The perovskite solar cell has commercial potential due to the low-cost of materials and manufacturing processes with cell efficiencies on par with traditional technologies. Nanomaterials have many properties that make them attractive for the perovskite devices, including low-cost inks, low temperature processing, stable material properties and good charge transport. In this feature article, the use of nanomaterials in the hole transport and electron transport layers are reviewed. Specifically, SnO2 and NiOx are the leading materials with the most promise for translation to large scale applications. The review includes a discussion of the synthesis, formulation, and processing of these nanoparticles and provides insights for their further deployment towards commercially viable perovskite solar cells.
RESUMO
A series of nickel oxide (NiOx) inks, in the perovskite antisolvent chlorobenzene (CB) containing 15% ethanol, were prepared for the fabrication of p-i-n perovskite solar cells by blade coating. The inks included triethylamine (Et3N) and alkyl xanthate salts as ligands to disperse NiOxparticle aggregates and stabilize suspension. A total of four inks were evaluated: 0X (Et3N with no alkyl xanthate), 4X (Et3N + potassiumn-butyl xanthate), 12X (Et3N + potassiumn-dodecyl xanthate), and 18X (Et3N + potassiumn-octadecyl xanthate). The inks were characterized by UV-visible spectroscopy and FT-IR spectroscopy and the resulting films analyzed by thermogravimetry and scanning electron microscopy. Devices prepared using the 0X ink resulted in a peak power conversion efficiency (PCE) of 14.47% (0.25 cm2) and 9.96% (1 cm2). The 0X devices showed no significant loss of PCE after 100 days in a nitrogen flow box. Devices prepared with inks containing alkyl xanthate ligand had lower PCE that decreased with decreasing chain length, 18X > 12X > 4X.