Thermally Stimulated Currents in Nanocrystalline Titania.

A thorough study on the distribution of defect-related active energy levels has been performed on nanocrystalline TiO2. Films have been deposited on thick-alumina printed circuit boards equipped with electrical contacts, heater and temperature sensors, to carry out a detailed thermally stimulated currents analysis on a wide temperature range (5-630 K), in view to evidence contributions from shallow to deep energy levels within the gap. Data have been processed by numerically modelling electrical transport. The model considers both free and hopping contribution to conduction, a density of states characterized by an exponential tail of localized states below the conduction band and the convolution of standard Thermally Stimulated Currents (TSC) emissions with gaussian distributions to take into account the variability in energy due to local perturbations in the highly disordered network. Results show that in the low temperature range, up to 200 K, hopping within the exponential band tail represents the main contribution to electrical conduction. Above room temperature, electrical conduction is dominated by free carriers contribution and by emissions from deep energy levels, with a defect density ranging within 1014-1018 cm-3, associated with physio- and chemi-sorbed water vapour, OH groups and to oxygen vacancies.

Leaching behaviour of hazardous waste under the impact of different ambient conditions.

The overall objective of this study is to provide an improved basis for the assessment of the leaching behaviour of waste marked as hazardous partly stabilised (European waste catalogue code 19 03 04∗). Four samples of hazardous partly stabilised waste were subjected to two leaching tests: up-flow column tests and batch equilibrium tests. The research was carried out in two directions: the first aims at comparing the results of the two experimental setups while the second aims at assessing the impact of different ambient conditions on the leaching behaviour of waste. Concerning this latter objective the effect of mesophilic temperature, mechanical constraints and acid environment were tested through column percolation tests. Results showed no significant differences between batch and column leaching test outcomes when comparing average concentrations calculated at a liquid to solid ratio of 10:1 l kg-1 TS. Among the tested ambient conditions, the presence of an acid environment (pH=4.5) accelerated the leaching process resulting in a higher cumulative released quantity measured on the majority of the investigated polluting substances. On the contrary, the effect of temperature and mechanical constraints seemed to not affect the process showing final contents even lower than values found for the standard test. This result was furthermore confirmed by the application of the principal component analysis.

Biochemical methane potential tests of different autoclaved and microwaved lignocellulosic organic fractions of municipal solid waste.

The aim of this research was to enhance the anaerobic biodegradability and methane production of two synthetic Organic Fractions of Municipal Solid Waste with different lignocellulosic contents by assessing microwave and autoclave pre-treatments. Biochemical Methane Potential assays were performed for 21days. Changes in the soluble fractions of the organic matter (measured by soluble chemical oxygen demand, carbohydrates and proteins), the first order hydrolysis constant kh and the cumulated methane production at 21days were used to evaluate the efficiency of microwaving and autoclaving pretreatments on substrates solubilization and anaerobic digestion. Microwave treatment led to a methane production increase of 8.5% for both the tested organic fractions while autoclave treatment had an increase ranging from 1.0% to 4.4%. Results showed an increase of the soluble fraction after pre-treatments for both the synthetic organic fractions. Soluble chemical oxygen demand observed significant increases for pretreated substrates (up to 219.8%). In this regard, the mediocre results of methane's production led to the conclusion that autoclaving and microwaving resulted in the hydrolysis of a significant fraction of non-biodegradable organic substances recalcitrant to anaerobic digestion.