Mud and burnt Roman bricks from Romula.

Sesquipedalian mud and burnt bricks (second to third century AD) were excavated from the Roman city of Romula located in the Lower Danube Region (Olt county, Romania). Along with local soils, bricks are investigated by petrographic analysis, X-ray fluorescence (XRF), X-ray diffraction (XRD), Fourier transformed infrared spectroscopy (FT-IR), electron microscopy (SEM/EDX), X-ray microtomography (XRT), thermal analysis (DTA-TG), MÓ§ssbauer spectroscopy, magnetometry, colorimetry, and mechanical properties assessment. The results correlate well with each other, being useful for conservation/restoration purposes and as reference data for other ceramic materials. Remarkably, our analysis and comparison with literature data indicate possible control and wise optimization by the ancient brickmakers through the recipe, design (size, shape, and micro/macrostructure), and technology of the desired physical-chemical-mechanical properties. We discuss the Roman bricks as materials that can adapt to external factors, similar, to some extent, to modern "smart" or "intelligent" materials. These features can explain their outstanding durability to changes of weather/climate and mechanical load.

Antibacterial composite coatings of MgB2 powders embedded in PVP matrix.

Three commercial powders of MgB2 were tested in vitro by MTS and LDH cytotoxicity tests on the HS27 dermal cell line. Depending on powders, the toxicity concentrations were established in the range of 8.3-33.2 µg/ml. The powder with the lowest toxicity limit was embedded into polyvinylpyrrolidone (PVP), a biocompatible and biodegradable polymer, for two different concentrations. The self-replenishing MgB2-PVP composite materials were coated on substrate materials (plastic foil of the reservoir and silicon tubes) composing a commercial urinary catheter. The influence of the PVP-reference and MgB2-PVP novel coatings on the bacterial growth of Staphylococcus aureus ATCC 25923, Enterococcus faecium DMS 13590, Escherichia coli ATCC 25922, Pseudomonas aeruginosa ATCC 27853, in planktonic and biofilm state was assessed in vitro at 6, 24, and 48 h of incubation time. The MgB2-PVP coatings are efficient both against planktonic microbes and microbial biofilms. Results open promising applications for the use of MgB2 in the design of anti-infective strategies for different biomedical devices and systems.

On the pinning force in high density MgB2 samples.

An analysis of the field dependence of the pinning force in different, high density sintered samples of MgB2 is presented. The samples were chosen to be representative for pure MgB2, MgB2 with additives, and partially oriented massive samples. In some cases, the curves of pinning force versus magnetic field of the selected samples present peculiar profiles and application of the typical scaling procedures fails. Based on the percolation model, we show that most features of the field dependence of the critical force that generate dissipation comply with the Dew-Hughes scaling law predictions within the grain boundary pinning mechanism if a connecting factor related to the superconducting connection of the grains is used. The field dependence of the connecting function, which is dependent on the superconducting anisotropy, is the main factor that controls the boundary between dissipative and non-dissipative current transport in high magnetic field. Experimental data indicate that the connecting function is also dependent on the particular properties (e.g., the presence of slightly non-stoichiometric phases, defects, homogeneity, and others) of each sample and it has the form of a single or double peaked function in all investigated samples.

Second magnetization peak, rhombic-to-square Bragg vortex glass transition, and intersecting magnetic hysteresis curves in overdoped BaFe2(As1-xPx)2 single crystals.

The second magnetization peak (SMP) in the fourfold symmetric superconducting single crystals (such as iron pnictides and tetragonal cuprates) has been attributed to the rhombic-to-square transition (RST) of the quasi-ordered vortex solid (the Bragg vortex glass, BVG). This represents an alternative to the pinning-induced BVG disordering as the actual SMP mechanism. The analysis of the magnetic response of BaFe2(As1-xPx)2 specimens presented here shows that the SMP is not generated by the RST. However, the latter can affect the pinning-dependent SMP onset field if this is close to the (intrinsic) RST line, through the occurrence of a "shoulder" on the magnetic hysteresis curves m(H), and a maximum in the temperature variation of the DC critical current density. These features disappear in AC conditions, where the vortex system is dynamically ordered in the RST domain, emphasizing the essential role of vortex dislocations for an efficient accommodation of the vortex system to the pinning landscape and the SMP development. The m(H) shoulder is associated with a precipitous pinning-induced proliferation of dislocations at the RST, where the BVG elastic "squash" modulus softens. The DC magnetization relaxation indicates that the pinning-induced vortex system disordering continues above the RST domain, as the basic SMP mechanism.

Reproducibility of small Ge2C6H10O7-added MgB2 bulks fabricated by ex situ Spark Plasma Sintering used in compound bulk magnets with a trapped magnetic field above 5 T.

Bulk discs (20 mm diameter and 4.3 mm thickness) of MgB2 added with Ge2C6H10O7 were obtained by Spark Plasma Sintering. Six samples with composition MgB2(Ge2C6H10O7)0.0014 and one undoped sample were fabricated under similar conditions and were magnetically characterized in order to determine the scattering of properties and reproducibility. The main source of the scattering of the properties is the decomposition of the additive due to elimination of the organic part in gas form, which occurs stepwise with intensive vacuum drops at around ~ 560 and ~ 740 °C. A third drop, which is sometimes not well resolved being part of the second peak at 740 °C, occurs at ~ 820 °C. The critical temperature at the midpoint of the transition, Tc, shows only a relatively small variation between 37.4 and 38 K, and the irreversibility field at a low temperature of 5 K takes values between 8 and 10 T. The pinning force and pinning force related parameters do not correlate with the carbon substituting for boron in MgB2 and suggest a synergetic influence of the microstructural details and carbon. Overall, despite the superconducting properties scattering, the samples are of high quality. Stacked into a column of six samples, they can trap at the center and on the surface of the column a magnetic field of 6.78 and 5.19 T at 12 K, 5.20 and 3.98 T at 20 K and 2.39, and 1.96 T at 30 K. These promising values, combined with facile fabrication of the samples with relatively high quality and reproducibility, show the feasibility of their use in building complex and large compound arrangements for bulk magnets and other applications.