The aim of this study was to determine the effect of sandblasting, grinding and plasma treatment on the adhesive bond strength between framework ceramic (Y-TZP) and veneering ceramic (feldspar ceramic). Therefore, four-point bending specimens (n = 180) were cut from densely sintered 3Y-TZP blanks. Subsequently, 80 of these samples received surface treatment by sandblasting and 80 samples by grinding. A reference group (20 samples) was not processed. Half of the specimens that received a surface treatment were additionally exposed to an oxygen plasma treatment. After processing, all specimens were manually veneered with feldspar ceramic and examined with a four-point bending test to evaluate the strain energy release rate G. The surface treatment parameters that achieved the highest and lowest G were transferred to real geometries of a posterior crown (n = 45). The crowns' ceramic framework was sandblasted and veneered by hand. The all-ceramic crowns were tested in a dynamic loading test and Wöhler curves were evaluated. Four-point bending samples blasted at an angle of 90° at 6 bar and a working distance of 1.5 cm without plasma treatment achieved the highest energy release rate. Samples blasted at an angle of 90° at 2 bar and a working distance of 1 cm with plasma treatment achieved the lowest energy release rate. Overall, plasma treatment did not improve bond strength. In the dynamic loading test, the group blasted with 2 bar showed the best results.