Dentin permeability after pretreatment with titanium tetrafluoride and self-etching or universal adhesive systems

Aim: To evaluate dentin permeability after pretreatment with 2.5% aqueous solution of titanium tetrafluoride (TiF4), followed by a self-etching universal adhesive system. Methods: Forty dentin discs (1.5 mm thick) were randomly divided into groups according to the application or non-application of a pretreatment, and the type of adhesive system to be tested (two-step self-etching/ Clearfil SE Bond/ Kuraray Medical, or universal adhesive system/ Single Bond Universal/ 3M ESPE). Both sides of the discs were conditioned with 37% phosphoric acid to remove the smear layer. The first hydraulic conductivity measurement (L1) was performed in a permeability machine, under 5 PSI pressure. The samples were sanded again to form a standardized smear layer. The teeth designated for pre-treatment with TiF4 received the TiF4 solutions applied actively for 60 seconds, and the adhesive systems were applied according to the manufacturer's instructions. Then, a new hydraulic conductivity measurement (L2) was performed for the purpose of calculating the hydraulic conductance at a later time, considering the water viscosity and the thickness of the specimen. The percentage (L) of dentin permeability after application of the adhesive system was obtained (L (%) = [(L1-L2) x100] / L1). The Mann-Whitney non-parametric test was applied. Results: There was no difference between the two adhesive systems, or between the groups with or without pretreatment, as regards dentin permeability (p>0.05). Conclusion: Pretreatment with 2.5% TiF4 did not influence dentin permeability, irrespective of the adhesive system used

Physicochemical characterization, water sorption and solubility of adhesive systems incorporated with titanium tetrafluoride, and its influence on dentin permeability.

Titanium tetrafluoride (TiF4) in an aqueous solution can decrease dentin permeability, but some effects of its incorporation into adhesive systems are not yet known. Therefore, the aim of this study was to characterize the physicochemical, water sorption (WS) and solubility (SL) properties of two adhesive systems (Clearfil SE Bond/C and Scotchbond Universal/S) incorporated with 0.0% (T0), 2.5% (T2) and 4.0% (T4) titanium tetrafluoride (TiF4), and determine dentin permeability (L) after application of these adhesive systems both immediately afterwards (baseline) and after 6 months of storage. The physicochemical analyses of the incorporated solutions were performed based on evaluating particle size (PS), polydispersity index (PDI) by dynamic light scattering, and zeta potential (ZP) by electrophoresis. WS and SL tests followed ISO 4049 standards, and used a 7-day water storage period. The L test was performed by analyzing human dentin discs before and after adhesive system application, and after storage. PS and PDI were higher for CT0 and ST4 (p < 0.0001; ANOVA, Tukey). ZP was lower for CT4, ST2 and ST4 (p < 0.0001; ANOVA, Tukey). A 4.0% TiF4 incorporation showed higher WS (p < 0.05; Mann Whitney, Kruskal Wallis, Dunn). Higher SL was observed for CT0 and ST4 (p < 0.05; Mann Whitney, Kruskal Wallis, Dunn). The L value at baseline was lower for ST4, but was not different from the CT4 groups after storage (p < 0.05; Mann Whitney, Kruskal Wallis, Dunn). It can be concluded that TiF4 affected the colloidal stability of Scotchbond, but did not alter the other properties. The 2.5% TiF4 did not affect the PDI, WS or L of the Clearfil, and can be considered an alternative for reducing hybrid layer degradation.