RESUMO
In a recent paper, novel polyester nanocomposites reinforced with up to 3 wt% of cellulose nanocrystals (CNCs) extracted from conifer fiber were characterized for their crystallinity index, water absorption, and flexural and thermal resistance. The use of this novel class of nanocomposites as a possible substitute for conventional glass fiber composites (fiberglass) was then suggested, especially for the 1 and 2 wt% CNC composites due to promising bending, density, and water absorption results. However, for effective engineering applications requiring impact and tensile performance, the corresponding properties need to be evaluated. Therefore, this extension of the previous work presents additional results on Izod and tensile tests of 1 and 2 wt% CNC-reinforced polyester composites, together with a comparative cost analysis with fiberglass. The chemical effect caused by incorporation of CNCs into polyester was also investigated by FTIR. In comparison to the neat polyester, the Izod impact energy increased 50% and 16% for the 1 and 2 wt% composites, respectively. On the other hand, the tensile strength and Young's modulus remained constant within the ANOVA statistical analysis. FTIR analysis failed to reveal any chemical modification caused by up to 2 wt% CNC incorporation. The present impact and tensile results corroborate the promising substitution of a polyester composite reinforced with very low amount of CNCs for common fiberglass in engineering application.
RESUMO
The application of cellulose nanocrystal has lately been investigated as polymer composites reinforcement owing to favorable characteristics of biodegradability and cost effectiveness as well as superior mechanical properties. In the present work novel nanocomposites of unsaturated polyester matrix reinforced with low amount of 1, 2, and 3 wt% of cellulose nanocrystals obtained from conifer fiber (CNC) were characterized. The polyester matrix and nanocomposites were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), bending test, and thermogravimetric analysis (TGA). The result showed that the addition of only 2 wt% CNC increased the nanocomposite flexural strength by 159%, the ductility by 500% and the toughness by 1420%. Fracture analyses by SEM revealed a uniform participation of the CNC in the polyester microstructure. The resistance to thermal degradation of the CNC reinforced nanocomposites was improved in more than 20 °C as compared to neat polyester. No significant changes were detected in the water absorptions and XRD pattern of the neat polyester with incorporations up to 3 wt% CNC. These results reveal that the 2 wt% CNC nanocomposite might be a promising more ductile, lightweight and cost-effective substitute for conventional glass fiber composites in engineering applications.