RESUMO
Additive manufacturing technologies enable lightweight, functionally integrated designs and development of biomimetic structures. They contribute to the reduction in material waste and decrease in overall process duration. A major challenge for the qualification for aerospace applications is the surface quality. Considering Ti-64 laser powder bed fusion (LPBF) parts, particle agglomerations and resulting re-entrant features are characteristic of the upper surface layer. Wet-chemical post-processing of the components ensures reproducible surface quality for improved fatigue behaviour and application of functional coatings. The 3D SurFin® and chemical milling treatments result in smoother surface finishes with characteristic properties. In order to characterise these surfaces, three methods for surface texture measurement (contact and non-contact) were applied, namely confocal microscopy, fringe projection and stylus profilometry. The aim of this work was to show their suitability for measurement of laser powder bed fusion as-built and post-processed surfaces and compare results across the evaluated surface conditions. A user-oriented rating of the methods, summarising advantages and disadvantages of the used instruments specifically and the methods in general, is provided. Confocal microscopy reaches the highest resolution amongst the methods, but measurements take a long time. The raw data exhibit large measurement artefacts for as-built and chemically milled conditions, requiring proper data post-processing. The stylus method can only capture 2D profiles and the measurement was restricted by particle agglomerations and craters. However, the method (process and instrument) is entirely standardised and handheld devices are inexpensive, making it accessible for a large group of users. The fringe projection method was the quickest and easiest regarding measurement and data post-processing. Due to large areal coverage, reproduction of location when performing repeat measurements is possible. The spatial resolution is lower than for confocal microscopy but is still considered sufficiently high to characterise the investigated surface conditions.
RESUMO
Metal additive manufacturing technologies have great potential for future use in load-bearing aerospace applications, requiring a deeper understanding of mechanical performance and influencing factors. The objective of this study was to investigate the influence of contour scan variation on surface quality, tensile and fatigue strength for laser powder bed fusion samples made of AlSi7Mg0.6 material and to create high-quality as-built surfaces. The samples were produced with identical bulk and different contour scan parameters to accommodate the investigation of the impact of as-built surface texture on mechanical properties. The bulk quality was evaluated by density measurements according to Archimedes' principle and tensile testing. The surfaces were investigated using the optical fringe projection method, and surface quality was assessed by the areal surface texture parameters Sa (arithmetic mean height) and Sk (core height, derived from material ratio curve). Fatigue life was tested at different load levels, and the endurance limit was estimated based on a logarithmic-linear relation between number of cycles and stress. All samples were found to have a relative density of more than 99%. Surface conditions distinctive in Sa and Sk were successfully created. The resulting mean values of the ultimate tensile strength σult are between 375 and 405 MPa for 7 different surface conditions. It was confirmed that the influence of contour scan variation on bulk quality is insignificant for the assessed samples. Regarding fatigue, one as-built condition was found to perform as well as surface post-processed parts and better than the as-cast material (compared to literature values). The fatigue strength at the endurance limit for 106 cycles is between 45 and 84 MPa for the three considered surface conditions.