Directly-Fused Ni(II)Porphyrin Conjugated Polymers with Blocked meso-Positions: Impact on Electrocatalytic Properties.

The oxidative coupling reaction of two Ni(II) porphyrins meso-substituted with three and four phenyl groups, Ni(II) 5,10,15-(triphenyl)porphyrin (NiPh3P) and Ni(II) 5,10,15,20-(tetraphenyl)porphyrin (NiPh4P) respectively, was investigated in a oxidative chemical vapor deposition (oCVD) process. Irrespective of the number of meso-substituents, high-resolution mass spectrometry evidences the formation of oligomeric species containing up to five porphyrin units. UV-Vis-NIR and XPS analyses of the oCVD films highlighted a strong dependence of the intermolecular coupling reaction with the substrate temperature. Specifically, higher substrate temperatures yield lowering of valence band maxima and reduction of the band gap. The formation of conjugated polymeric assemblies results in increased conductivities as compared to their sublimed counterparts. Yet, electrocatalytic measurements exhibit water oxidation onset overpotentials (308 mV for pNiPh3P and 343 mV for pNiPh4P) comparatively higher than the onset overpotential measured for the oCVD film from Ni(II) 5,15-(diphenyl)porphyrin (pNiPh2P), i. e. 283 mV. Although DFT and comparative oCVD studies suggest the formation of directly fused porphyrins involving 'phenyl-mediated' and ß-ß linkages when reacting tetra-meso-substituted porphyrins, the present findings highlight that multiple direct fusion (ß-ß/meso-meso/ß-ß or meso-ß/ß-meso) is essential for Ni(II) porphyrin-based conjugated polymers to enable a dinuclear radical oxo-coupling operating mechanism for water oxidation at low overpotential and durable catalytic activity.

A Polymer-Derived Co(Fe)Ox Oxygen Evolution Catalyst Benefiting from the Oxidative Dehydrogenative Coupling of Cobalt Porphyrins.

Thin films of cobalt porphyrin conjugated polymers bearing different substituents are prepared by oxidative chemical vapor deposition (oCVD) and investigated as heterogeneous electrocatalysts for the oxygen evolution reaction (OER). Interestingly, the electrocatalytic activity originates from polymer-derived, highly transparent Co(Fe)Ox species formed under operational alkaline conditions. Structural, compositional, electrical, and electrochemical characterizations reveal that the newly formed active catalyst greatly benefited from both the polymeric conformation of the porphyrin-based thin film and the inclusion of the iron-based species originating from the oCVD reaction. High-resolution mass spectrometry analyses combined with density functional theory (DFT) calculations showed that a close relationship exists between the porphyrin substituent, the extension of the π-conjugated system cobalt porphyrin conjugated polymer, and the dynamics of the polymer conversion leading to catalytically active Co(Fe)Ox species. This work evidences the precatalytic role of cobalt porphyrin conjugated polymers and uncovers the benefit of extended π-conjugation of the molecular matrix and iron inclusion on the formation and performance of the true active catalyst.

Enhanced Photocatalytic Hydrogen Evolution from Water Splitting on Ta2O5/SrZrO3 Heterostructures Decorated with CuxO/RuO2 Cocatalysts.

Photocatalytic H2 generation by water splitting is a promising alternative for producing renewable fuels. This work synthesized a new type of Ta2O5/SrZrO3 heterostructure with Ru and Cu (RuO2/CuxO/Ta2O5/SrZrO3) using solid-state chemistry methods to achieve a high H2 production of 5164 µmol g-1 h-1 under simulated solar light, 39 times higher than that produced using SrZrO3. The heterostructure performance is compared with other Ta2O5/SrZrO3 heterostructure compositions loaded with RuO2, CuxO, or Pt. CuxO is used to showcase the usage of less costly cocatalysts to produce H2. The photocatalytic activity toward H2 by the RuO2/CuxO/Ta2O5/SrZrO3 heterostructure remains the highest, followed by RuO2/Ta2O5/SrZrO3 > CuxO/Ta2O5/SrZrO3 > Pt/Ta2O5/SrZrO3 > Ta2O5/SrZrO3 > SrZrO3. Band gap tunability and high optical absorbance in the visible region are more prominent for the heterostructures containing cocatalysts (RuO2 or CuxO) and are even higher for the binary catalyst (RuO2/CuxO). The presence of the binary catalyst is observed to impact the charge carrier transport in Ta2O5/SrZrO3, improving the solar to hydrogen conversion efficiency. The results represent a valuable contribution to the design of SrZrO3-based heterostructures for photocatalytic H2 production by solar water splitting.

