Crown Reconstruction of Erosive Wear Using High-viscosity Glass Ionomer Cement: A Case Report.

The aim of this clinical report is to present a possible alternative treatment, with 24-month follow-up, for restoring tooth loss due to extensive erosive tooth wear. A 21-year-old male patient, complaining of intense sensitivity in the maxillary posterior teeth, and presenting severe wear on maxillary premolar and molar teeth due to gastroesophageal reflux, sought care in the university clinics. The planned treatment was to refer for medical treatment and perform restorations with the high-viscosity glass ionomer cement Equia Forte (GC Corporation, Tokyo, Japan), aiming to restore the dental anatomy and to consequently decrease the pain symptomatology. A silicone guide, obtained from a diagnostic waxing, was used during the restorative approach considering the patient's occlusion. After all the clinical steps of the restorative technique, an occlusal adjustment of restorations was performed. During monthly recalls up to 24 months, the treatment was stable and in service. In addition, the patient reported no pain and improved chewing, leading to a better quality of life.

Clinical Evaluation of Lithium Disilicate Veneers Manufactured by CAD/CAM Compared with Heat-pressed Methods: Randomized Controlled Clinical Trial.

CLINICAL RELEVANCE: Lithium disilicate veneers for esthetic restorations show great accuracy and similarity, regardless of the type of fabrication technique.

Effectiveness of LED/Laser Irradiation on In-Office Dental Bleaching after Three Years.

The present in vivo randomized, triple-blinded, and split-mouth clinical study evaluated the effectiveness of a hybrid light (HL) source on the color change, stability, and tooth sensitivity in patients submitted to different in-office bleaching techniques. Twenty volunteers were divided into two groups and four subgroups. A split-mouth design was conducted to compare two in-office bleaching techniques (with and without light activation): 35% Lase Peroxide Sensy (LPS) + HL: 35% hydrogen peroxide (HP) + HL; 35% LPS: 35% HP; 25% LPS + HL: 25% HP + HL; and 35% Whiteness HP (WHP): 35% HP. For the groups activated with HL, the HP was applied on the enamel surface three consecutive times using a 3 × 2-minute protocol (three HL activations for two minutes each, with a 30-second interval for a total of seven minutes and 30 seconds) for each gel application, totaling 22 minutes and 30 seconds. For the other groups, HP was applied 3 × 15 minutes, totaling 45 minutes. A spectrophotometer was used to measure the color change (ΔE) before the treatment and 24 hours, one week, and one, 12, and 36 months after. A visual analog scale was used to evaluate the tooth sensitivity before the treatment, immediately following treatment, 24 hours, and one week after. Analysis of variance, Tukey's, Kruskall-Wallis, and Wilcoxon tests, all with α = 0.05 were performed. Statistical analysis did not reveal any significant differences (ΔE) between the in-office bleaching techniques with or without HL in the periods evaluated; the activation with HL required 50% less time to achieve such results. The groups without HL presented statistical differences for ΔE when comparing 24 hours with the other follow-up times (intergroup) and an increase in tooth sensitivity in the initial periods. All techniques and bleaching agents were effective on bleaching during a 36-month evaluation of color stability. The groups activated with HL presented lower sensitivity and required a lower activation time.

Bonding Polycrystalline Zirconia With 10-MDP-containing Adhesives.

OBJECTIVE: The objective of this study was to evaluate the influence of adhesives with different 10-MDP concentrations on the shear bond strength of a resin cement to zirconia. METHODS AND MATERIALS: Six experimental adhesives were prepared with the following composition: camphorquinone, 1,2-diaminobenzene, butylhydroxytoluene, diphenyliodonium hexafluorophosphate, 2-hydroxyethyl methacrylate triethylene glycol dimethacrylate, ethoxylated bisphenol A glycol dimethacrylate, urethane dimethacrylate, bisphenol A diglycidyl methacrylate, and ethanol. The 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) monomer was added at 0wt%, 3wt%, 6wt%, 9wt%, 12wt%, or 15wt%. Three commercially available adhesives were evaluated: Single Bond Universal, Single Bond 2, and Signum Zirconia Bond. Resin cement cylinders made with RelyX Ultimate were bonded to yttria-stabilized tetragonal zirconia polycrystal with one of the evaluated adhesives and were subjected to the shear bond strength evaluation. Failure modes were analyzed with a stereoscopic loupe. Statistical analyses were performed with one-way analysis of variance and the Tukey's Honestly Significant Difference test (α=0.05). Pearson's was used to correlate the percentage of 10-MDP in the experimental adhesives and shear bond strength. RESULTS: There were significant differences between adhesives (p<0.00001). The highest shear bond strength values were obtained with the Signum Zirconia Bond and Single Bond Universal. Single Bond 2 showed the lowest values. There were no differences between experimental adhesives. All groups showed adhesives failures. A nonlinear correlation was found between bond strength and percentage of 10-MDP in experimental adhesives (r=0.872). CONCLUSIONS: The commercially available adhesives indicated for bonding to zirconia showed the highest bonding values.