Hemostatic Patches Based on Crosslinked Chitosan Films Applied in Interventional Procedures.

In this study, we manufactured biocompatible hemostatic crosslinked chitosan (CS) patches and analyzed their physicochemical and biological properties for femoral arterial puncture applications. CS is a representative hemostatic material but has some drawbacks, such as swelling, shrinkage, and brittleness. Thus, it was crosslinked via a 1-ethyl-3-(3-dimethyl aminopropyl) carbodiimide (EDC)/N-hydroxysuccinimide (NHS) coupling reaction and a nucleophilic addition reaction with citric acid (CA), glutaraldehyde (GTA), and genipin (GP) to remedy its shortcomings. The CSCA (crosslinked CS with CA/EDC), CSGTA (crosslinked CS with GTA), and CSG (crosslinked CS with GP) films showed low swelling degrees and good mechanical properties (excluding CSCA) compared with those of neat CS films. Additionally, every crosslinked CS film coated with thrombin (TB-CS) showed enhanced hemostatic ability in the whole blood clotting and activated partial thromboplastin time tests. Furthermore, the CSCA, CSGTA, and CSGP were nontoxic in an in vitro cell cytotoxicity test (3-(4,5-dimethylthiazolyl-2)-2,5-diphenyltetrazolium bromide assay) using L-929 mouse fibroblasts cells.

Mechanical Properties and Bioactivity of Polyetheretherketone/Hydroxyapatite/Carbon Fiber Composite Prepared by the Mechanofusion Process.

The main obstacles in the melt-processing of hydroxyapatite (HA) and carbon fiber (CF) reinforced polyetheretherketone (PEEK) composite are the high melting temperature of PEEK, poor dispersion of HA nanofillers, and poor processability due to high filler content. In this study, we prepared PEEK/HA/CF ternary composite using two different non-melt blending methods; suspension blending (SUS) in ethanol and mechanofusion process (MF) in dry condition. We compared the mechanical properties and bioactivity of the composite in a spinal cage application in the orthopedic field. Results showed that the PEEK/HA/CF composite made by the MF method exhibited higher flexural and compressive strengths than the composite prepared by the SUS method due to the enhanced dispersibility of HA nanofiller. On the basis of in vitro cell compatibility and cell attachment tests, PEEK/HA/CF composite by mechanofusion process showed an improvement in in vitro bioactivity and osteo-compatibility.

Novel PEEK Copolymer Synthesis and Biosafety - I: Cytotoxicity Evaluation for Clinical Application.

In this research, we synthesized novel polyetheretherketone (PEEK) copolymers and evaluated the biosafety and cytotoxicity of their composites for spinal cage applications in the orthopedic field. The PEEK copolymers and their composites were prepared through a solution polymerization method using diphenyl sulfone as a polymerization solvent. The composite of PEEK copolymer showed good mechanical properties similar to that of natural bone, and also showed good thermal characteristics for the processing of clinical use as spine cage. The results of an in vitro cytotoxicity test did not show any evidence of a toxic effect on the novel PEEK composite. On the basis of these cytotoxicity test results, the PEEK composite also proved its in vitro biosafety for application to an implantable spine cage.

In-vitro toxicity study of poly(alkylphenol) as vulcanizing agent.

In this study, cytotoxicity of various novel poly(alkylpehnol) derivatives which, one of constituent for vulcanizing agent, could be adjusted in medical elastic rubber applications were investigated under various conditions of cytotoxicity test. By MTT-assay which according to ISO 10993-5 regulation, we could figure out cell viability of mouse fibroblast in various sample conditions. Furthermore, by Live & Dead Cell assay, we could get colorimetric cell viability via fluorescence images.