO) double perovskite grown on top of two different (001)-SrTiO3 and (001)-LaAlO3 substrates by RF magnetron sputtering. A strong dependence of the structural and magnetic properties on the film thickness is found. The ferromagnetic transition temperature (TC) and saturation magnetization (Ms) are found to decrease when reducing the film thickness. In our case, the thinnest films show a loss of ferromagnetism at the film-substrate interface. In addition, the electronic structure of some characteristic PNMO samples is deeply analyzed using X-ray absorption spectroscopy (XAS) and X-ray magnetic circular dichroism (XMCD) measurements and compared with theoretical simulations. Our results show that the oxidation states of Ni and Mn ions are stabilized as Ni2+ and Mn4+, thus the ferromagnetism is mainly due to Ni2+-O-Mn4+ superexchange interactions, even in samples with poor ferromagnetic properties. XMCD results also make evident large variations on the spin and orbital contributions to the magnetic moment as the film's thickness decreases.

Optimization of the Growth Process of Double Perovskite Pr2-δNi1-xMn1+xO6-y Epitaxial Thin Films by RF Sputtering.

Epitaxial thin films of Pr2-δNi1-xMn1+xO6-y (PNMO) double perovskite were grown on (001)-oriented SrTiO3 substrates by RF magnetron sputtering. The influence of the growth parameters (oxygen pressure, substrate temperature, and annealing treatments) on the structural, magnetic and transport properties, and stoichiometry of the films was thoroughly investigated. It is found that high-quality epitaxial, insulating, and ferromagnetic PNMO thin films can only be obtained in a narrow deposition parameter window. It is shown that a careful selection of the growth conditions allows for obtaining a high degree of Ni/Mn cation ordering, which is reflected in the values of the Curie temperature, TC, and saturation magnetization, MS, which are very close to those of bulk material.

Formation of Nickel Oxide Nanocuboids in Ferromagnetic La2Ni1-xMn1+xO6.

The control of the spontaneous formation of nanostructures at the surface of thin films is of strong interest in many different fields, from catalysts to microelectronics, because surface and interfacial properties may be substantially enhanced. Here, we analyze the formation of nickel oxide nanocuboids on top of La2Ni1-xMn1+xO6 double perovskite ferromagnetic thin films, epitaxially grown on SrTiO3 (001) substrates by radio-frequency (RF) magnetron sputtering. We show that, by annealing the films at high temperature under high oxygen partial pressure, the spontaneous segregation of nanocuboids is enhanced. The evolution of the structural and magnetic properties of the films is studied as a function of the annealing treatments at different temperatures. It is shown that the formation of NiOx nanocuboids leads to a nanostructured film surface with regions of locally different electrical transport characteristics.