Watt-level 775†nm SHG with 70% conversion efficiency and 97% pump depletion in annealed/reverse proton exchanged diced PPLN ridge waveguides.

We report on fabrication of ridge waveguides formed in congruent periodically poled lithium niobate substrates using annealed and reverse proton exchange followed by diamond blade dicing. 1 W of second-harmonic generation at 775 nm has been obtained in a single-pass in 50 mm long ridge waveguides with internal conversion efficiency of 70%. At this power level, 97% pump depletion has been reached. Although elevated temperature operation and ridge geometry help to mitigate photorefractive damage (PRD) effects, nevertheless, at even higher second harmonic outputs significant power drop with blue shift and distortion of the SHG tuning curve have been observed indicating an onset of PRD.

Efficient Nd:Ti:LiNbO3 ridge waveguide lasers emitting around 1085 nm.

In this work, we report on efficient neodymium-doped titanium in-diffused ridge waveguide lasers in x-cut congruent LiNbO3 under excitation at 814 nm. For the sample fabrication we used our novel technique of three-side evaporation and in-diffusion for Nd and Ti incorporation into pre-defined ridges. Due to improved photorefractive damage resistance by indium tin oxide (ITO) coating we achieved stable laser operation at 1084.7 nm with a maximum output power of 108 mW and a slope efficiency of 34% exceeding the best literature values for Nd:Ti:LiNbO3 ridge waveguide lasers.