Influence of glass fibre post length and remaining dentine thickness on the fracture resistance of root filled teeth.

AIM: To evaluate, ex vivo, the influence of glass fibre post length and remaining thickness of dentine on the fracture resistance of bovine roots, after thermomechanical ageing. METHODOLOGY: Ninety bovine roots of the same size were root filled and randomly distributed into nine groups (n = 10), according to the root weakening protocol (NW - nonweakened; MW - medium weakened; HW - highly weakened) and post length (7 mm; 9 mm and 12 mm). The weakening of roots was performed using diamond burs, resulting in different thicknesses of remaining dentine. The post spaces were prepared, and in the weakened roots, the glass fibre posts were customized with composite resin, to create posts matching the canal size. Chemically activated resin cement was used to lute the posts. After luting, full crowns made of composite resin were attached to a silicon matrix. To reproduce physiological mobility, the roots were covered with polyether and embedded in polyurethane. The thermomechanical cycling was performed (1 200 000 cycles; 88N; 3,8 Hz; 5 ± 1 °C to 55 ± 1 °C). Then, the specimens were subjected to compressive force in a universal testing machine (1 mm min-1 ; 100 kgf) to analyse the fracture resistance. The specimens were analysed through a stereomicroscope to classify the failure mode (repairable/catastrophic). The values were subjected to statistical analysis (two-way anova and Tukey's test at 5%). The frequencies of failure mode were compared using chi-square test. RESULTS: The association between length and dentine thickness was significant (P > 0.05). The difference was between NW and HW roots for posts of 12 mm in length. There was an association between failure mode and the length and remaining dentine thickness. CONCLUSIONS: Reduced dentine thickness in roots with longer posts had lower fracture resistance values, as catastrophic failure was more predominant.

Ultrasonic activation of internal bleaching agents.

AIM: To evaluate the effectiveness of ultrasonic activation of bleaching agents during ex vivo internal bleaching. METHODOLOGY: Fifty canine human teeth were artificially stained, root filled and divided into five groups (n = 10) that received SP - sodium perborate plus deionized water (control group), CP - 37% carbamide peroxide gel, CPUS - 37% carbamide peroxide gel plus ultrasonic application, HP - 35% hydrogen peroxide gel or HPUS - 35% hydrogen peroxide gel plus ultrasonic application. In groups CP and HP, the bleaching agent was left inside the pulp chamber for three applications of 10 min. In groups CPUS and HPUS, the same process was performed, but ultrasonic vibration was applied to the bleaching agent by an alloy tip for 30 s, with 30 s intervals. Two sessions were performed. The colour was measured initially and after each session by an intraoral dental spectrophotometer. The variation (Δ) of the colour parameters based on the CIELab system L*, a* and b*, and the colour alteration ΔE* were calculated after first and second section. Data were analysed by one-way anova and Tukey's test. RESULTS: There was no significant difference amongst groups for ΔL*, Δa* and ΔE*, but there was a significant difference for Δb* in the first and second sessions (P = 0.0006 and 0.0016, respectively). After the first session, Δb* was significantly greater for groups HP and HPUS, without a significant difference between them. For the second session, group HPUS had the greatest Δb* values, but they were similar to groups HP and SP; group CP had the lowest values, which were similar to groups CPUS and SP. CONCLUSION: Ultrasonic activation of bleaching agents during ex vivo internal bleaching was no more effective than conventional internal bleaching procedures, without activation.

Antimicrobial analysis of chlorhexidine gel and intracanal medicaments against microorganisms inoculated in root canals.

AIM: The aim of this paper was to evaluate the antimicrobial activity of 2% chlorhexidine gel (CLX) associated with various intracanal medicaments against Candida albicans and Enterococcus faecalis inoculated in root canals. METHODS: Thirty six human single-rooted teeth were contaminated with C.albicans and E.faecalis. The canals were instrumented using 2% CLX gel and were divided into three groups according to the intracanal medicaments (ICM) used. Group 1: calcium hydroxide paste [Ca(OH)2], Group 2: 2% chlorhexidine gel (CLX) and Group 3: 2% CLX gel + Ca(OH)2. The root canal collections were performed after 21 days of contamination (control collection), after instrumentation (1st collection), after 14 days of intracanal medicament (2nd collection) and 7 days after medicament removal (3rd collection). The microbiological samples were plated in culture media and incubated for 48 hours. The results were submitted to Kruskal-Wallis test (P ≤ 0.05). RESULTS: It was verified that the instrumentation with CLX reduced the number of CFU/ml significantly when compared with the confirmation collection (control). However, the use of the ICM was only capable to eliminate completely the microorganisms in the root canals without difference statistics between them. CONCLUSION: Although the use of 2% chlorherixidine gel reduces the number of microorganisms significantly, only the ICM calcium hydroxide and calcium hydroxide associated with chlorhexidine are able to eliminate these microorganisms completely.

Structural resistance in immature teeth using root reinforcements in vitro.

The purpose of this study was to evaluate in vitro the efficacy of root reinforcements by light-cured composite resin or zirconium fiber post in simulated immature non-vital teeth. Fifty-six bovine incisors teeth were used for this study. The crown of each tooth was removed in the medium third to obtain a standard length of 30 mm. The specimens were divided into four groups (n = 14): G1) the root canals were instrumented and enlarged to simulate immature non-vital teeth and were reinforced with a light-cured composite resin using a translucent curing post (Luminex system); (G2) the specimens were instrumented, enlarged and they received root reinforcement with zirconium fiber post; G3 (positive control): they received similar treatment to the G1 and G2 groups, but did not receive root reinforcement; G4 (negative control): the roots were not weakened and did not receive reinforcement. Every tooth was submitted to compressive force using an Instron testing machine with an angle of 45 degrees at a speed of 1 mm min(-1) until the fracture. The results showed a markedly increased resistance to fracture in the G1 and G2 (122.38 and 122.08 kg f, respectively). Among the results of G1 and G2 there was not any significant difference (P > 0.05) but they were significantly different from the control groups (P < 0.05). The conclusion is that the use of root reinforcements with zirconium fiber post or composite resin can increase significantly the structural resistance of the weakened teeth, decreasing the risk of the fracture.