RESUMO
Purposes: The objective of this work was to produce and characterise biodegradable poly (vinyl alcohol) (PVA) nanofibre loaded with green propolis extract (GPE), chitosan (CS) and nystatin (NYS) alone and in mixtures as a potential wound dressing material. Methods: The GPE, NYS and CS1% were loaded in electrospinning compositions based on PVA 7%, 8% and 12% solubilised in milli-Q water or a mixture of water and glacial acetic acid. The electrospinning compositions without actives (blank) and those loaded with actives were characterised by determining the pH, electrical conductivity and rheological properties. An image analysis procedure applied to photomicrographs obtained by scanning electronic microscopy (SEM) allowed the determination of the nanofibres' diameter distribution and average surface porosity. The disintegration time and swelling ratio of the nanofibre mats were also determined. Results: The physicochemical parameters of the electrospinning compositions (pH, electrical conductivity and rheology) and the incorporated active ingredients (GPE, CS and NYS) affected the electrospun nanofibre mats properties. The electrospun nanofibres' mean diameters and surface porosity ranged from 151.5 to 684.5 nm and from 0.29 ± 0.04 to 0.50 ± 0.05. The PVA/CS electrospun nanofibres fibres exhibited the smallest diameters, high surface porosity, water absorption capacity and disintegration time. The characteristics of the PVA/CS nanofibres mat associated with the biodegradability of the polymers make them a novel material with the potential to be applied as wound and burn dressings.
RESUMO
Currently, the inappropriate disposal of plastic materials, such as polyethylene terephthalate (PET) wastes, is a major environmental problem since it can cause serious damage to the environment and contribute to the proliferation of pathogenic microorganisms. To reduce this accumulation, PET-type bottles have been recycled, and also explored in other applications such as the development of membranes. Thus, this research aims to develop electrospun microfiber membranes from PET wastes and evaluate their use as an air filter media. The solution concentrations varied from 20 to 12% wt% of PET wastes, which caused a reduction of the average fiber diameter by 60% (from 3.25 µm to 1.27 µm). The electrospun filter membranes showed high mechanical resistance (4 MPa), adequate permeability (4.4 × 10-8 m2), high porosity (96%), and provided a high collection efficiency (about 100%) and low-pressure drop (212 Pa, whose face velocity was 4.8 cm/s) for the removal of viable aerosol nanoparticles. It can include bacteria, fungi, and also viruses, mainly SARS-CoV-2 (about 100 nm). Therefore, the developed electrospun membranes can be applied as indoor air filters, where extremely clean air is needed (e.g., hospitals, clean zones of pharmaceutical and food industry, aircraft, among others).
RESUMO
Air pollution and solid pollution are considered global problems, and endanger human health mainly due to the emission of fine particulate matter released into the atmosphere and improper disposal of post-consumer plastic bottles. Therefore, it is urgent to develop filter media to effectively protect the public. The properties of plastics make them potential candidates for nanofiber mat formers due to their attractive structural and mechanical characteristics. This work aims to produce and evaluate novel PET electrospun fibers dispensed with the use of support materials to be used as filter media to remove nanoparticles from the air. The electrospinning process was carried out by changing the concentration of the polymer solution, the needle diameter, and the electrospinning processing time at two rotation speeds. The average diameters of the micro- and nanofibers of the filter media produced ranged from 3.25 µm to 0.65 µm and it was possible to conclude that, as the size of the fibers decreased, the mechanical strength increased from 3.2 to 4.5 MPa. In filtration tests, a collection efficiency of up to 99% with low-pressure drops (19.4 Pa) was obtained for nanoparticles, demonstrating high quality factor filter media, which could be applicable in gas filtration.