Electronic and energy level engineering of directly fused porphyrin-conjugated polymers - impact of the central metal cation.

The integration of porphyrins and their derivatives in functional devices for solar-assisted fuel production is both highly attractive and challenging due to the difficulties in processing them. This limitation is overcome in the gas-phase approach, particularly by oxidative chemical vapor deposition (oCVD), leading to the simultaneous synthesis and deposition of conjugated porphyrin coatings. We have investigated the impact of the metal cation of 5,15-diphenyl metalloporphyrins (MDPP; M = Co, Cu, Mg, Zn, Pd, Pt, Ag, Ru, Ag, and FeCl) on the dehydrogenative coupling reaction leading to fused-metalloporphyrin thin films via oCVD and on the optoelectronic properties of the resulting thin films. We found that the nature of the chelated cation strongly affects the intermolecular coupling efficiency, as well as the occurrence of side reactions such as chlorination, intramolecular cyclization, demetallation/re-metalation, and oxidation of the porphyrin core. Moreover, we discussed the influence of the above-mentioned reactions on the optoelectronic properties of the fused metalloporphyrin coatings, in view of their potential application in photo-electrocatalytic systems. This study paves the way toward the engineering and future implementation of porphyrin-based systems for clean and efficient solar fuel production.

Low Temperature Open-Air Plasma Deposition of SrTiO3 Films for Solar Energy Harvesting: Impact of Precursors on the Properties and Performances.

Strontium titanate (STO) is a well-known oxide used in a wide variety of applications due to its excellent stability and optoelectronic properties. However, its integration in photoelectrocatalytic devices is limited by the lack of fast and scalable methods to produce robust films at a low temperature and atmospheric pressure. Herein, we report an atmospheric pressure plasma-enhanced chemical vapor deposition (AP-PECVD) approach for the synthesis of STO crystalline films and their applications for photoelectrochemical solar energy conversion. The film crystallinity, which plays a determinant role in the photoelectrochemical performance, was linked to the selected strontium precursor and injection method. Through thermal stability studies of the precursors [Sr(dpm), Sr(ipo), Sr(acac), and Ti(ipo)] and analysis of the solution droplet size, it was demonstrated that the closer thermal decomposition behavior and superior miscibility of the Sr(dpm) and Ti(ipo) precursors led to more homogeneous and crystalline films with the highest photoelectrochemical performance (16.5 µA cm-2 at 1.23 V vs RHE under 100 mW cm-2), which can be further improved by a factor of 3.4 using thermal annealing at 500 °C. Evidence of the impact of a strontium precursor on the properties of STO films is provided through thermogravimetric analysis, X-ray diffraction, energy-dispersive system, UV-vis, X-ray photoelectron spectroscopy, HIM-SIMS, and photoelectrochemical analysis.

Fused Metalloporphyrin Thin Film with Tunable Porosity via Chemical Vapor Deposition.

Porous and highly conjugated multiply fused porphyrin thin films are prepared from a fast and single-step chemical vapor deposition approach. While the solution-based coupling of porphyrins is usually undertaken at room temperature, the gas phase reaction of nickel(II) 5,15-(diphenyl)porphyrin and iron(III) chloride (FeCl3) is investigated for temperatures as high as 200 °C. Helium ion and atomic force microscopy, supported by weight and thickness measurements, shows a drastic decrease of the fused porphyrin thin film's density accompanied by the formation of a mesoporous morphology upon increase of the reaction temperature. The increase of the film's porosity is attributed to formation of a greater amount of HCl (originated from both the oxidative coupling and chlorination reactions) and the release of gaseous FeCl3 byproducts, i.e., Cl2, at higher deposition temperatures. In addition, high resolution mass spectrometry reveals that increase of the reaction temperature promotes a higher degree of conjugation of the fused porphyrins chains, which ensures that high electronic conductivities are maintained along with high porosity. The method reported herein could enable the engineering of fused porphyrin thin films in sensing and catalytic devices.

Molecular flattening effect to enhance the conductivity of fused porphyrin tape thin films.

