RESUMO
The aim of the present in vitro study was to evaluate specific mechanical and physicochemical properties of three calcium silicate-based sealers, BioRoot™ Flow (BRF), CeraSeal (CRS) and TotalFill® (TF). Samples were prepared to evaluate different physicochemical and mechanical properties of the tested sealers. These evaluations were accomplished by investigating the pH changes over time, porosity, roughness, flow properties, compressive strength and wettability. The results were statistically evaluated using one-way analysis of variance. All three sealers demonstrated an alkaline pH from 1 h of immersion in water to 168 h. A higher porosity and hydrophily were detected in BRF samples compared to CRS and TF. No significant difference was found between the tested materials in the flow properties. Lower compressive strength values were observed for BRF compared to TF and CRS. Differently shaped structures were detected on the three materials after 7 days of immersion in PBS. The three materials demonstrated a higher solubility than 3% after 24 h of immersion in water (CRS < BRF < TF). The novel premixed calcium silicate sealer (BRF) had comparable physicochemical properties to the existing sealers. The lower compressive strength values could facilitate the removal of these materials during retreatment procedures. Further studies should investigate the biological effects of the novel sealer.
RESUMO
BACKGROUND: Recently several calcium silicate flowable sealers have been introduced as endodontic materials for the root canal. This clinical study tested the use of a new premixed calcium silicate bioceramic sealer in association with the Thermafil warm carrier-based technique (TF). Epoxy-resin-based sealer with the warm carrier-based technique was the control group. METHODOLOGY: Healthy consecutive patients (n = 85) requiring 94 root canal treatments were enrolled in this study and assigned to one filling group (Ceraseal-TF n = 47, AH Plus-TF n = 47) in accordance with operator training and best clinical practice. Periapical X-rays were taken preoperatively, after root canal filling and after 6, 12 and 24 months. Two evaluators blindly assessed the periapical index (PAI) and sealer extrusion in the groups (k = 0.90). Healing rate and survival rate were also evaluated. Chi-square tests was used to analyze significant differences between the groups. Multilevel analysis was performed to evaluate the factors associated with healing status. RESULTS: A total of 89 root canal treatments in 82 patients were analyzed at the end-line (24 months). The total drop-out was 3.6% (3 patients; 5 teeth). A total of 91.1% of healed teeth (PAI 1-2) was observed in Ceraseal-TF, with 88.6% in AH Plus-TF. No significant difference was observed on healing outcome and survival among the two filling groups (p > 0.05). Apical extrusion of the sealers occurred in 17 cases (19.0%). Of these, 6 occurred in Ceraseal-TF (13.3%) and 11 in AH Plus-TF (25.0%). Three Ceraseal extrusions were radiographically undetectable after 24 months. All the AH Plus extrusions did not change during the evaluation time. CONCLUSIONS: The combined use of the carrier-based technique and premixed CaSi-based bioceramic sealer showed clinical results comparable with carrier-based technique and epoxy-resin-based sealer. The radiographical disappearance of apically extruded Ceraseal is a possible event in the first 24 months.