Cytotoxicity evaluation of a new ozonized olive oil.

OBJECTIVE: The cytocompatibility of a new ozonized olive oil toward immortalized human gingival fibroblasts (HGFs) was evaluated and compared with two common antimicrobial agents based on chlorhexidine digluconate (CHX). MATERIALS AND METHODS: The cytocompatibility of the samples was tested on immortalized HGF-1 cells by 3-(4, 5-dimethyl thiazolyl-2)-2,5-diphenyltetrazolium bromide (MTT) assay. The cells were incubated for 2 or 24 h with increasing dilution of ozonized olive oil or CHX agents. The percentage of viable cells was calculated relative to control cells set to 100%. RESULTS: The ozonized olive oil is cytocompatible, and the viability values of the cells treated for 2 or 24 h with increasing concentrations of ozonized olive oil were significantly higher (P < 0.01) compared with the values obtained using CHX. CONCLUSIONS: The present data demonstrate that due to its cytocompatibility, the new ozonized olive oil could be considered an alternative antibacterial agent.

Effect of different surface finishing/polishing procedures on color stability of esthetic restorative materials: A spectrophotometric evaluation.

OBJECTIVE: To evaluate the color stability of different esthetic restorative materials after surface finishing/polishing with different procedures. MATERIALS AND METHODS: All materials were polymerized into silicone rubber rings to obtain specimens identical in size. Samples were randomly assigned into four groups (10 specimens of each composite for each group), and they were finished with different procedures: Control group (Group 1), three or two polishers interspersed with diamond grit (Groups 3 and 2, respectively), and one tungsten carbide bur + one polisher interspersed with diamond grit (Group 4). After staining process in coffee, a colorimetric evaluation according to the CIE L*a*b* system was performed by a blind trained operator at 7, 14, 21, and 28 days. Shapiro-Wilk test and Kruskal-Wallis analysis of variance were applied to assess significant differences among restorative materials. Means of the different polishing/finishing groups were compared with Scheffe's multiple comparison test at the 0.05 level of significance. RESULTS: In control group, significant lower discolorations were recorded for Essentia, Admira Fusion, and Estelite. After finishing, Filtek Supreme XTE and Ceram.X Universal showed a significantly lower degree of staining. The finishing technique used for Group 4 produced higher color changes. CONCLUSIONS: Tungsten carbide burs produced the higher color variations; after finishing, the nanofilled composites showed lower discoloration than nanohybrid ones, and the time of exposure to the staining agent and the polishing/finishing technique influenced the color change.

Evaluation of the antibacterial activity of a new ozonized olive oil against oral and periodontal pathogens.

BACKGROUND: In the present study, the antimicrobial properties of a new ozonized olive oil (O-zone gel) against oral and periodontal pathogens will be evaluated and compared with that of common CHX-based agents. MATERIAL AND METHODS: O-zone gel was compared with two agents based on chlorhexidine digluconate (CHX): Corsodyl Dental Gel and Plak Gel. A. actinomycetemcomitans, P. intermedia and S. mutans, were selected and the antibacterial capability of the compounds was tested by using direct contact agar diffusion test (DCT) and minimum inhibitory concentration (MIC) and minimum bactericidal concentration (MBC) evaluations. Differences between specific means were analyzed by a one-way analysis of variance (ANOVA). Group means were compared using a one-way ANOVA and Tukey's test (P<0.05). RESULTS: O-zone gel reported inhibition zones which correspond to 33% and 43% of that achieved by the CHX agents. No inhibition of bacterial growth (MIC) on the Gram-positive strain by using O-zone gel was found and no antimicrobial effect (MBC) was observed by using O-zone gel on both Gram-negative and -positive strains. CONCLUSIONS: The new ozonated oil was a relatively moderate antiseptic. Gram-negative bacteria proved to be more sensitive to ozonized olive oil than Gram-positive ones. The ozonized olive oil demonstrated a lower antibacterial activity if compared to the CHX-based agents tested. Key words:Agar diffusion test, antibacterial activity, direct contact test, ozone, ozonized olive oil.

Solubility and pH of bioceramic root canal sealers: A comparative study.

