Understanding the Influence of Gypsum upon a Hybrid Flame Retardant Coating on Expanded Polystyrene Beads.

A low-cost and effective flame retarding expanded polystyrene (EPS) foam was prepared herein by using a hybrid flame retardant (HFR) system, and the influence of gypsum was studied. The surface morphology and flame retardant properties of the synthesized flame retardant EPS were characterized using scanning electron microscopy (SEM) and cone calorimetry testing (CCT). The SEM micrographs revealed the uniform coating of the gypsum-based HFR on the EPS microspheres. The CCT and thermal conductivity study demonstrated that the incorporation of gypsum greatly decreases the peak heat release rate (PHRR) and total heat release (THR) of the flame retarding EPS samples with acceptable thermal insulation performance. The EPS/HFR with a uniform coating and the optimum amount of gypsum provides excellent flame retardant performance, with a THR of 8 MJ/m2, a PHRR of 53.1 kW/m2, and a fire growth rate (FIGRA) of 1682.95 W/m2s. However, an excessive amount of gypsum weakens the flame retardant performance. The CCT results demonstrate that a moderate gypsum content in the EPS/HFR sample provides appropriate flame retarding properties to meet the fire safety standards.

Expanded Polystyrene Beads Coated with Intumescent Flame Retardant Material to Achieve Fire Safety Standards.

The compatibility and coating ratio between flame retardant materials and expanded polystyrene (EPS) foam is a major impediment to achieving satisfactory flame retardant performance. In this study, we prepared a water-based intumescent flame retardant system and methylene diphenyl diisocyanate (MDI)-coated expandable polystyrene microspheres by a simple coating approach. We investigated the compatibility, coating ratio, and fire performance of EPS- and MDI-coated EPS foam using a water-based intumescent flame retardant system. The microscopic study revealed that the water-based intumescent flame retardant materials were successfully incorporated with and without MDI-coated EPS microspheres. The cone calorimeter tests (CCTs) of the MDI-coated EPS containing water-based intumescent flame retardant materials exhibited better flame retardant performance with a lower total heat release (THR) 7.3 MJ/m2, peak heat release rate (PHRR) 57.6 kW/m2, fire growth rate (FIGRA) 2027.067 W/m2.s, and total smoke production (TSP) 0.133 m2. Our results demonstrated that the MDI-coated EPS containing water-based intumescent flame retardant materials achieved flame retarding properties as per fire safety standards.