Microscopic States and the Verwey Transition of Magnetite Nanocrystals Investigated by Nuclear Magnetic Resonance.

57Fe nuclear magnetic resonance (NMR) of magnetite nanocrystals ranging in size from 7 nm to 7 µm is measured. The line width of the NMR spectra changes drastically around 120 K, showing microscopic evidence of the Verwey transition. In the region above the transition temperature, the line width of the spectrum increases and the spin-spin relaxation time decreases as the nanocrystal size decreases. The line-width broadening indicates the significant deformation of magnetic structure and reduction of charge order compared to bulk crystals, even when the structural distortion is unobservable. The reduction of the spin-spin relaxation time is attributed to the suppressed polaron hopping conductivity in ferromagnetic metals, which is a consequence of the enhanced electron-phonon coupling in the quantum-confinement regime. Our results show that the magnetic distortion occurs in the entire nanocrystal and does not comply with the simple model of the core-shell binary structure with a sharp boundary.

Fe and Co NMR studies of magnetoelectric Co2 Y-type hexaferrite BSCFAO.

The Fe3+ and Co2+ NMR spectra for Ba0.3Sr1.7Co2(Fe0.96Al0.04)12O22 (BSCFAO) and Ba0.3Sr1.7Co2Fe12O22 (BSCFO) were obtained in a zero magnetic field at a low temperature. We observed change in the enhancement effect of the NMR signals depending on the setting field, which was varied when applied along the b-axis and then turned off before the measurement was taken. The experimental results indicate that the magnetic structure changes from an alternating longitudinal cone to a transverse cone when the setting field is 250 mT. They also show that the spins of Co2+ ions together with those of Fe3+ ions constitute a part of the overall magnetic structure and that the substitution of Al3+ for Fe3+ weakens the magnetic anisotropy within the easy plane. From a comparison of the enhancement factors of the Fe3+ NMR obtained with the RF pulse applied along the a-axis and the c-axis, we found that the magnetic easy plane anisotropy is approximately 16 times greater than the anisotropy within the easy plane. No changes of the NMR spectra were observed under an electric field of 1.2 MV m-1.