BACKGROUND: This study compared the solubility and the pH of different root canal sealers in vitro. MATERIAL AND METHODS: BioRoot™RCS, TotalFill BC Sealer, MTA Fillapex, SealapexTM, AH Plus, EasySeal, Pulp Canal Sealer™ and N2 were tested. Similar specimens were prepared using ring molds with an internal diameter of 20 ± 0,1 mm and a height of 1,5 ± 0,1 mm and digitally weighted to register the mass of each specimen before and after immersion in distilled water. Solubility was determined after 24 hours and statistically analysed using a one-way ANOVA test and post-hoc Tukey test. The pH value was measured by a digital pH meter after 3 and 24 hours from manipulation. RESULTS: BioRoot™RCS and TotalFill BC Sealer showed significantly higher solubility (P<0.05). All the remnant root canal sealers fulfilled the requirements of solubility of the International Standard Organization 6876 demonstrating a weight loss of less than 3%. BioRoot™RCS and Totalfill BC Sealer exhibited high alkaline pH over time (P<0.05); the alkalinity of the other tested cements was significantly lower. CONCLUSIONS: The prolonged alkalinity of bioceramic sealer matched the increase in solubility. This may encourage their biological and antimicrobial effects, but the ongoing solubility may impact their ability to prevent apical leakage. Key words:pH, root canal sealers, solubility.

Discoloration of different esthetic restorative materials: A spectrophotometric evaluation.

OBJECTIVE: A crucial property of esthetic restorative materials is their long-term color stability. The aim of this in vitro study was to evaluate the color stability of esthetic restorative materials (one microfilled flowable composite, one nanofilled composite, one nanoybrid composite, one microfilled composite, and one nanoybrid ormocer-based composite) after surface roughening with cola and exposure to different staining solutions (coffee and red wine). MATERIALS AND METHODS: All materials were polymerized into silicone rubber rings (2 mm × 6 mm × 8 mm) to obtain 150 specimens identical in size. Seventy-five specimens of Group A were first exposed to cola for 24 h, and then samples were immersed in coffee or red wine over a 28-day test period. A colorimetric evaluation, according to the CIE L*a*b* system, was performed at 7, 14, 21, 28 days. Shapiro-Wilk test and Kruskal-Wallis analysis of variance were applied to assess significant differences among restorative materials. Means were compared with Scheffe's multiple comparison test at the 0.05 level of significance. RESULTS: Specimens of Group A showed higher variations when compared with Group B's specimens (P < 0.05). After 28 days, the immersion protocols caused a clinically perceivable color change for all materials tested (P < 0.05). CeramX Universal and Admira Fusion showed the lowest ΔE variations (P < 0.05). CONCLUSIONS: Staining beverages caused significant discolorations for all the materials tested. The first exposure to cola enhanced the subsequent staining with coffee or red wine. Nanohybrid composites reported the lowest color variations.

Antibacterial activity of different root canal sealers against Enterococcus faecalis.

BACKGROUND: The aim of the present study was to compare in vitro the antimicrobial activity of different root canal sealers against Enterococcus faecalis, prior and subsequent to setting. MATERIAL AND METHODS: Agar diffusion test (ADT) was used for evaluating the antibacterial activity of non-set sealer while the direct contact test (DCT) was used for after setting. RESULTS: ADT: Except for TotalFill BC Sealer all the others sealers tested showed antibacterial activity. BioRoot™RCS, MTA Fillapex and Sealapex Root Canal Sealer showed the lowest antibacterial activity, a significant increase in antibacterial effect for both Pulp Canal Sealer™ and AH plus sealers were found. Significantly higher were the mean diameters of the bacterial inhibition zone by both EasySeal or N2 sealers. DCT: AH plus and Sealapex Root Canal Sealer doesn't show any bactericidal effect after 6 min of contact. After 15 and 60 min of contact a significant increment for AH plus and for Sealapex Root Canal Sealer of the bactericidal effect was found. Significantly much higher was the antibacterial effect of Sealapex Root Canal Sealer compare to that observed for AH plus. BioRootTMRCS, MTA Fillapex, Pulp Canal Sealer™ and N2 showed at least means of the number of colonies formed in milliliter after 6 min of contact. Except for N2, a significant increase in bactericidal effect after 15 and 60 min for the other compared sealers (BioRootTMRCS, MTA Fillapex and Pulp Canal Sealer™). CONCLUSIONS: For every contact times considered, both TotalFill BC Sealer and EasySeal were bactericidal against E. faecalis and killed all bacteria. Key words:Agar diffusion test, antibacterial activity, direct contact test, Enterococcus faecalis, root canal sealer.