The straightforward synthesis of directly fused porphyrins (porphyrin tapes) from 5,15-diphenyl porphyrinato nickel(ii) complexes with different substituents on the phenyl rings is achieved while processing from the gas phase. The porphyrin tapes, exhibiting NIR absorption, are readily obtained in thin film form. The gas phase approach cuts the need for solubilizing groups allowing for the first time the study of their conductivity according to the substituent. 2-Point probe and conductivity AFM measurements evidence that reducing the size of the meso substituents, phenyl < mesityl < di(3,5-tert-butyl)phenyl < di(2,6-dodecyloxy)phenyl, improves the thin film conductivity by several orders of magnitude. Density functional theory and gel permeation chromatography, correlate this improvement to changes in the intermolecular distances and molecular geometry. Furthermore, the oCVD of porphyrins with free ortho-phenyl positions causes intramolecular dehydrogenative side reactions inducing a complete planarization of the molecule. This molecular flattening drastically affects the π-π stacking between the porphyrins further enhancing the electronic properties of the films.

Reactivity of Nickel(II) Porphyrins in oCVD Processes-Polymerisation, Intramolecular Cyclisation and Chlorination.

Oxidative chemical vapour deposition of (5,15-diphenylporphyrinato)nickel(II) (NiDPP) with iron(III) chloride as oxidant yielded a conjugated poly(metalloporphyrin) as a highly coloured thin film, which is potentially useful for optoelectronic applications. This study clarified the reactive sites of the porphyrin monomer NiDPP by HRMS, UV/Vis/NIR spectroscopy, cyclic voltammetry and EPR spectroscopy in combination with quantum chemical calculations. Unsubstituted meso positions are essential for successful polymerisation, as demonstrated by varying the porphyrin meso substituent pattern from di- to tri- and tetraphenyl substitution. DFT calculations support the proposed radical oxidative coupling mechanism and explain the regioselectivity of the C-C coupling processes. Depositing the conjugated polymer on glass slides and on thermoplastic transparent polyethylene naphthalate demonstrated the suitability of the porphyrin material for flexible optoelectronic devices.

Thermoresponsive Water-Soluble Polymer Layers and Water-Stable Copolymer Layers Synthesized by Atmospheric Plasma Initiated Chemical Vapor Deposition.

The growth of thermoresponsive layers with the atmospheric pressure plasma-initiated chemical vapor deposition (AP-PiCVD) process is reported for the first time. N-vinyl caprolactam (NVCL) was successfully homopolymerized and copolymerized with ethylene glycol dimethacrylate (EGDMA), yielding water-soluble and water-stable thermoresponsive thin films, respectively. Strong chemical retention and high thermoresponsivity were achieved, highlighting the ability of AP-PiCVD to grow functional conventional homopolymers and copolymers.

Conductive Fused Porphyrin Tapes on Sensitive Substrates by a Chemical Vapor Deposition Approach.

Oxidative polymerization of nickel(II) 5,15-diphenyl porphyrin and nickel(II) 5,15-bis(di-3,5-tert-butylphenyl) porphyrin by oxidative chemical vapor deposition (oCVD) yields multiply fused porphyrin oligomers in thin film form. The oCVD technique enables one-step formation, deposition, and p-doping of conjugated poly(porphyrins) coatings without solvents or post-treatments. The decisive reactions and side reactions during the oCVD process are shown by high-resolution mass spectrometry. Owing to the highly conjugated structure of the fused tapes, the thin films exhibit an electrical conductivity of 3.6×10-2  S cm-1 and strong absorption in the visible to near-infrared spectral region. The formation of smooth conjugated poly(porphyrins) coatings, even on sensitive substrates, is demonstrated by deposition and patterning on glass, silicon, and paper. Formation of conductive poly(porphyrins) thin films could enable the design of new optoelectronic devices using the oCVD approach.

Precursors for Atmospheric Plasma-Enhanced Sintering: Low-Temperature Inkjet Printing of Conductive Copper.

Bidentate diamine and amino-alcohol ligands have been used to form solid, water-soluble, and air-stable monomeric copper complexes of the type [Cu(NH2CH2CH(R)Y)2(NO3)2] (1, R=H, Y=NH2; 2, R=H, Y=OH; 3, R=Me, Y=OH). The complexes were characterized by elemental analysis, mass spectrometry, infrared spectroscopy, thermal gravimetric analysis, and single-crystal X-ray diffraction. Irrespective of their decomposition temperature, precursors 1-3 yield highly conductive copper features [1.5×10-6â€…Ω m (±5×10-7â€…Ω m)] upon atmospheric-pressure plasma-enhanced sintering.

