Chemical method for improving both the electrical conductivity and mechanical properties of carbon nanotube yarn via intramolecular cross-dehydrogenative coupling.

Chemical post-treatment of the carbon nanotube fiber (CNTF) was carried out via intramolecular cross-dehydrogenative coupling (ICDC) with FeCl3 at room temperature. The Raman intensity ratio of the G band to the D band (IG/ID ratio) of CNT fiber increased from 2.3 to 4.6 after ICDC reaction. From the XPS measurements, the AC═C/AC-C ratio of the CNT fiber increased from 3.6 to 4.8. It is of keen interest that both the electrical conductivity and tensile strength of CNT yarn improved to 3.5 × 10(3) S/cm and 420 MPa, which is 180 and 200% higher than that of neat CNT yarn.

Defect healing of reduced graphene oxide via intramolecular cross-dehydrogenative coupling.

A chemical defect healing of reduced graphene oxide (RGO) was carried out via intramolecular cross-dehydrogenative coupling (ICDC) with FeCl3 at room temperature. The Raman intensity ratio of the G-band to the D-band, the IG/ID ratio, of the RGO was increased from 0.77 to 1.64 after the ICDC reaction. From XPS measurements, the AC=C/AC-C ratio, where the peak intensities from the C=C and C-C bonds are abbreviated as AC=C and AC-C, of the RGO was increased from 2.88 to 3.79. These results demonstrate that the relative amount of sp(2)-hybridized carbon atoms is increased by the ICDC reaction. It is of great interest that after the ICDC reaction the electrical conductivity of the RGO was improved to 71 S cm(-1), which is 14 times higher than that of as-prepared RGO (5 S cm(-1)).