Tensile properties in collagen-rich tissues of Quarter Horses with hereditary equine regional dermal asthenia (HERDA).

REASONS FOR PERFORMING STUDY: Hereditary equine regional dermal asthenia (HERDA) is an autosomal recessive disorder of Quarter Horses characterised by skin fragility. Horses with HERDA have a missense mutation in peptidyl-prolyl cis-trans isomerase B (PPIB), which encodes cyclophilin B and alters folding and post translational modifications of fibrillar collagen. OBJECTIVES: The study aimed to test the hypothesis that tendons, ligaments and great vessels, which, like skin, are rich in fibrillar collagen, will also have abnormal biomechanical properties in horses with HERDA. STUDY DESIGN: Ex vivo biomechanical study comparing horses with and without a diagnosis of HERDA. METHODS: Forelimb suspensory ligament, superficial and deep digital flexor tendons; withers, forelimb and abdominal skin; the main pulmonary artery and the aortic arch were harvested from 6 horses with HERDA and 6 control horses without the HERDA allele. Tissues were distracted to failure. Tensile strength (TS), elastic modulus (EM) and energy to failure (ETF) were compared. RESULTS: Horses with HERDA had significantly lower TS and EM in tendinoligamentous tissues and great vessels, respectively. The TS, EM and ETF were significantly lower in skin from horses with HERDA. Differences in TS and ETF were more extreme at the withers than at the forelimb or abdomen. CONCLUSIONS: Tendinoligamentous tissue, great vessels and skin are significantly weaker in horses with HERDA than in horses lacking the PPIB mutation, substantiating that diverse tissues with high fibrillar collagen content are abnormal in HERDA and that the HERDA phenotype is not limited to the integument.

A cryogenic clamping technique that facilitates ultimate tensile strength determinations in tendons and ligaments.

OBJECTIVE: To describe the use of a cryogenic clamp of novel design for tensile strength testing of tendinous and ligamentous tissues with inherently high tensile strength. METHODS: Inexpensive, easily machined steel clamps were manufactured to facilitate rapid insertion into a standard wedge-screw grip apparatus installed on a testing system with a control system attached. The deep digital flexor tendon (DDFT) of six horses was trimmed to a uniform dumbbell shape and secured in clamps using partial submersion in liquid nitrogen for approximately 45 seconds and immediately tested. Approximate time between removal from liquid nitrogen and failure of tendon was four minutes. RESULTS: Failure was achieved in all tendons tested in a region approximating a midpoint between the clamps. Ultimate failure loads of up to 6745 N were achieved without slippage of the tissue from the grips. The ultimate tensile strength of the normal equine DDFT determined in this study was 111.82 ± 11.53 N/mm2, and the stress versus grip-to-grip elongation plots for our equine DDFT were representative of a standard non-linear elastic curve obtained in similar studies. CLINICAL SIGNIFICANCE: We present a low cost device for quantifying physical properties of specimens with high connective tissue concentrations and inherent high tensile strength. Results of this study indicate that this device provides a practical alternative to other more costly methods of adequately securing larger tendons and ligaments for tensile strength testing.