Transparent anti-fogging and self-cleaning TiO2/SiO2 thin films on polymer substrates using atmospheric plasma.

Transparent anti-fogging and self-cleaning coatings are of great interest for many applications, including solar panels, windshields and displays or lenses to be used in humid environments. In this paper, we report on the simultaneous synthesis, at atmospheric pressure, of anatase TiO2 nanoparticles and low-temperature, high-rate deposition of anatase TiO2/SiO2 nanocomposite coatings. These coatings exhibit durable super-hydrophilic and photocatalytic properties. The strategy followed relies on concomitant and separated injections of titania, i.e. titanium isopropoxide, and silica, i.e. hexamethyldisiloxane, precursors in the stream of a blown-arc discharge to form transparent anti-fogging and self-cleaning anatase TiO2/SiO2 nanocomposite coatings on polymer substrates.

Significance of a Noble Metal Nanolayer on the UV and Visible Light Photocatalytic Activity of Anatase TiO2 Thin Films Grown from a Scalable PECVD/PVD Approach.

UV and visible light photocatalytic composite Pt and Au-TiO2 coatings have been deposited on silicon and glass substrates at low temperature using a hybrid ECWR-PECVD/MS-PVD process. Methylene blue, stearic acid, and sulfamethoxazole were used as dye, organic, and antibiotic model pollutants, respectively, to demonstrate the efficiency of these nanocomposite coatings for water decontamination or self-cleaning surfaces applications. Raman investigations revealed the formation of anatase polymorph of TiO2 in all synthesized coatings with a shifting of the main vibrational mode peak to higher wavenumber in the case of Au-TiO2 coating, indicating an increase number of crystalline defects within this coating. Because of the difference of the chemical potentials of each of the investigated noble metals, the sputtered metal layers exhibit different morphology. Pt sputtered atoms, with high surface adhesion, promote formation of a smooth 2D layer. On the other hand, Au sputtered atoms with higher cohesive forces promote the formation of 5-10 nm nanoparticles. As a result, the surface plasmon resonance phenomenon was observed in the Au-TiO2 coatings. UV photoactivity of the nanocomposite coatings was enhanced 1.5-3 times and 1.3 times for methylene blue and stearic acid, respectively, thanks to the enhancement of electron trapping in the noble metal layer. This electron trapping phenomenon is higher in the Pt-TiO2 coating because of its larger work function. On the other hand, the enhancement of the visible photoactivity was more pronounced (3 and 7 times for methylene blue and stearic acid, respectively) in the case of Au-TiO2 thanks to the surface plasmon resonance. Finally, these nanocomposite TiO2 coatings exhibited also a good ability for the degradation of antibiotics usually found in wastewater such as sulfamethoxazole. However, a complementary test have showed an increase of the toxicity of the liquid medium after photocatalysis, which could be due the presence of sulfamethoxazole's transformation byproducts.

Photocatalytic Anatase TiO2 Thin Films on Polymer Optical Fiber Using Atmospheric-Pressure Plasma.

Due to the undeniable industrial advantages of low-temperature atmospheric-pressure plasma processes, such as low cost, low temperature, easy implementation, and in-line process capabilities, they have become the most promising next-generation candidate system for replacing thermal chemical vapor deposition or wet chemical processes for the deposition of functional coatings. In the work detailed in this article, photocatalytic anatase TiO2 thin films were deposited at a low temperature on polymer optical fibers using an atmospheric-pressure plasma process. This method overcomes the challenge of forming crystalline transition metal oxide coatings on polymer substrates by using a dry and up-scalable method. The careful selection of the plasma source and the titanium precursor, i.e., titanium ethoxide with a short alkoxy group, allowed the deposition of well-adherent, dense, and crystalline TiO2 coatings at low substrate temperature. Raman and XRD investigations showed that the addition of oxygen to the precursor's carrier gas resulted in a further increase of the film's crystallinity. Furthermore, the films deposited in the presence of oxygen exhibited a better photocatalytic activity toward methylene blue degradation assumedly due to their higher amount of photoactive {101} facets.

Interstitial Boron-Doped TiO2 Thin Films: The Significant Effect of Boron on TiO2 Coatings Grown by Atmospheric Pressure Chemical Vapor Deposition.