Biological and antibacterial properties of a new silver fiber post: In vitro evaluation.

BACKGROUND: The incorporation of nano silver particles (AgNPs) to improve antibacterial properties of dental materials has become increasingly common. The aim of the present study was to compare the antibacterial activity and cytotoxicity effects of different fiber posts: glass fiber post, quartz fiber post, nano fiber post and silver fiber post. MATERIAL AND METHODS: The antibacterial activity against S. mutans, S. salivarius and S. sanguis was evaluated by using the agar disc diffusion test (ADT). Four wells of 3x2 mm (one for each material) were made with a punch by removing the agar and filled with the materials to be evaluated. The size of the inhibition zone was calculated. An extract was made eluting the posts in cell culture medium using the surface area-to-volume ratio of approximately 1.25cm²/ml between the surface of the samples and the volume of medium. Cell cultures were then exposed to 100 µL of the extracts medium. After 24 h, cell viability was determined using the MTT assay. RESULTS: Silver fiber post was the only material showing a fair antibacterial effect against all the three streptococcal strains. The level of cytotoxicity of all the fiber posts tested was higher than 90% and therefore they were considered not cytotoxic. CONCLUSIONS: The new silver fiber post reported a fair antibacterial activity. On the other hand all the fiber posts tested (including the post with incorporated AgNPs) proved to be biocompatible, suggesting that their application does not represent a threat to human health. Key words:Antibacterial activity, agar disc diffusion test, biocompatibility, fiber post, MTT test.

Resin infiltrant for non-cavitated caries lesions: evaluation of color stability.

BACKGROUND: The objective of this in vitro study was to evaluate the over time color stability of one resin infiltrant (Icon) upon exposure to staining solutions (coffee and wine) compared with one nano-hybrid sealant (Grandio Seal), one transparent fissure sealant with fluoride (Control Seal) and one nanofilled composite (Filtek Supreme XTE). MATERIAL AND METHODS: All materials were polymerized according to manufacturers' instructions into silicon rings (height 1 mm; internal diameter 6 mm; external diameter 8 mm) to obtain specimens identical in size. The specimens were immersed in staining solutions at room temperature over a 28-day test period. The control samples have not been subjected to the staining process. A colorimetric evaluation according to the CIE L*a*b* system was performed by a blind trained operator at 7, 14, 21, 28 days of the staining process. Shapiro Wilk test and Kruskal Wallis ANOVA were applied to assess significant differences among different materials. Means were compared with Scheffe's multiple-comparison test at the 0.05 level of significance. RESULTS: In the case of all materials, immersion in solutions resulted in clinically perceivable color changes after 1 week (∆E < 3.3). Lowest CIE L* variation was registered for Control Seal and Grandio Seal both after 1 week and after 1 month, while Icon showed significantly higher variation (P < 0.05). Color coordinate CIE a* varied significantly more for Icon samples (P > 0.05). Color coordinate CIE b* varied similarly for all materials tested (P > 0.05). CONCLUSIONS: Immersion in coffee or red wine resulted in clinically perceivable color changes for all materials tested. Icon showed the highest color variations both after 1 week and 1 month. Icon can fix the initial esthetic problem associated with white spot lesions, but the resin may become more discolored than other materials over time. Key words:CIE Lab, color stability, resin infiltrant.

Fluoride release and uptake abilities of different fissure sealants.

