RESUMO
Experimental studies were conducted on the effects of lead oxide on the microstructure and the ferroelectric properties of lead zirconate-titanate (PZT) films obtained by the method of radio frequency (RF) magnetron sputtering of a ceramic PZT target and PbO2 powder with subsequent heat treatment. It is shown that the change in ferroelectric properties of polycrystalline PZT films is attributable to their heterophase structure with impurities of lead oxide. It is also shown that, even in the original stoichiometric PZT film, under certain conditions (temperature above 580 °C, duration greater than 70 min), impurities of lead oxide may be formed. The presence of a sublayer of lead oxide leads to a denser formation of crystallization centers of the perovskite phase, resulting in a reduction of the grain size as well as the emergence of a charge on the lower interface. The formation of the perovskite structure under high-temperature annealing is accompanied by the diffusion of lead into the surface of the film. Also shown is the effect of the lead ions segregation on the formation of the self-polarized state of thin PZT films.
RESUMO
The high dielectric constant ferroelectric-polymer nanocomposite was developed for producing the heat-resistant and chemical stable planar layers. According to the composite coatings formation conditions, the following value ranges of dielectric constant and loss factor were received: 30â»400 for dielectric constant and 0.04â»0.1 for loss tangent, accordingly. Unlike of composite components, the obtained composite material is characterized by thermo-stability of electrical parameters up to 250 °C. The dielectric frequency spectra of the composite exhibit two clearly visible peaks in contrast to the spectra of the polymer and ferroelectric ceramics. The developed composite material can be used as a built-in film capacitors material in microelectronic devices.