RESUMO
Poly(propylene carbonate) (PPC) decomposes at high temperature to release CO2. This CO2-generation temperature of PPC can be reduced down to less than 80 °C with the aid of a photoacid generator (PAG). In the present work, we demonstrate that using an additional helper component, surface plasmonic gold nanorods (GNRs), the PPC degradation reaction can also be initiated by infrared (IR) irradiation. For this purpose, a PPC-containing nanoparticle formulation was developed in which PPC-based amphiphilic block copolymers (BCPs), poly(poly(ethylene glycol) methacrylate- b-propylene carbonate- b-poly(ethylene glycol) methacrylate) (PPEGMA-PPC-PPEGMA), were self-assembled with GNRs and PAG molecules via solvent exchange. Under IR irradiation, GNRs produce heat that can cause PPC to decompose into CO2, and PAG (after UV pretreatment) catalyzes this PPC degradation process. Two PPEGMA-PPC-PPEGMA materials were used for this study: PPEGMA7.3K-PPC5.6K-PPEGMA7.3K ("G7C6G7") and PPEGMA2.1K-PPC5.6K-PPEGMA2.1K ("G2C6G2"). Addition of CTAB-coated GNRs dispersed in water to a G2C6G2 solution in DMF produced individually G2C6G2-encapsulated GNRs, whereas the same solvent exchange procedure resulted in the formation of polymer-coated GNR clusters when G7C6G7 was used as the encapsulating material. GNR/G2C6G2 NPs exhibited a surface plasmon resonance peak at 697 nm. The clustered morphology of G7C6G7-encapsulated GNRs caused a blue shift of the absorbance maximum to 511 nm. As a consequence, GNR/G2C6G2 NPs showed a greater absorbance/heat generation rate under IR irradiation than did GNR/G7C6G7 NPs. The IR-induced CO2 generation rate was about 4.2 times higher with the GNR/G2C6G2+PAG sample than that with the GNR/G7C6G7+PAG sample. Both GNR/G7C6G7+PAG and GNR/G2C6G2+PAG systems produced ultrasound contrast enhancement effects under continuous exposure to IR light for >20 min; contrast enhancement was more spatially uniform for the GNR/G2C6G2+PAG sample. These results support the potential utility of PPC as a CO2-generating contrast agent in ultrasound imaging applications.
RESUMO
Determining arterial macrophage expression is an important goal in the molecular imaging of atherosclerosis. Here, we compare the efficacy of two synthetic, high density lipoprotein (HDL) based contrast agents for magnetic resonance imaging (MRI) of macrophage burden. Each form of HDL was labeled with gadolinium and rhodamine to allow MRI and fluorescence microscopy. Either the 37 or 18 amino acid peptide replaced the apolipoprotein A-I in these agents, which were termed 37pA-Gd or 18A-Gd. The diameters of 37pA-Gd and 18A-Gd are 7.6 and 8.0 nm, respectively, while the longitudinal relaxivities are 9.8 and 10.0 (mM s)(-1). 37pA has better lipid binding properties. In vitro tests with J774A.1 macrophages proved the particles possessed the functionality of HDL by eliciting cholesterol efflux and were taken up in a receptor-like fashion by the cells. Both agents produced enhancements in atherosclerotic plaques of apolipoprotein E knockout mice of approximately 90% (n = 7 per agent) and are macrophage specific as evidenced by confocal microscopy on aortic sections. The half-lives of 37pA-Gd and 18A-Gd are 2.6 and 2.1 h, respectively. Despite the more favorable lipid interactions of 37pA, both agents gave similar, excellent contrast for the detection of atherosclerotic macrophages using MRI.