BACKGROUND: The long-term capability of resin sealants and glass ionomer cements to release fluoride is associated to a reduction in pit and fissure caries. The regular use of fluoride varnishes/toothpastes can result in the absorption of fluoride into the sealant. The objective of the present study was to assess the fluoride release/uptake capacities of different fissure sealants. MATERIAL AND METHODS: Three different fissure sealants (Fuji Triage/GC, Fissurit FX/Voco and Grandio Seal/Voco) were examined. Ten discs of each material were prepared. Each disc was incubated with distilled water and then the solution analyzed for diluted for fluoride concentration, using a combination of fluoride electrode (OrionGP 1 S/N 13824, Orion Research Inc, Boston, MA, USA) connected to an expandable ion analyzer (Orion 720A, Orion Research Inc, Boston, MA, USA). Standard curves between 1 and 100 ppm F- were used to calibrate the electrode. Cumulative fluoride release was measured on days 1, 2, 3, 5, 7, 21, 35 and 49, then two different fluoride varnishes/pastes (Profluorid Varnish/Voco, MI Paste Plus/GC), were applied to the sealants tested, and fluoride release (after reuptake) was measured on days 56, 70 and 84. RESULTS: Kruskal Wallis test confirmed significant differences in fluoride release between Fuji Triage/GC and Fissurit FX/Voco and Grandio Seal/Voco from day 1 (P < 0.001). The application of fluoride varnish Profluorid Varnish enhanced the fluoride release for all sealants (P < 0.05). MI Paste Plus enhanced the fluoride release for all sealants except for Fuji Triage/GC (P > 0.05). CONCLUSIONS: The GIC-based sealant (Fuji Triage/GC) released significantly more fluoride than the resin sealants tested. The exposure to the fluoridated varnish (Profluorid Varnish) significantly recharged the sealants tested more than the CPP-ACPF toothpaste (MI Paste Plus). KEY WORDS: Fissure sealants, fluoride release, fluoride uptake, glass ionomer cements.

Influence of different luting protocols on shear bond strength of computer aided design/computer aided manufacturing resin nanoceramic material to dentin.

BACKGROUND: The purpose of this study was to evaluate the influence of three different luting protocols on shear bond strength of computer aided design/computer aided manufacturing (CAD/CAM) resin nanoceramic (RNC) material to dentin. MATERIALS AND METHODS: In this in vitro study, 30 disks were milled from RNC blocks (Lava Ultimate/3M ESPE) with CAD/CAM technology. The disks were subsequently cemented to the exposed dentin of 30 recently extracted bovine permanent mandibular incisors. The specimens were randomly assigned into 3 groups of 10 teeth each. In Group 1, disks were cemented using a total-etch protocol (Scotchbond™ Universal Etchant phosphoric acid + Scotchbond Universal Adhesive + RelyX™ Ultimate conventional resin cement); in Group 2, disks were cemented using a self-etch protocol (Scotchbond Universal Adhesive + RelyX™ Ultimate conventional resin cement); in Group 3, disks were cemented using a self-adhesive protocol (RelyX™ Unicem 2 Automix self-adhesive resin cement). All cemented specimens were placed in a universal testing machine (Instron Universal Testing Machine 3343) and submitted to a shear bond strength test to check the strength of adhesion between the two substrates, dentin, and RNC disks. Specimens were stressed at a crosshead speed of 1 mm/min. Data were analyzed with analysis of variance and post-hoc Tukey's test at a level of significance of 0.05. RESULTS: Post-hoc Tukey testing showed that the highest shear strength values (P < 0.001) were reported in Group 2. The lowest data (P < 0.001) were recorded in Group 3. CONCLUSION: Within the limitations of this in vitro study, conventional resin cements (coupled with etch and rinse or self-etch adhesives) showed better shear strength values compared to self-adhesive resin cements. Furthermore, conventional resin cements used together with a self-etch adhesive reported the highest values of adhesion.

Effect of glycine pretreatment on the shear bond strength of a CAD/CAM resin nano ceramic material to dentin.

BACKGROUND: The purpose of this study was to evaluate the effect of glycine pretreatment on the shear bond strength between dentin and a CAD/CAM resin nano ceramic material (LavaTM Ultimate Restorative), bonded together with adhesive cements using three different luting protocols (total-etch; self-etch; self-adhesive). MATERIAL AND METHODS: Thirty cylinders were milled from resin nano ceramic blocks with CAD/CAM technology. The cylinders were subsequently cemented to the exposed dentin of 30 bovine permanent mandibular incisors. The specimens were assigned into six groups of five teeth each according to luting procedure and dentin pretreatment. In the first two groups (A1, A2) 10 cylinders were cemented using a total-etch protocol; in groups B1 and B2, 10 cylinders were cemented using a self-etch protocol; in groups C1 and C2, 10 cylinders were cemented using a self-adhesive protocol; in groups A1, B1 and C1 the dentinal surface was also treated with glycine powder. All cemented specimens were submitted to a shear bond strength test. Statistical analysis was performed with Stata 9.0 software. RESULTS: ANOVA showed the presence of significant differences among the various groups (P <0.0001). CONCLUSIONS: Glycine did not change the different bond strength demonstrated by the various luting protocols tested. Conventional resin composite cements used together with a self-etch adhesive reported the highest values. However the use of glycine seems to increase the bond strength of self-adhesive resin cements. KEY WORDS: Adhesive cements, CAD/CAM, glycine, luting system, resin nano ceramic, shear bond strength.

