Phase stability of Fe-5at%Cr and Fe-10at%Cr films under Fe+ ion irradiation.

This work is within the objective of understanding the effects caused to Fe-Cr alloys by fast Fe ion irradiation. As the penetration length of Fe ion is of the order of hundreds of nanometers, 70 nm Fe-5at%C and Fe-10at%Cr films were irradiated at room temperature with 490 keV Fe+ ions at increasing fluence corresponding to a maximum damage of 50 displacements per atom (dpa). In Fe-5at%Cr alloy the Cr solute concentration remains unaltered even after a damage of 50 dpa. In the 10at%Cr the Cr solute concentration is reduced, with the increase of damage, asymptotically to a value of 7.2 at%.