Hierarchical ZnO Nanowires-loaded Sb-doped SnO2-ZnO Micrograting Pattern via Direct Imprinting-assisted Hydrothermal Growth and Its Selective Detection of Acetone Molecules.

We propose a novel synthetic route by combining imprinting transfer of a Sb-doped SnO2 (ATO)-ZnO composite micrograting pattern (MP), i.e., microstrip lines, on a sensor substrate and subsequent hydrothermal growth of ZnO nanowires (NWs) for producing a hierarchical ZnO NW-loaded ATO-ZnO MP as an improved chemo-resistive sensing layer. Here, ATO-ZnO MP structure with 3-µm line width, 9-µm pitch, and 6-µm height was fabricated by direct transfer of mixed ATO and ZnO nanoparticle (NP)-dispersed resists, which are pre-patterned on a polydimethylsiloxane (PDMS) mold. ZnO NWs with an average diameter of less than 50 nm and a height of 250 nm were quasi-vertically grown on the ATO-ZnO MP, leading to markedly enhanced surface area and heterojunction composites between each ATO NP, ZnO NP, and ZnO NW. A ZnO NW-loaded MP sensor with a relative ratio of 1:9 between ATO and ZnO (1:9 ATO-ZnO), exhibited highly sensitive and selective acetone sensing performance with 2.84-fold higher response (R air/R gas = 12.8) compared to that (R air/R gas = 4.5) of pristine 1:9 ATO-ZnO MP sensor at 5 ppm. Our results demonstrate the processing advantages of direct imprinting-assisted hydrothermal growth for large-scale homogeneous coating of hierarchical oxide layers, particularly for applications in highly sensitive and selective chemical sensors.

Uniformly embedded silver nanomesh as highly bendable transparent conducting electrode.

Ag-nanomesh-based highly bendable conducting electrodes are developed using a combination of metal nanotransfer printing and embossing for the 6-inch wafer scale. Two Ag nanomeshes, including pitch sizes of 7.5 and 10 µm, are used to obtain highly transparent (approximately 85% transmittance at a wavelength of 550 nm) and electrically conducting properties (below 10 Ω sq(-1)). The Ag nanomeshes are also distinguished according to the fabrication process, which is called transferred or embedded Ag nanomesh on polyethylene terephthalate (PET) substrate, in order to compare their stability against bending stress. Then the enhancement of bending stability when the Ag nanomesh is embedded in the PET substrate is confirmed.