The effect of Zn on pore characteristics in lotus-type porous Cu alloy was investigated. The lotustype porous Cu-Zn alloys were fabricated with Zn content from 0.01 to 0.1 at% by the centrifugal casting method. The results demonstrated that the porosity was rarely affected by Zn content. However, the average pore diameter and pore number density of the lotus type porous Cu-Zn alloys were significantly affected by the Zn content. The average pore diameter decreased as the Zn content increased up to 0.01 at%, and then increased as the Zn content increased up to 0.1 at%. In contrast, the variations in the pore number density of the lotus-type porous Cu-Zn alloys showed the reversed tendency with respect to that of the average pore diameter. The increase in heterogeneous nucleation sites for pores attributed to the decreased average pore diameter and the increased pore number density.
RESUMO
Lotus-type porous Cu-Fe and Cu-Cr with long cylindrical pores was fabricated by centrifugal casting under hydrogen atmosphere and the effect of alloying elements on pore characteristics of lotus-type porous Cu was investigated. For the lotus type porous Cu-Fe alloy, the porosity slightly decreased and the average pore diameter slightly increased with increasing Fe content. For the lotus-type porous Cu-Cr alloy, the porosity sharply decreased and the average pore diameter drastically increased with an increase in the Cr content. From these results, it was found that the pore evolution and growth are affected by alloying element and this leads to the change in the pore characteristics of lotus-type porous Cu-Fe and Cu-Cr alloys.