RESUMO
Fe-Pd magnetic shape-memory alloys are of major importance for microsystem applications due to their magnetically driven large reversible strains under moderate stresses. In this context, we focus on the synthesis of nanostructured Fe70Pd30 shape-memory alloy antidot array thin films with different layer thicknesses in the range from 20 nm to 80 nm, deposited onto nanostructured alumina membranes. A significant change in the magnetization process of nanostructured samples was detected by varying the layer thickness. The in-plane coercivity for the antidot array samples increased with decreasing layer thickness, whereas for non-patterned films the coercive field decreased. Anomalous coercivity dependence with temperature was detected for thinner antidot array samples, observing a critical temperature at which the in-plane coercivity behavior changed. A significant reduction in the Curie temperature for antidot samples with thinner layer thicknesses was observed. We attribute these effects to complex magnetization reversal processes and the three-dimensional magnetization profile induced by the nanoholes. These findings could be of major interest in the development of novel magnetic sensors and thermo-magnetic recording patterned media based on template-assisted deposition techniques.
RESUMO
The results reported here represent the first direct experimental observations supporting the existence of a solid-to-solid phase transition induced by thermal treatment in magnetic ionic liquids (MILs). The phase transitions of the solid phases of 1,3-dimethylimidazolium tetrachloroferrate, DimimFeCl4, are closely related to its thermal history. Two series of solid-to-solid phase transitions can be described in this MIL: (i) from room temperature (RT) phase II [space group (s.g.) = P21] to phase I-a [s.g. = P212121] via thermal quenching or via fast cooling at T > 2 K min(-1); (ii) from phase I-a to phase I-b [s.g. = P21/c] when the temperature was kept above 180 K for several minutes. The latter involves a slow translational and reorientational dynamical process of both the imidazolium cation and the tetrachloroferrate anion and has been characterized using synchrotron and neutron powder diffraction and DFT (density functional theory) studies. The transition is also related to the modification of the super-exchange pathways of low-temperature phases which show a overall antiferromagnetic behavior. A combination of several experimental methods such as magnetometry, Mössbauer and muon spectroscopy together with polarized and non-polarized neutron powder diffraction has been used in order to characterize the different features observed in these phases.
RESUMO
We present the first magnetic phase of an ionic liquid with anion-π interactions, which displays a three-dimensional (3D) magnetic ordering below the Néel temperature, TN = 7.7 K. In this material, called Dimim[FeBr4], an exhaustive and systematic study involving structural and physical characterization (synchrotron X-ray, neutron powder diffraction, direct current and alternating current magnetic susceptibility, magnetization, heat capacity, Raman and Mössbauer measurements) as well as first-principles analysis (density functional theory (DFT) simulation) was performed. The crystal structure, solved by Patterson-function direct methods, reveals a monoclinic phase (P21 symmetry) at room temperature with a = 6.745(3) Å, b = 14.364(3) Å, c = 6.759(3) Å, and ß = 90.80(2)°. Its framework, projected along the b direction, is characterized by layers of cations [Dimim](+) and anions [FeBr4](-) that change the orientation from layer to layer, with Fe···Fe distances larger than 6.7 Å. Magnetization measurements show the presence of 3D antiferromagnetic ordering below TN with the existence of a noticeable magneto-crystalline anisotropy. From low-temperature neutron diffraction data, it can be observed that the existence of antiferromagnetic order is originated by the antiparallel ordering of ferromagnetic layers of [FeBr4](-) metal complex along the b direction. The magnetic unit cell is the same as the chemical one, and the magnetic moments are aligned along the c direction. The DFT calculations reflect the fact that the spin density of the iron ions spreads over the bromine atoms. In addition, the projected density of states (PDOS) of the imidazolium with the bromines of a [FeBr4](-) metal complex confirms the existence of the anion-π interaction. Magneto-structural correlations give no evidence for direct iron-iron interactions, corroborating that the 3D magnetic ordering takes place via superexchange coupling, the Fe-Br···Br-Fe interplane interaction being defined as the main exchange pathway.
RESUMO
A new magnetic ionic liquid (MIL) with 3D antiferromagnetic ordering has been synthetized and characterized. The information obtained from magnetic characterization was supplemented by analysis of DFT calculations and the magneto-structural correlations. The result gives no evidence for direct iron-iron interactions, corroborating that the 3D magnetic ordering in MILs takes place via super-exchange coupling containing two diamagnetic atoms intermediaries.
RESUMO
The solid state exhibits a fascinating variety of phases, which can be stabilized by the variation of external parameters such as temperature, magnetic field and pressure. Until recently, numerical analysis of magnetic and/or orbital phases with collective excitations on a periodic lattice tended to be done on a case-by-case basis. Nowadays dynamical matrix diagonalization (DMD) has become an important and powerful standard method for the calculation of dispersive modes. The application of DMD to the interpretation of inelastic neutron scattering (INS) data on dispersive magnetic excitations is reviewed. A methodical survey of calculations employing spin-orbit and intermediate coupling schemes is illustrated by examples. These are taken from recent work on rare earth, actinide and transition metal compounds and demonstrate the application of the formalism developed.