Cost-effective activated carbons for CO2 adsorption were developed from molasses using H2SO4, H3PO4, HCl, NaOH, and KOH as activating agents. At the temperature of 0 °C and a pressure of 1 bar, CO2 adsorption equal to 5.18 mmol/g was achieved over activated carbon obtained by KOH activation. The excellent CO2 adsorption of M-KOH can be attributed to its high microporosity. However, activated carbon prepared using HCl showed quite high CO2 adsorption while having very low microporosity. The absence of acid species on the surface promotes CO2 adsorption over M-HCl. The pore size ranges that are important for CO2 adsorption at different temperatures were estimated. The higher the adsorption temperature, the more crucial smaller pores were. For 1 bar pressure and temperatures of 0, 10, 20, and 30 °C, the most important were pores equal and below: 0.733, 0.733, 0.679, and 0.536 nm, respectively.
RESUMO
This paper reports on the electrical and broadband dielectric spectroscopy studies of Zn2-xMgxInV3O11 materials (where x = 0.0, 0.4, 1.0, 1.6, 2.0) synthesized using a solid-state reaction method. These studies showed n-type semiconducting properties with activation energies of 0.147-0.52 eV in the temperature range of 250-400 K, symmetric and linear I-V characteristics, both at 300 and 400 K, with a stronger carrier emission for the matrix and much less for the remaining samples, as well as the dipole relaxation, which was the slowest for the sample with x = 0.0 (matrix) and was faster for Mg-doped samples with x > 0.0. The faster the dipole relaxation, the greater the accumulation of electric charge. These effects were analyzed within a framework of the DC conductivity and the Cole-Cole fit function, including the solid-state density and porosity of the sample. The resistivity vs. temperature dependence was well fitted using the parallel resistor model. Our ab initio calculations also show that the bandgap increased with the Mg content.