RESUMO
Cellulose nanocrystals (CNC) were obtained from macauba and gravata fibers. Macauba (or Bocaiuva) is a palm tree found throughout most of Brazil and Gravata is an abundant kind of bromelia with 1-2m long leaves, found in Brazilian Pantanal and Cerrado. The raw fibers of both fibers were mercerized with NaOH solutions and bleached; they were then submitted to acid hydrolysis using H2SO4 at 45 °C, varying the hydrolysis time from 15 up to 75 min. The fibers were analyzed by X-ray diffraction (XRD), FTIR Spectroscopy, scanning electron microscopy (SEM) and thermal stability by thermogravimetric analysis (TG). XRD patterns did not present changes in the crystal structure of cellulose after mercerization, but it was observed a decrease of hemicellulose and lignin contents, and consequently an increase of cellulose content with the increase of NaOH solution concentration in the mercerization. After acid hydrolysis, the cellulose nanocrystals (CNC) were also analyzed by transmission electron microscopy (TEM) which showed an acicular or rod-like aspect and nanometric dimensions of CNC from both fibers, but the higher values of aspect ratio (L/D) were found on CNC obtained from gravata after 45 min of acid hydrolysis. The mercerization and subsequent bleaching of fibers influenced the crystallinity index and thermal stability of the resulting CNC, but their properties are mainly influenced by the hydrolysis time, i. e., there is an increase in crystallinity and thermal stability up to 45 min of hydrolysis, after this time, both properties decrease, probably due to the cellulose degradation by the sulfuric acid.
RESUMO
Biodegradable blends of urea plasticized thermoplastic starch (UTPS) and poly(ε-caprolactone) (PCL) were prepared in a co-rotating twin screw extruder. The UTPS and PCL content varied in a range of 25wt%. The materials were characterized by capillary rheometry, scanning electron microscopy (SEM), termogravimetry (TGA), differential scanning calorimetry (DSC) and tensile tests. Capillary rheometry showed better interaction between UTPS and PCL at 110°C than at 130°C. SEM showed immiscibility of all blends and good dispersion of UTPS in PCL matrix up to 50wt%. However, a co-continuous morphology was found for UTPS/PCL 75/25. Thermal analysis showed that introducing PCL in UTPS, increased Tonset due to higher thermal stability of PCL, and blends presented an intermediate behavior of neat polymers. The presence of PCL in blends improved significantly the mechanical properties of neat UTPS. Because they are totally biodegradable, these blends can be vehicles for controlled or slow release of nutrients to the soil while degraded.