Bilayer Anion-Exchange Membrane with Low Borohydride Crossover and Improved Fuel Efficiency for Direct Borohdyride Fuel Cell.

The development of membranes with low fuel crossover and high fuel efficiency is a key issue in direct borohydride fuel cells (DBFCs). In previous work, we produced a poly(vinyl alcohol) (PVA)-anion-exchange resin (AER) membrane with a low fuel crossover and a low fuel efficiency by introducing Co ions. In this work, a bilayer membrane was designed to improve the fuel efficiency and cell performance. The bilayer membrane was prepared by casting a PVA-AER wet gel onto the partially desiccated Co-PVA-AER gel. The bilayer membrane showed a borohydride permeability of 1.34 × 10-6 cm2·s-1, which was even lower than that of the Co-PVA-AER membrane (1.98 ×10-6 cm2·s-1) and the PVA-AER membrane (2.80 × 10-6 cm2·s-1). The DBFC using the bilayer membrane exhibited a higher fuel efficiency (37.4%) and output power (1.73 Wh) than the DBFCs using the Co-PVA-AER membrane (33.3%, 1.27 Wh) and the PVA-AER membrane (34.3%, 1.2 Wh). Furthermore, the DBFC using the bilayer membrane achieved a peak power density of 327 mW·cm-2, which was 2.14 times of that of the DBFC using the PVA-AER membrane (153 mW·cm-2). The drastic improvement benefited from the bilayer design, which introduced an interphase to suppress fuel crossover and avoided unnecessary borohydride hydrolysis.

Reconstruction of TiO2/MnO2-C nanotube/nanoflake core/shell arrays as high-performance supercapacitor electrodes.

Construction of electrodes with fast reaction kinetics is of great importance for achieving advanced supercapacitors. Herein we report a facile combined synthetic strategy with atomic layer deposition (ALD) and electrodeposition to rationally fabricate nanotube/nanoflake core/shell arrays. ALD-TiO2 nanotubes are used as the skeleton core for assembly of electrodeposited MnO2-C nanoflake shells forming a core/shell structure. Highly porous architecture and good electrical conductivity are combined in this unique core/shell structure, resulting in fast ion/electron transfer. In tests of electrochemical performance, the TiO2/MnO2-C core/shell arrays are characterized as cathode for asymmetric supecapacitors and exhibit high specific capacitance (880 F g-1 at 2.5 A g-1), excellent rate properties (735 F g-1 at 30 A g-1) and good long-term cycling stability (94.3% capacitance retention after 20 000 cycles). The proposed electrode construction strategy is favorable for fabrication of other advanced supercapacitor electrodes.