RESUMO
The aim of this study was to prepare an injectable DNA-loaded nano-calcium phosphate paste that is suitable as bioactive bone substitution material. For this we used the well-known potential of calcium phosphate in bone contact and supplemented it with DNA for the in-situ transfection of BMP-7 and VEGF-A in a critical-size bone defect. 24 New Zealand white rabbits were randomly divided into two groups: One group with BMP-7- and VEGF-A-encoding DNA on calcium phosphate nanoparticles and a control group with calcium phosphate nanoparticles only. The bone defect was created at the proximal medial tibia and filled with the DNA-loaded calcium phosphate paste. As control, a bone defect was filled with the calcium phosphate paste without DNA. The proximal tibia was investigated 2, 4 and 12 weeks after the operation. A histomorphological analysis of the dynamic bone parameters was carried out with the Osteomeasure system. The animals treated with the DNA-loaded calcium phosphate showed a statistically significantly increased bone volume per total volume after 4 weeks in comparison to the control group. Additionally, a statistically significant increase of the trabecular number and the number of osteoblasts per tissue area were observed. These results were confirmed by radiological analysis. The DNA-loaded bone paste led to a significantly faster healing of the critical-size bone defect in the rabbit model after 4 weeks. After 12 weeks, all defects had equally healed in both groups. No difference in the quality of the new bone was found. The injectable DNA-loaded calcium phosphate paste led to a faster and more sustained bone healing and induced an accelerated bone formation after 4 weeks. The material was well integrated into the bone defect and new bone was formed on its surface. The calcium phosphate paste without DNA led to a regular healing of the critical-size bone defect, but the healing was slower than the DNA-loaded paste. Thus, the in-situ transfection with BMP-7 and VEGF-A significantly improved the potential of calcium phosphate as pasty bone substitution material.
Assuntos
Materiais Biocompatíveis/química , Proteína Morfogenética Óssea 7/química , Regeneração Óssea , Fosfatos de Cálcio/química , Nanoestruturas/química , Fator A de Crescimento do Endotélio Vascular/química , Animais , Substitutos Ósseos , DNA/química , Humanos , Osteoclastos/citologia , Coelhos , Tíbia/patologia , Alicerces Teciduais , Transfecção , CicatrizaçãoRESUMO
A three-layer system of nanocrystalline hydroxyapatite (first layer; 1000nm thick), silver nanoparticles (second layer; 1.5µg Ag cm-2) and calcium phosphate (third layer, either 150 or 1000nm thick) on titanium was prepared by a combination of electrophoretic deposition of silver nanoparticles and the deposition of calcium phosphate by radio frequency magnetron sputtering. Scanning electron microscopy showed that the silver nanoparticles were evenly distributed over the surface. The adhesion of multilayered coating on the substrate was evaluated using the scratch test method. The resistance to cracking and delamination indicated that the multilayered coating has good resistance to contact damage. The release of silver ions from the hydroxyapatite/silver nanoparticle/calcium phosphate system into the phosphate-buffered saline (PBS) solution was measured by atomic absorption spectroscopy (AAS). Approximately one-third of the incorporated silver was released after 3days immersion into PBS, indicating a total release time of the order of weeks. There were no signs of cracks on the surface of the coating after immersion after various periods, indicating the excellent mechanical stability of the multilayered coating in the physiological environment. An antimicrobial effect against Escherichia coli was found for a 150nm thick outer layer of the calcium phosphate using a semi-quantitative turbidity test.
Assuntos
Antibacterianos/administração & dosagem , Fosfatos de Cálcio/química , Nanopartículas Metálicas/química , Prata/química , Titânio/química , Microscopia Eletrônica de VarreduraRESUMO
Alloyed silver-gold nanoparticles were prepared in nine different metal compositions with silver/gold molar ratios of ranging from 90:10 to 10:90. The one-pot synthesis in aqueous medium can easily be modified to gain control over the final particle diameter and the stabilizing agents. The purification of the particles to remove synthesis by-products (which is an important factor for subsequent in vitro experiments) was carried out by multiple ultracentrifugation steps. Characterization by transmission electron microscopy (TEM), differential centrifugal sedimentation (DCS), dynamic light scattering (DLS), UV-vis spectroscopy and atomic absorption spectroscopy (AAS) showed spherical, monodisperse, colloidally stable silver-gold nanoparticles of ≈7 nm diameter with measured molar metal compositions very close to the theoretical values. The examination of the nanoparticle cytotoxicity towards HeLa cells and human mesenchymal stem cells (hMSCs) showed that the toxicity is not proportional to the silver content. Nanoparticles with a silver/gold molar composition of 80:20 showed the highest toxicity.
RESUMO
The antibacterial action of silver is utilized in numerous consumer products and medical devices. Metallic silver, silver salts, and also silver nanoparticles are used for this purpose. The state of research on the effect of silver on bacteria, cells, and higher organisms is summarized. It can be concluded that the therapeutic window for silver is narrower than often assumed. However, the risks for humans and the environment are probably limited.