Application of 20% silver nanoclusters in polymethacrylic acid on simulated dentin caries; its penetration depth and effect on surface hardness.

The aims of this study were: To evaluate the surface hardness of simulated dentin caries lesions treated with either silver nanoclusters (AgNCls) synthesized in polymethacrylic acid (PMAA) or 38% silver diammine fluoride (SDF), as well as observe the penetration of the treatment solutions into the simulated caries lesions. Dentin blocks 4 mm thick obtained from caries-free third molars were sectioned and then simulated caries lesions on the occlusal dentin surfaces were created. Each specimen (n = 8) was divided into four sections: (A) treated with 20% AgNCls/PMAA; (B) treated with SDF 38% (FAgamin, Tedequim, Cordoba, Argentina); (C) sound tooth protected by nail-varnish during artificial caries generation (positive control); and (D) artificial caries lesion without surface treatment (negative control). AgNCls/PMAA or SDF were applied on the simulated lesions with a microbrush for 10 s, then excess removed. The surface hardness was measured by means of Vickers indentation test. To trace the depth of penetration, up to 400 µm, of silver ions, elemental composition of the samples was observed using EDX, coupled with SEM, and measured every 50 µm from the surface towards the pulp chamber. Laser Induced Breakdown Spectroscopy (LIBS) was also employed to trace silver ion penetration; the atomic silver line 328.06 nm was used with a 60 µm laser spot size to a depth of 240 µm. Student's-t test identified significant differences between treatment groups for each depth and the Bonferroni test was used for statistical analysis of all groups (p < 0.05). Mean surface hardness values obtained were 111.2 MPa, 72.3 MPa, 103.3 MPa and 50.5 MPa for groups A, B, C and D respectively. There was a significant difference between groups A and C compared with groups B and D, the group treated with AgNCls/PMAA achieved the highest surface hardness, similar or higher than the sound dentin control. A constant presence of silver was observed throughout the depth of the sample for group A, while group B showed a peak concentration of silver at the surface with a significant drop beyond 50 µm. The 20% AgNCls/PMAA solution applied to simulated dentin caries lesions achieved the recovery of surface hardness equivalent to sound dentin with the penetration of silver ions throughout the depth of the lesion.

Color changes and shear bond strength to simulated caries lesions treated with a novel solution of 20% silver nanoclusters in polymethacrylic acid.

The aims of the study were: (1) To compare the staining effect on demineralized dentin simulating caries between silver nanoclusters (AgNCls) synthesized using polymethacrylic acid (PMAA) and silver diammine fluoride (SDF), and (2) to measure the shear bond strength (SBS) of a glass ionomer cement (GIC) to simulated caries lesions with and without the application of AgNCls/PMAA or SDF. Dentine blocks 4 mm thick from twenty-four non-carious third molars were sectioned and coated with nail varnish (Revlon, New York, USA). Simulated caries lesions on occlusal dentin surfaces were created (66 h in 0.05 M acetate buffer 2.2 mM calcium/phosphate pH 5.0). Specimens were divided into groups and treated with (n = 8): (A) 20% AgNCls/PMAA; (B) SDF 38% (Fagamin, Tedequim, Córdoba, Argentina); or (C) without treatment. AgNCls/PMAA or SDF were applied on the exposed surfaces with a microbrush for 10 s. Samples were incubated for 24 h at 37 °C at 100% relative humidity. Surface color was measured according to the CIE-L*a*b* system before and after demineralization (R0 and R1), 24 h and one week after treatment (R2 and R3), using a spectrophotometer (CM-600D Konica Minolta Sesing Inc., Japan). Groups A and B received an extra application of AgNCls/PMAA or SDF before a conventional GIC (Fuji IX-Gold Label, GC Corp, Tokyo, Japan) was bonded using a mold, 4 mm diameter × 3 mm high. For SBS, a Universal Testing Machine (Digimess RS-8000-5, China)-crosshead speed of 1 mm/min-was used. Statistical analysis was performed using ANOVA, Student-t and Scheffe-test at a significance of p < 0.05. Group A presented a stable color p = 0.24 between R1-R2 and R1-R3 in contrast to significant color changes in Group B (p = 0.02). SBS was higher (p < 0.01) in Group A (10.4 ± 2.7 MPa) compared to Groups B (3.3 ± 1.3 MPa) and C (4.0 ± 0.4 MPa), where no differences between the latter groups were observed (p = 0.77). Results of this preliminary study demonstrated that 20% AgNCls/PMAA did not stain simulated carious dentin and improved SBS of the GIC. The relevance of this study relies on the development of a therapeutic system to potentially arrest caries lesions without staining.

Nonrestorative Caries Treatment: A Systematic Review Update.

Caries is the most prevalent chronic noncommunicable disease. Strategies to prevent its onset and early interventions to arrest the progression of early lesions have been emphasised throughout recent decades to avoid or delay the restorative spiral of the tooth. More individuals are retaining their natural teeth into old age, thereby necessitating ongoing restorative dentistry intervention for their maintenance. The aim of this systematic review was to update the state of the art regarding clinical studies reporting the effectiveness of different nonrestorative caries treatment options in the 5-year period from 2017 to 2022. Relevant articles were retrieved from 2 electronic databases, including randomised clinical trials (RCTs) published from January 2017 until April 2022, assessing effectiveness and secondary effects of at least one nonrestorative caries treatment option, carried out with adults and/or children with noncavitated or cavitated carious lesions on either primary or permanent teeth and diagnosed by radiographs or visual/tactile assessment. All 35 included articles presented the results of RCTs with a follow-up period ranging from 6 to 84 months. Most of these studies were considered high-quality articles with a low risk of bias. Sealants and fluoride gels and varnishes were mentioned in 12 studies as effective strategies to prevent the onset of caries lesions and to arrest them in the early stages. Resin infiltration reported high caries arresting rates in noncavitated proximal lesions in 10 publications. Silver diammine fluoride presented high caries-arresting rates in open dentin lesions, both in primary and permanent dentitions as well as in root caries lesions that were accessible for cleansing. New evidence has been published between 2017 and 2022 as the result of numerous clinical studies providing further evidence of the effectiveness of nonrestorative caries treatment options.