2,4-Dichlorophenoxyacetic acid (2,4-D) adsorptive removal by algal magnetic activated carbon nanocomposite.

In the present study, ferric oxide nanoparticles impregnated with activated carbon from Ulva prolifera biomass (UPAC-Fe2O3) were prepared and employed to remove 2,4-Dichlorophenoxyacetic acid (2,4-D) by adsorption. The UPAC-Fe2O3 nanocomposite was characterized for its structural and functional properties by a variety of techniques. The nanocomposite had a jagged, irregular surface with pores due to uneven scattering of Fe2O3 nanoparticles, whereas elemental analysis portrayed the incidence of carbon, oxygen, and iron. XRD analysis established the crystalline and amorphous planes corresponding to the iron oxide and carbon phase respectively. FT-IR analyzed the functional groups that confirmed the integration of Fe2O3 nanoparticles onto nanocomposite surfaces. VSM and XPS studies uncovered the superparamagnetic nature and presence of carbon and Fe2O3, respectively, in the UPAC-Fe2O3 nanocomposite. While the surface area was 292.51 m2/g, the size and volume of the pores were at 2.61 nm and 0.1906 cm3/g, respectively, indicating the mesoporous nature and suitability of the nanocomposites that could be used as adsorbents. Adsorptive removal of 2,4-D by nanocomposite for variations in process parameters like pH, dosage, agitation speed, adsorption time, and 2,4-D concentration was studied. The adsorption of 2,4-D by UPAC-Fe2O3 nanocomposite was monolayer chemisorption owing to Langmuir isotherm behavior along with a pseudo-second-order kinetic model. The maximum adsorption capacity and second order rate constant values were 60.61 mg/g and 0.0405 g/mg min respectively. Thermodynamic analysis revealed the spontaneous and feasible endothermic adsorption process. These findings confirm the suitability of the synthesized UPAC-Fe2O3 nanocomposite to be used as an adsorbent for toxic herbicide waste streams.

As (III) removal using superparamagnetic magnetite nanoparticles synthesized using Ulva prolifera - optimization, isotherm, kinetic and equilibrium studies.

In this study, magnetite nanoparticles (MNPs) were synthesized using the seaweed - Ulva prolifera, an amply found marine source in the Western coastal regions of India. The surface and other properties of MNPs were characterized by many sophisticated methods. Spherical nanoclusters were observed in the FESEM image and iron and oxygen elements were seen in EDS results. XRD peaks were consistent with magnetite standards and MNPs had good crystallinity. FTIR portrayed the specific signals for MNPs and TGA profile ascertained the thermal stability. Magnetic saturation of 41.84 emu/g with negligible hysteresis loop substantiated the superparamagnetism. XPS pointed out the presence of Fe and O with oxidation states specific for MNPs, and the results were consistent with EDS. BET revealed a high specific surface area (144.98 m2/g) of MNPs with mesopores. The synthesized MNPs were used as nanoadsorbent for the removal of As (III) from aqueous solution. The central composite design was used for optimizing As (III) adsorption on MNPs. The optimum conditions were found out as 97.5% at pH: 9, rotation speed: 150 rpm, time: 90 min, and MNPs dosage: 1.15 g/L. The adsorption process fitted in a better way with the Langmuir isotherm and pseudo-second-order model. The highest adsorption capacity was 12.45 mg/g, which is substantially larger than the documenter reports. The spontaneous and endothermic nature of adsorption were ascertained from thermodynamic studies. The results suggested that the synthesized MNPs using the extract of U. prolifera could be alternative nanoadsorbents for eliminating toxic heavy metals from waste streams.

Photocatalytic degradation of methylene blue dye using newly synthesized zirconia nanoparticles.

Zirconium oxide nanoparticles (ZrO2NPs) were prepared using the leaf extract of Muntingia calabura as a reductant. The absorption peak at 232 nm confirmed the signature peak for ZrO2NPs with band energy at 5.07 eV. The ZrO2NPs were tetragonal and highly crystalline, possessing a mean diameter of 14.83 nm as confirmed by XRD studies. The lattice constants (a = 0.362 nm and c = 0.511 nm) were consistent with the literature. Spherical nanoaggregates (29.25 nm) were seen in FESEM image and the specific signals for Zr and O were noticed in EDS image. The tetragonal phase of the ZrO2NPs were further confirmed from the XPS and Raman studies. PL spectrum had a sharp emission at 493 nm. The FTIR spectrum revealed the presence of various functional groups. ZrO2NPs were thermally stable with 5.76% total weight loss - as revealed from TGA profile. The photocatalytic breakdown of methylene blue (MB) dye under the influence of solar irradiation was performed using ZrO2NPs which exhibited 89.11% degradation within 5 h. Hence, the synthesized ZrO2NPs can be used as an alternate potential photocatalyst for the degradation of various dyes present in waste streams.