Microstructure and chemical composition of Roman orichalcum coins emitted after the monetary reform of Augustus (23 B.C.).

A collection of ancient Roman orichalcum coins, i.e., a copper-zinc alloy, minted under the reigns from Caesar to Domitianus, have been characterised using scanning electron microscopy (SEM-EDS) and electron microprobe analysis (EMPA). We studied, for the first time, coins emitted by Romans after the reforms of Augustus (23 B.C.) and Nero (63-64 A.D). These coins, consisting of asses, sestertii, dupondii and semisses, were analysed using non- and invasive analyses, aiming to explore microstructure, corrosive process and to acquire quantitative chemical analysis. The results revealed that the coins are characterized by porous external layers, which are affected by dezincification and decuprification processes. As pictured by the X-ray maps, the elemental distribution of Cu and Zn shows patterns of depletion that in some cases penetrate in deep up to 1 mm. The composition of the un-corroded nucleus is a Cu-Zn alloy containing up to 30% of Zn, typical of coins produced via cementation process.

FIB-FESEM and EMPA results on Antoninianus silver coins for manufacturing and corrosion processes.

A set of ancient Antoninianus silver coins, dating back between 249 and 274 A.D. and minted in Rome, Galliae, Orient and Ticinum, have been characterized. We use, for the first time, a combination of nano-invasive (focused ion beam-field emission scanning electron microscopy-X-ray microanalysis (FIB-FESEM-EDX), voltammetry of microparticles (VIMP)) and destructive techniques (scanning electron microscopy (SEM-EDX) and electron microprobe analysis (EMPA)) along with non-invasive, i.e., micro-Raman spectroscopy. The results revealed that, contrary to the extended belief, a complex Ag-Cu-Pb-Sn alloy was used. The use of alloys was common in the flourishing years of the Roman Empire. In the prosperous periods, Romans produced Ag-Cu alloys with relatively high silver content for the manufacture of both the external layers and inner nucleus of coins. This study also revealed that, although surface silvering processes were applied in different periods of crisis under the reign of Antoninii, even during crisis, Romans produced Antoninianus of high quality. Moreover, a first attempt to improve the silvering procedure using Hg-Ag amalgam has been identified.

X-Ray Fluorescence Analysis and Self-Organizing Maps Classification of the Etruscan Gold Coin Collection at the Monetiere of Florence.

The "Monetiere" of Florence hosts the most important collection of Etruscan coins in the world. In the framework of the longstanding collaboration between the Monetiere and the Applied Laser and Spectroscopy Laboratory in Pisa, the Etruscan gold coin collection of the museum was studied. The measurements were performed at the Monetiere, using a portable energy-dispersive X-ray fluorescence (XRF) instrument. The quantitative determination of the gold alloys used for the realization of the coins was obtained applying the fundamental parameters method to the XRF spectra; as a result, using the self-organizing maps method, we were able to classify the coins in four main groups. The main parameter determining the classification is the quantity of silver in the alloy. The results obtained shed some light about the origin of the coins under study.