RESUMO
Dynamic impact tests using thin metal plates for ballistic characterization have received significant attention in recent years. The Johnson-Cook (J-C) model is extensively used in numerical modeling of impact and penetration in metals. The AISI (American Iron and Steel Institute) 301 steel family presents good impact behavior, excellent formability, and high corrosion resistance. Thus, NICRO (Nickel and Hard Chrome Plated Steel) 12.1 (part of the AISI 301 steel family) was chosen in this work, although parameters of the J-C model or impact results were not found in the literature. In this work, NICRO 12.1 steel plates, were characterized in ballistics with an initial impact velocity up to 200 m/s and three shape nose projectiles. The Johnson-Cook parameters for the NICRO 12.1 steel were calculated for a large range of temperatures and strain rates. Impact tests were carried out using three projectiles: conical, hemispherical, and blunt. The ballistic curves, failure mode, and maximum deformation obtained with each projectile, experimentally and numerically, were compared, and a good correlation was obtained.
RESUMO
This work focuses on the combination of two complementary non-destructive techniques to analyse the final deformation and internal damage induced in aramid composite plates subjected to ballistic impact. The first analysis device, a 3D scanner, allows digitalising the surface of the tested specimen. Comparing with the initial geometry, the permanent residual deformation (PBFD) can be obtained according to the impact characteristics. This is a significant parameter in armours and shielding design. The second inspection technique is based on computed tomography (CT). It allows analysing the internal state of the impacted sample, being able to detect possible delamination and fibre failure through the specimen thickness. The proposed methodology has been validated with two projectile geometries at different impact velocities, being the reaction force history on the specimen determined with piezoelectric sensors. Different loading states and induced damages were observed according to the projectile type and impact velocity. In order to validate the use of the 3D scanner, a correlation between impact velocity and damage induced in terms of permanent back face deformation has been realised for both projectiles studied. In addition, a comparison of the results obtained through this measurement method and those obtained in similar works, has been performed in the same range of impact energy. The results showed that CT is needed to analyse the internal damage of the aramid sample; however, this is a highly expensive and time-consuming method. The use of 3D scanner and piezoelectric sensors is perfectly complementary with CT and could be relevant to develop numerical models or design armours.