Effect of erosive and abrasive stress on sealing ability of different desensitizers: In-vitro study.

This in vitro study examined the sealing ability of different desensitizing agents under a chemo-mechanical stress condition. For the study, a total of 144 extracted, caries-free human third molars were used to produce 1 mm-thick dentin discs. The specimens were divided randomly into four groups: Superseal (SS), Gluma (GL), Gluma Self-etch (GS), and Tooth Coat (TC). For each group, the permeability was measured before and after applying the desensitizer, after being exposed to Coca Cola for 5 minutes, and after 3150 strokes of a brushing abrasion. The decrease in permeability after the erosive and abrasive stress was analyzed by ANOVA and Tukey post hoc test. As a result, the dentin permeability decreased significantly for all desensitizers immediately after application (p < 0.05). SS and GS showed a significant difference in permeability reduction observed immediately after application and after acid action with Coca Cola (p < 0.05). After brushing abrasion, the permeability reduction decreased significantly for all desensitizers tested in this study (p < 0.05). TC showed the largest decrease in dentinal permeability compared to that of the other desensitizers and the differences were significant after brushing abrasion (p < 0.05). All tested desensitizers were effective in reducing dentin permeability. The behavioral characteristics under erosive and abrasive stress varied according to the products used. TC exhibited excellent sealing ability among the other desensitizers.

Time of Application of Sodium Ascorbate on Bonding to Bleached Dentin.

This study examined the effects of different application times of sodium ascorbate (SA) on the bond strength of composite resin to bleached dentin. Specimens with an exposed dentin surface were divided into 3 groups according to the type of bleaching agent used: Group A, mixture of sodium perborate (SP) and distilled water (DW); Group B, mixture of SP and hydrogen peroxide (HP); control group, no bleaching. Each group was classified into 10 subgroups. Subgroups IB and DB underwent immediate bonding and delayed bonding, respectively. 10% SA was applied to 3, 5, 10, and 30 minutes and 1, 24, 48, and 72 hours, respectively. Microtensile bond strength (µTBS) was measured after restoration, and the data was analyzed by one-way ANOVA and Scheffé's test. Before restoration, the dentin surfaces were examined by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). SEM showed that most dentin surfaces were filled with crystals when SA was applied to more than 24 hours. EDS revealed peaks of calcium, carbon, oxygen, and sodium. The application of SA for 5 minutes to 48 hours or for 30 minutes to 24 hours is suggested when a mixture of SP and DW or HP is used, respectively.

Effect of Dentin Wetness on the Bond Strength of Universal Adhesives.

The effects of dentin wetness on the bond strength and adhesive interface morphology of universal adhesives have been investigated using micro-tensile bond strength (µTBS) testing and confocal laser scanning microscopy (CLSM). Seventy-two human third molars were wet ground to expose flat dentin surfaces. They were divided into three groups according to the air-drying time of the dentin surfaces: 0 (without air drying), 5, and 10 s. The dentin surfaces were then treated with three universal adhesives: G-Premio Bond, Single Bond Universal, and All-Bond Universal in self-etch or etch-and-rinse mode. After composite build up, a µTBS test was performed. One additional tooth was prepared for each group by staining the adhesives with 0.01 wt % of Rhodamine B fluorescent dye for CLSM analysis. The data were analyzed statistically using ANOVA and Tukey's post hoc tests (α = 0.05). Two-way ANOVA showed significant differences among the adhesive systems and dentin moisture conditions. An interaction effect was also observed (p < 0.05). One-way ANOVA showed that All-Bond Universal was the only material influenced by the wetness of the dentin surfaces. Wetness of the dentin surface is a factor influencing the micro-tensile bond strength of universal adhesives.