Effect of self-assembling peptide P11 -4 on enamel erosion: AFM and SEM studies.

The aim of the present in vitro study was to evaluate the protective effect of self-assembling peptide P11 -4 (Curodont™ Protect/Credentis) on enamel erosion produced by a soft-drink, by using Atomic Force Microscopy (AFM) and Scanning Electron Microscopy (SEM). Thirty human incisors were equally and randomly assigned to 6 groups. Group 1: intact enamel, group 2: soft drink, group 3: Curodont(™) Protect applied, group 4: Curodont(™) Protect applied + soft drink, group 5: soft drink + Curodont(™) Protect applied, group 6: soft drink + Curodont(™) Protect applied + soft drink. Specimens were observed through atomic force microscopy (AFM). The root mean-square roughness (Rrms) was obtained from the AFM images and the differences in the averaged values among the groups were analyzed by Shapiro-Wilk test in order to assess the normality of the distribution. Parametric ANOVA and post hoc Tuckey test were performed to assess the differences between the different groups. After demineralization process, enamel demonstrated a high degree of surface porosity. This morphological aspect was reflected in the increase of Rrms values. No significant differences (p > 0.05) were reported between intact enamel and enamel only treated with P11 -4 and between eroded enamel and enamel treated with P11 -4 and then demineralized. However significant differences (p < 0.05) were recorded when comparing softened enamel with softened enamel further remineralized with biomimetic self-assembling peptides and enamel treated with the protective paste between two acid attacks. The use of P11 -4 remineralizing may offer a degree of protection from enamel erosion. SCANNING 38:344-351, 2016. © 2015 Wiley Periodicals, Inc.

Ultrastructural evaluation of enamel surface morphology after tooth bleaching followed by the application of protective pastes.

The aim of the present in vitro study was to evaluate the morphology of bleached enamel surface followed by the application of different protective pastes. Specimens were prepared from 50 human incisors free of caries and defects. The bleaching procedure was performed with 35% hydrogen peroxide (Perfect Bleach Office+). For the remineralization treatment, different protective pastes (Tooth Mousse, MI Paste Plus, Remin Pro, and Profluorid Varnish) were evaluated. Specimens were randomly assigned to 10 groups of 5 specimens each. The specimens were analyzed under scanning electron microscopy. The superficial morphology of enamel was examined and scored as follows: 0, enamel with smooth surface morphology; 1, enamel with slight irregularities; 2, enamel with moderate irregularities; 3, enamel with accentuated irregularities. The photomicrographs were evaluated in a double-blind manner by three examiners, previously calibrated. Results were analyzed by a Kruskal-Wallis nonparametric test, at the significance level of 0.05. Dunn method posttest was applied for multiple comparisons. A different superficial morphology was observed among control group specimens and specimens treated with bleaching agent and protective pastes (p < 0.05). Enamel bleached showed pronounced surface changes and irregularities, significantly different from other groups except for groups 8 (enamel + Perfect Bleach Office+ + Remin Pro) and 10 (enamel + Perfect Bleach Office+ + Profluorid Varnish) (p > 0.05). The application of the tested pastes after bleaching is effective on repairing enamel surface morphology, demonstrating a higher efficacy for the CPP-ACP products compared to fluoridated ones. SCANNING 38:221-226, 2016. © 2015 Wiley Periodicals, Inc.

Color stability of esthetic restorative materials: a spectrophotometric analysis.

Objective: The aim of this in vitro study was to evaluate the color stability of different restorative materials (one microfilled composite, one nanofilled composite, one nanohybrid composite and one Ormocer-based composite) after exposure to different staining solutions (coffee, coca-cola and red wine). Material and methods: All materials were polymerized into silicon rings (2 mm ×6 mm ×8 mm) to obtain specimens identical in size. Thirty cylindrical specimens of each material were prepared. They were immersed in staining solutions over a 28-day test period. A colorimetric evaluation according to the CIE L*a*b* system was performed by a blind trained operator at 7, 14, 21, 28 days of the staining process. The Shapiro-Wilk test and Kruskal-Wallis ANOVA were applied to assess significant differences among restorative materials. The paired t-test was applied to test which CIE L*a*b* parameters significantly changed after immersion in staining solutions. Results: All restorative materials showed clinically perceptible color differences after immersion in coffee. L* and b* values showed the highest variability. Coca cola and red wine did not influence the color stability for all restorative materials except for Filtek Supreme XTE. Conclusions: Coffee caused a significant color change in all types of tested composite resins. Filtek Supreme XTE demonstrated alone a staining susceptibility to red wine; no other significant differences among the materials were demonstrated. Long-term exposure to some food dyes (coffee in particular) can significantly affect the color stability of modern esthetic restorative materials regardless of materials' different composition.

