In this paper, we investigate the several roles that hydrogen plays in the catalytic growth of carbon nanotubes from the point of view of gas species, catalyst activation and subsequent interaction with the carbon nanotubes. Carbon nanotubes and nanofibres were grown by thermal chemical vapour deposition, using methane and a mixture of hydrogen and helium, for a range of growth temperatures and pre-treatment procedures. Long, straight carbon nanotubes were obtained at 900 °C, and although the growth yield increases with the growth temperature, the growth shifts from nanotubes to nanofibres. By introducing a helium purge as part of the pre-treatment procedure, we change the gas chemistry by altering the hydrogen concentration in the initial reaction stage. This simple change in the process resulted in a clear difference in the yield and the structure of the carbon nanofibres produced. We find that the hydrogen concentration in the initial reaction stage significantly affects the morphology of carbon fibres. Although hydrogen keeps the catalyst activated and increases the yield, it prevents the formation of graphitic nanotubes.
RESUMO
The growth of carbon nanotubes from Ni catalysts is reversed and observed in real time in a transmission electron microscope, at room temperature. The Ni catalyst is found to be Ni3C and remains attached to the nanotube throughout the irradiation sequence, indicating that C most likely diffuses on the surface of the catalyst to form nanotubes. We calculate the energy barrier for saturating the Ni3C (2-13) surface with C to be 0.14 eV, thus providing a low-energy surface for the formation of graphene planes.