Microstructure and Mechanical Properties of Structural Steels and Alloys.

Structural steels and alloys represent a wide domain of materials whose development directly affects human civilization [...].

Regularities of Microstructure Evolution in a Cu-Cr-Zr Alloy during Severe Plastic Deformation.

The effect of severe plastic deformation by the conforming process of equal channel angular extrusion (ECAE-Conform) followed by cold rolling on the microstructures developed in a Cu-0.1Cr-0.1Zr alloy was investigated. Following the ECAE-Conform of 1 to 8 passes (corresponding strains were 0.8 to 6.4) cold rolling to a total strain of 4 was accompanied by substantial grain refinement and strengthening. An average grain size tended to approach 160 nm with an increase in the rolling reduction. An increase in the ECAE-Conform strain promoted the grain refinement during subsequent cold rolling. The fraction of the ultrafine grains with a size of 160 nm after cold rolling to a strain of 4 increased from 0.12 to 0.52 as the number of ECAE-Conform passes increased from 1 to 8. Correspondingly, the yield strength increased above 550 MPa. The strengthening could be expressed by a Hall-Petch type relationship with a grain size strengthening factor of 0.11 MPa m0.5.

Effect of Rotary Swaging on the Structure, Mechanical Characteristics and Aging Behavior of Cu-0.5%Cr-0.08%Zr Alloy.

A study of the effect of rotary swaging (RS) on the microstructure and properties of the pre-extruded and pre-quenched Cu-0.5%Cr-0.08%Zr alloy was performed. RS leads to the formation of an ultrafine-grained (UFG) microstructure. UFG structure formation caused by RS increases the ultimate tensile strength (UTS) up to 443 ± 5 MPa and 597 ± 9 MPa for pre-quenched and pre-extruded alloys, respectively. Additionally, the reduction in ductility occurs after RS. It should be noted that UTS is increased for a pre-quenched alloy, while the strength of a pre-extruded alloy is dropped. The growth of UTS for the pre-quenched alloy is associated with the precipitation of fine Cr particles, whereas the recovery processes in the pre-extruded alloy induce the reduction in its UTS. An additional advantage of RS is an increase in the fatigue limit of the pre-quenched alloy up to 265 MPa, and of the pre-extruded alloy up to 345 MPa. The combination of extrusion and RS allows for the increase of the UTS of the Cu-0.5%Cr-0.08%Zr alloy up to 597 ± 9 MPa, while the levels of ductility and electrical conductivity are 10.9 ± 0.9% and 82.0 ± 1.7% IACS, respectively.