In vitro antibacterial activity of different pulp capping materials.

BACKGROUND: Direct pulp capping involves the application of a dental material to seal communications between the exposed pulp and the oral cavity (mechanical and carious pulp exposures) in an attempt to act as a barrier, protect the dental pulp complex and preserve its vitality. The aim of this study was to evaluate and compare, by the agar disc diffusion test, the antimicrobial activity of six different pulp-capping materials: Dycal (Dentsply), Calcicur (Voco), Calcimol LC (Voco), TheraCal LC (Bisco), MTA Angelus (Angelus), Biodentine (Septodont). MATERIAL AND METHODS: Streptococcus salivarius, Streptococcus sanguis and Streptococcus mutans strains were selected to evaluate the antimicrobial activity by the agar disc diffusion test of different pulp capping materials. Paper disks were impregnated whit each pulp capping materials and placed onto culture agar-plates pre-adsorbed with bacterial cells and further incubated for 24 h at 37°C. The growth inhibition zones around each pulp capping materials were recorded and compared for each bacterial strain. RESULTS: For the investigation of the antibacterial properties the ANOVA showed the presence of significant differences among the various materials. Tukey test showed that MTA-based materials induced lower growth inhibition zones. CONCLUSIONS: MTA-based products show a discrete antibacterial activity varying from calcium hydroxide-based materials which present an higher antibacterial activity. KEY WORDS: Agar disc diffusion test, antimicrobial activity, calcium hydroxide, MTA, pulp capping materials.

Viscosity of endodontic irrigants: Influence of temperature.

BACKGROUND: The aim of this study was to assess the influence of temperature on the viscosity of different endodontic irrigants. MATERIALS AND METHODS: The measurements of viscosity of 3% hydrogen peroxide, 0.9% sodium chloride, aqueous solution of 0.2% chlorhexidine (CHX) and 0.2% cetrimide, 5% sodium hypochlorite (NaOCl) and 17% ethylenediaminetetraacetic acid (EDTA) at different temperatures (22°C, 30°C, 40°C, 50°C and 60°C) were obtained using Mohr balance and Ostwald viscometer. The Shapiro-Wilk test and Mann-Whitney U-tests were used for the statistical analysis. (α = 0.05). RESULTS: No significant differences were recorded at each temperature among 3% hydrogen peroxide, 0.9% sodium chloride and aqueous solution of 0.2% CHX and 0.2% cetrimide. 5% NaOCl and 17% EDTA showed the higher values. Viscosity statistically decreased with increasing temperature. CONCLUSION: Within the limitations of this study, 5% NaOCl and 17% EDTA are significantly viscous at room temperature and their viscosity reduces with elevating temperature.

In vitro cytotoxicity evaluation of different pulp capping materials: a comparative study.

Direct pulp capping covers the exposed surface of the pulp to maintain its vitality and preserve its functional and biologic activity. The aim of the present study was to compare the biocompatibility effects of seven different pulp-capping materials in vitro: Dycal®, Calcicur®, Calcimol LC®, TheraCal LC®, ProRoot MTA®, MTA-Angelus®, and Biodentine®. Using the Transwell insert methodology by Alamar blue test, we evaluated the cytocompatibility of the above mentioned materials towards murine odontoblasts cells (MDPC-23) at three different times (24, 48, and 72 h). For additional control, the cell viability at 72 hours was also assessed by MTT assay. Morphological analysis of murine odontoblasts was assessed by Confocal Laser Scanning Microscope. The results indicate significantly different biocompatibility among materials with different composition. Biodentine® and mineral trioxide aggregate (MTA)-based products showed lower cytotoxicity, varying from calcium hydroxide-based materials, which exhibited higher cytotoxicity. Although our findings are limited to in vitro conditions, the observation that Biodentine® caused a cytotoxic effect similar to MTA suggests that it may be considered an alternative in pulp-capping treatment, as calcium hydroxide-based materials present higher cytotoxic effects.

