Takovite-aluminosilicate-Cr materials prepared by adsorption of Cr3+ from industrial effluents as catalysts for hydrocarbon oxidation reactions.

The catalytic efficiency of takovite-aluminosilicate-chromium catalysts obtained by adsorption of Cr(3+) ions from aqueous solutions by a takovite-aluminosilicate nanocomposite adsorbent is reported. The adsorbent was synthesized by the coprecipitation method. The catalytic activity of the final Cr-catalysts depended on the amount of adsorbed chromium. (Z)-cyclooctene conversion up to 90% with total selectivity for the epoxide was achieved when the oxidation was carried out with hydrogen peroxide, at room temperature. After five consecutive runs, the catalysts maintained high activity, although after the sixth reuse, the epoxide yields strongly decreased to 35%. The catalysts were also efficient for cyclohexane oxidation, reaching up to 18% conversion, with cyclohexanone/cyclohexanol selectivity close to 1.2. On the whole, their use as catalysts gives a very interesting application for the solids obtained by adsorption of a contaminant cation such as Cr(3+).

Influence of catalyses on the preparation of YVO4:Eu 3+ phosphors by the sol-gel methodology.

YVO(4):Eu(3+) phosphors have been prepared by the hydrolytic sol-gel methodology, with and without alkaline catalyst. The solid powder was obtained by reaction between yttrium III chloride and vanadium alkoxides; the europium III chloride was used as structural probe. The powder was treated at 100, 400, 600, or 800 °C for 4 h. The samples were characterized by X-ray diffraction, thermal analysis, and photoluminescence. The XRD patterns revealed YVO(4) crystalline phase formation for the sample prepared without the catalyst and heat-treated at 600 °C and for the sample prepared in the presence of ammonium as catalyst and heat-treated at 100 °C. The average nanosized crystallites were estimated by the Scherrer equation. The sample which was produced via alkaline catalysis underwent weight loss in two stages, at 100 and 400 °C, whereas the sample obtained without catalyst presented four stages of weight loss, at 150, 250, 400, and 650 °C. The excitation spectra of the samples treated at different temperatures displayed the charge transfer band (CTB) at 320 nm. PL data of all the samples revealed the characteristic transition bands arising from the (5)D(0) → (5)F(J) (J = 0, 1, 2, 3, and 4) manifolds under maximum excitation at 320, 394, and 466 nm in all cases. The (5)D(0) → (7)F(2) transition often dominates the emission spectra, indicating that the Eu(3+) ion occupies a site without inversion center. The long lifetime suggests that the matrix can be applied as phosphors. In conclusion, the sol-gel methodology is a very efficient approach for the production of phosphors at low temperature.

New highly luminescent hybrid materials: terbium pyridine-picolinate covalently grafted on kaolinite.

Luminescent hybrid materials derived from kaolinite appear as promising materials for optical applications due to their specific properties. The spectroscopic behavior of terbium picolinate complexes covalently grafted on kaolinite and the influence of the secondary ligand and thermal treatment on luminescence are reported. The resulting materials were characterized by thermal analysis, element analysis, X-ray diffraction, infrared absorption spectroscopy, and photoluminescence. The thermogravimetric curves indicated an enhancement in the thermal stability up to 300 °C for the lanthanide complexes covalently grafted on kaolinite, with respect to the isolated complexes. The increase in the basal spacing observed by X-ray diffraction confirmed the insertion of the organic ligands into the basal space of kaolinite, involving the formation of a bond between Al-OH and the carboxylate groups, as evidenced by infrared spectroscopy. The luminescent hybrid material exhibited a stronger characteristic emission of Tb(3+) compared to the isolated complex. The excitation spectra displayed a broad band at 277 nm, assigned to a ligand-to-metal charge transfer, while the emission spectra presented bands related to the electronic transitions characteristic of the Tb(3+) ion from the excited state (5)D(4) to the states (7)F(J) (J=5, 4, and 3), with the 4→5 transition having high intensity with green emission.

New synthesis strategies for effective functionalization of kaolinite and saponite with silylating agents.

Functionalization of Brazilian São Simão kaolinite and Spanish Yunclillos saponite with the alkoxysilanes 3-aminopropyltriethoxysilane and 3-mercaptopropyltrimethoxysilane is reported. The resulting hybrids were characterized by X-ray diffraction, thermal analysis, infrared absorption spectroscopy, and scanning electron microscopy, which demonstrated the effectiveness of the interlamellar grafting process. The X-ray diffractograms revealed incorporation of the alkoxide molecules into the interlayer space of the clays. The displacement of the stretching bands of interlayer hydroxyls in the infrared spectra of the modified kaolinites and the increased intensity of the Mg-OH vibrations in the spectra of the modified saponites confirmed the functionalization of the clays. The thermal behavior of the organoclays confirmed the stability of the hybrids, which was dependent on the clay used for preparation of the materials.

Hybrid materials prepared by interlayer functionalization of kaolinite with pyridine-carboxylic acids.

This paper presents the results of the functionalization of Brazilian São Simão kaolinite with pyridine-2-carboxylic and pyridine-2,6-dicarboxylic acids. The functionalization involved refluxing of the pyridine-carboxylic acid in the presence of kaolinite previously intercalated with dimethyl sulfoxide; both acids effectively displaced dimethyl sulfoxide from the clay interlayer. The resulting materials were characterized by X-ray diffraction, thermal analysis, infrared absorption spectroscopy, and C and N elemental analysis. The X-ray diffractograms revealed the incorporation of the acid molecules into the interlayer space of kaolinite. The thermogravimetric curves of the kaolinite samples functionalized with the pyridine-carboxylic acids indicated that the materials were thermally stable up to 300 degrees C. The displacements of the bands due to interlayer hydroxyls in the infrared absorption spectra also confirmed the functionalization of the kaolinite with the pyridine-carboxylic acids.

Porphyrin-kaolinite as efficient catalyst for oxidation reactions.

The preparation, characterization, and application in oxidation reactions of new biomimetic catalysts are reported. Brazilian Sao Simao kaolinite clay has been functionalized with [meso-tetrakis(pentafluorophenyl)porphinato]iron(III), Fe(TPFPP). To obtain the functionalized clay, the natural clay was purified by dispersion-sedimentation, expanded by insertion of dimethyl sulfoxide (DMSO), and functionalized with amino groups by substitution of DMSO with ethanolamine. These previous steps allowed clay functionalization with Fe(TPFPP), leading to a layered material with a basal spacing of 10.73 A. Clay functionalization with the porphyrin was confirmed by formation of the secondary amine, as demonstrated by FTIR bands at 3500-3700 cm(-1). UV-vis spectroscopy revealed a red shift in the Soret band of the iron porphyrin in the functionalized material as compared to the parent iron porphyrin catalyst in solution, indicating Fe(III)P --> Fe(II)P reduction. The catalytic performance of the functionalized clay was evaluated in the epoxidation of cyclooctene, with complete selectivity for the epoxide (100% epoxide yield), and ketonization of cyclohexane, cyclohexanone being the major product. The novel catalyst was also evaluated in the Baeyer-Villiger (BV) oxidation of cyclohexanone, with 85% conversion of cyclohexanone in epsilon-caprolactone, with total selectivity to epsilon-caprolactone.