Mastic asphalt (MA) has been particularly popular in recent years for bridge pavements due to many advantages such as easy application, good waterproofing properties, and high durability. However, the drawback of mastic asphalt in comparison to other asphalt mixtures is its lower resistance to permanent deformation. Trinidad Lake Asphalt (TLA) is often applied to make mastic asphalt resistant to permanent deformation. Practical experience demonstrates that serious failures may occur if MA pavement design and materials selection is not taken into account sufficiently. Therefore in this study, the influence of two parameters: zero shear viscosity (ZSV) of TLA-modified binder and mastic composition described by the filler-binder ratio, on the permanent deformation resistance of the MA mixture was evaluated. The primary purpose of determining the ZSV of the TLA-modified binders was to evaluate the rutting potential of the binders. The permanent deformation (rutting) resistance of the MA mixtures was evaluated based on static and dynamic indentation tests. The optimum content of TLA in the base bitumen and the optimum filler-binder ratio in the MA mixture were obtained based on multiple performance evaluations for modified binder, mastic and MA mixtures, i.e., 20% and 4.0, respectively.
RESUMO
The application of various modifiers has emerged in recent years to improve conventional petroleum-based bitumen properties. The natural asphalt called Trinidad Lake Asphalt (TLA) has been applied very often due to its consistent properties, high viscosity and density, and superior rheological properties, and effective blending with other bitumen. However, most studies on TLA-modified binders always focused on physical and rheological properties in the original (unaged) condition, but the details about aging properties are often neglected. This study aimed to investigate the effect of short-term aging on the physical and rheological characteristics of the 35/50 base bitumen modified by the addition of two different TLA contents. The conventional physical tests and dynamic shear rheological tests were undertaken before and after aging to measure the penetration and softening point, complex shear modulus, and phase angle of the modified binders, as well as to calculate the zero shear viscosity using the Cross model fitting procedure. Based on the results of the above-mentioned comprehensive testing, the effect of aging on TLA-modified binder properties was evaluated using aging indices, as well as a direct comparison of results. The tests revealed that the short-term aging of TLA-modified binders did not worsen or reduce the pavement resistance to permanent deformation or the load-bearing capacity of the asphalt mixture.