The work presented here describes the preparation of transparent interstitial boron-doped TiO2 thin-films by atmospheric pressure chemical vapor deposition (APCVD). The interstitial boron-doping, on TiO2, proved by X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD), is shown to enhance the crystallinity and significantly improve the photocatalytic activity of the TiO2 films. The synthesis, highly suitable for a reel-to-reel process, has been carried out in one step.

Metal-Organic Covalent Network Chemical Vapor Deposition for Gas Separation.

The chemical vapor deposition (CVD) polymerization of metalloporphyrin building units is demonstrated to provide an easily up-scalable one-step method toward the deposition of a new class of dense and defect-free metal-organic covalent network (MOCN) layers. The resulting hyper-thin and flexible MOCN layers exhibit outstanding gas-separation performances for multiple gas pairs.

Atmospheric pressure plasma-initiated chemical vapor deposition (AP-PiCVD) of poly(diethylallylphosphate) coating: a char-forming protective coating for cellulosic textile.

An innovative atmospheric pressure chemical vapor deposition method toward the deposition of polymeric layers has been developed. This latter involves the use of a nanopulsed plasma discharge to initiate the free-radical polymerization of an allyl monomer containing phosphorus (diethylallylphosphate, DEAP) at atmospheric pressure. The polymeric structure of the film is evidence by mass spectrometry. The method, highly suitable for the treatment of natural biopolymer substrate, has been carried out on cotton textile to perform the deposition of an efficient and conformal protective coating.

Dual application of (aqua)(chlorido)(porphyrinato)chromium(III) as hypersensitive amine-triggered ON switch and for dioxygen activation.

Although synthesis and substitution reactions of chlorido chromium(III) porphyrins Cr(III)(TPP)(Cl)(L) (H2TPP = 5,10,15,20-tetraphenyl porphyrin, L = pyridine, H2O, ROH, etc.), have been well-established in coordination chemistry for decades, an unexpected dichotomous reactivity of Cr(III)(TPP)(Cl)(H2O) (1) toward amines is disclosed here. This reactivity leads to the application of 1 as highly sensitive substoichiometric and irreversible ON switch for amine detection by an autocatalytic pathway. The concomitant activation of O2 by the 1/amine system is furthermore exploited in an electrochemically driven epoxidation of norbonene using O2 as initial oxidant.

Robust bio-inspired antibacterial surfaces based on the covalent binding of peptides on functional atmospheric plasma thin films.

Here, we describe a robust process aiming at conferring antibacterial properties on stainless steel through the covalent grafting of nisin, a natural antimicrobial peptide, onto a functional plasma thin film deposited by an atmospheric pressure dielectric barrier discharge process. The three different steps of the procedure, namely the deposition of a carboxyl rich thin layer, the surface activation by using a zero-length crosslinking agent and the nisin immobilisation, are reported and thoroughly characterised. A correlation between the carboxylic group surface concentration and the surface roughness onto the antibacterial properties of the layers is evidenced. Finally, IR analyses appear as a powerful analytical tool allowing us to validate the different chemical surface modifications, to confirm the relevance of the activation step to achieve a stable and homogenous peptide grafting over all the surfaces, as well as to investigate the secondary structure of immobilized peptides.

A novel dry chemical path way for diene and dienophile surface functionalization toward thermally responsive metal-polymer adhesion.

In this paper, we report a new and easily up-scalable dry chemical method to functionalize with diene and dienophile groups a large range of surfaces, such as metal, polymer, or glass, and we demonstrate the potentiality of this technique to realize thermally responsive adhesion between these materials. A complete and extensive surface chemistry analysis of the grafted surfaces, based on the deposition of an anhydride-rich thin plasma polymer layer by using an atmospheric pressure dielectric barrier discharge (DBD) plasma process, and its subsequent gas phase aminolysis reaction with specific diene or dienophile compound is discussed. The optimization of the assembling condition for these tailored surfaces has led to achieve a Diels-Alder adhesion force up to 0.6 N/mm at ambient temperature, which can be reduced by a factor of 50 when the retro Diels-Alder is ignited at a heating temperature around 200 °C. The study of the failure interface produced after peeling tests is presented and a mechanism of failure is proposed, based on forensic analyses involving surface analytical techniques such as XPS, ToF-SIMS, and SEM combined to AFM analyses for the retrieving of chemical and morphological information.