On-Line Optical Monitoring of the Mixing Performance in Co-Rotating Twin-Screw Extruders.

The use of real-time techniques to evaluate the global mixing performance of co-rotating twin-screw extruders is well consolidated, but much less is reported on the specific contribution of individual screw zones. This work uses on-line flow turbidity and birefringence to ascertain the mixing performance of kneading blocks with different geometries. For this purpose, one of the barrel segments of the extruder was modified in order to incorporate four sampling devices and slit dies containing optical windows were attached to them. The experiments consisted in reaching steady extrusion and then adding a small amount of tracer. Upon opening each sampling device, material was laterally detoured from the local screw channel, and its turbidity and birefringence were measured by the optical detector. Residence time distribution curves (RTD) were obtained at various axial positions along three different kneading blocks and under a range of screw speeds. It is hypothesized that K, a parameter related to the area under each RTD curve, is a good indicator of dispersive mixing, whereas variance can be used to assess distributive mixing. The experimental data confirmed that these mixing indices are sensitive to changes in processing conditions, and that they translate the expected behavior of each kneading block geometry.

Impact strength of denture base and reline acrylic resins: An in vitro study.

This study evaluated the impact strength of a denture base resin (Lucitone 550-L) and four reline resins (Tokuyama Rebase II-T; Ufi Gel Hard-U; New Truliner-NT, and Kooliner-K), both intact and in a reline combination (L/L, L/T, L/U, L/NT, and L/K). For each group (n = 20), half of the specimens were thermocycled before testing. Charpy tests were performed, and the impact strengths were calculated. Data were analyzed by two-way analyses of variance and Tukey's test (p = 0.05). For the intact groups, mean impact strength values for L (1.65 and 1.50) were significantly higher than those of the reline resins (0.38-1.17). For the relined groups, the highest mean impact strength values were produced by L/T (5.76 and 5.12), L/NT (6.20 and 6.03), and L/K (5.60 and 5.31) and the lowest by L/U (0.76 and 0.78). There were no significant differences between L and L/L. Thermocycling reduced the impact strength of T (from 0.73 to 0.38) and L/L (from 1.82 to 1.56).