Protective effect of casein phosphopeptide-amorphous calcium phosphate on enamel erosion: Atomic force microscopy studies.

The aim of this study was to investigate the in vitro effect of a casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) paste (GC Tooth Mousse- TM, GC Corporation, Tokyo, Japan) on preventing enamel erosion, by using Atomic Force Microscopy (AFM). 30 human incisors, were equally assigned to 6 groups: intact enamel, enamel + soft drink, enamel + TM, enamel + TM + soft drink, enamel + soft drink + TM, enamel + soft drink + TM + soft drink. Specimens were observed through atomic force microscopy (AFM). The most common topographical parameters were determined, such as the surface roughness (Rrms ). The use of soft drink on intact enamel has roughened the surface of the sample. The application of the CPP-ACP paste on non-treated enamel made the surface smoother. A significant decrease in roughness was seen after remineralization with CPP-ACP paste. Significant differences were recorded when comparing softened enamel with softened enamel remineralized with CPP-ACP paste. Comparing eroded enamel with demineralized/remineralized specimens, the application of a CPP-ACP paste leads to a significant reduction in roughness values. AFM images of enamel surface treated with CPP-ACP resulted in less morphological changes of the tooth substrate when compared with the only eroded enamel surface morphology; thus, indicating that CPP-ACP paste promoted remineralization. Specimens' surface roughness remained similar regardless that the protective agent is used before or after exposure to coke or between two demineralizing cycles. The results confirmed the effectiveness of the CPP-ACP paste on preventing enamel erosion produced by soft drinks.

Biological and chemical-physical properties of root-end filling materials: A comparative study.

AIM: The purpose of the study is to evaluate and compare the biological and chemical-physical properties of four different root-end filling materials. MATERIALS AND METHODS: Cytotoxicity towards murine odontoblasts cells (MDPC-23) was evaluated using the Transwell insert methodology by Alamar blue test. Streptococcus salivarius, S. sanguis, and S. mutans strains were selected to evaluate the antimicrobial activity by agar disc diffusion test. Solubility was determined after 24 h and 2 months. pH values were measured after 3 and 24 h. To evaluate radiopacity, all materials were scanned on a GE Healthcare Lunar Prodigy. RESULTS: Excellent percentage of vitality were obtained by mineral trioxide aggregate (MTA)-based materials and Biodentine. MTA-Angelus, ProRoot MTA, and Intermediate Restorative Material (IRM) showed the highest values for the inhibition zones when tested for S. mutans, while Biodentine showed the largest inhibition zone when tested for S. sanguis. All the materials fulfilled the requirements of the International Standard 6876, demonstrating low solubility with a weight loss of less than 3%. No significant reduction in pH value was demonstrated after 24 h. ProRoot MTA and MTA-Angelus showed the highest values of radiographic density. CONCLUSIONS: The differences showed by the root-end filling materials tested do not cover completely the ideal clinical requests.

Atomic force microscopy study of enamel remineralization.

AIM: The aim of the present in vitro study was the evaluation of two products: a CPP-ACP paste (GC Tooth Mousse, GC Corp.) and a desensitizing toothpaste (Colgate Sensitive Pro Relief, Colgate-Palmolive) on preventing enamel erosion produced by a soft drink (Coca Cola) by using Atomic Force Microscopy (AFM). METHODS: Thirty enamel specimens were assigned to 6 groups of 5 specimens each. 1: intact enamel, 2: enamel + soft drink, 3: intact enamel + Colgate Sensitive Pro Relief, 4: enamel + soft drink + Colgate Sensitive Pro Relief, 5: intact enamel + GC Tooth Mousse, 6: enamel + soft drink + GC Tooth Mousse. The surface of each specimen was imaged by AFM. The root mean-square roughness (Rrms) was obtained from the AFM images and the differences in the averaged values among the groups were analyzed by ANOVA test. RESULTS: Comparing groups 4 and 6 (soft drink + toothpastes) with group 2 (eroded enamel) a statistical difference (P<0.05) was registered, suggesting effectiveness in protecting enamel against erosion of the products investigated. CONCLUSIONS: The use of new formulation toothpastes can prevent enamel demineralization.