Tribo-Mechanical Investigation of Glass Fiber Reinforced Polymer Composites under Dry Conditions.

Tribo-mechanical experiments were performed on Glass Fiber Reinforced Polymer (GRFP) composites against different engineering materials, and the tribological behavior of these materials under dry conditions was investigated. The novelty of this study consists of the investigation of the tribomechanical properties of a customized GFRP/epoxy composite, different from those identified in the literature. The investigated material in the work is composed of 270 g/m2 fiberglass twill fabric/epoxy matrix. It was manufactured by the vacuum bag method and autoclave curing procedure. The goal was to define the tribo-mechanical characteristics of a 68.5% weight fraction ratio (wf) of GFRP composites in relation to the different categories of plastic materials, alloyed steel, and technical ceramics. The properties of the material, including ultimate tensile strength, Young's modulus of elasticity, elastic strain, and impact strength of the GFPR, were determined through standard tests. The friction coefficients were obtained using a modified pin-on-disc tribometer using sliding speeds ranging from 0.1 to 0.36 m s-1, load 20 N, and different counter face balls from Polytetrafluoroethylene (PTFE), Polyamide (Torlon), 52,100 Chrome Alloy Steel, 440 Stainless Steel, and Ceramic Al2O3, with 12.7 mm in diameter, in dry conditions. These are commonly used as ball and roller bearings in industry and for a variety of automotive applications. To evaluate the wear mechanisms, the worm surfaces were examined and investigated by a Nano Focus-Optical 3D Microscopy, which uses cutting-edge µsurf technology to provide highly accurate 3D measurements of surfaces. The obtained results constitute an important database for the tribo-mechanical behavior of this engineering GFRP composite material.

Tribological Investigation of Glass Fiber Reinforced Polymer Composites against 52100 Chrome Alloy Steel Based on ELECTRE Decision-Making Method.

Fibers play an important role when studying the tribological behavior of reinforced friction composites. The purpose of the current research is to develop a glass fiber reinforced polymer (GFRP) recipe with improved tribological properties as well as to find the composites with the optimal tribological behavior. A ball-on-disc tribometer was used to perform dry sliding friction testing, the obtained results were then analyzed with the ELECTRE (ELimination Et Choix Traduisant la REalite-elimination and choice translating the reality) method based on a utility matrix having process parameters the applied load, sliding velocity, and weight percentage of the fiber content. The ELECTRE method was chosen to find the optimal tribological parameters, with respect to more performance criteria, because it is one of the best multiple criteria decision-making methods. The optimal combination of parameters for the multi-response characteristics of the investigated friction composite was at an applied load of 10 N, a sliding velocity of 0.1 ms-1 and a 54% weight fiber content. The results showed that the addition of glass fiber (GF) content did not considerably improve the tribological behavior of the friction composites. In addition, from the nano focus-optical 3D scanning electron microscopy, images of the friction, tested friction and wear composites, plate formation, fiber-matrix delamination, fiber pull-out, and matrix cracking and damage, various wear mechanisms were identified.

Experimental Investigation of the Tribological Behaviors of Carbon Fiber Reinforced Polymer Composites under Boundary Lubrication.

Friction and wear experiments were performed on carbon fiber-reinforced polymer (CFRP) composites, and the tribological behavior of these materials under boundary lubrication (based on the 5100 4T 10 W-30 engine oil with TiO2 Degussa P25 nanoparticles) was investigated. Experiments were carried out in two directions: one at a different normal load from 6 to 16 N and one at a low sliding speed of 110 mm/min under boundary lubrication conditions. The obtained results reveal the stick-slip effect and the static and dynamic coefficient of friction decreased slightly with increasing normal applied load on the carbon fiber reinforced polymer composite pairs. The second direction highlights through experimental tests on the pin on disc tribometer that the friction coefficient increases with the increase in normal load (20-80 N) and sliding velocity (0.4-2.4 m/s). On the other hand, it is found that the friction coefficient is slightly lower than in the stick-slip phase. During the running-in process, the friction coefficient of the CFRP pair increases steadily as the rubbing time increases, and after a certain rubbing period, it remains constant regardless of the material of the counter face. The obtained results show that for the observed interval, the influence of normal load and sliding velocity have relatively small fraction coefficients and low wear depths. A 3D analysis of the profile demonstrated the texture of wear marks and tracks of these engineering composite materials. Furthermore, the height variations of wear marks and the morphologies of the worn surfaces of specimens under boundary lubrication conditions were analyzed.

Effect of TiO2 nanoparticles on the tribological properties of lubricating oil: an experimental investigation.

Nano-lubricants offer improved tribological properties in many applications, such as machines and engines. The presence of nanoparticles in the lubricating oil affects its wear, friction, thermal, chemical and physical properties in many ways. Titanium dioxide (TiO2) is a promising lubricant additive for enhanced engine efficiency. This article reports the effect of 10 W-30 pure base engine oil suspended TiO2 nanoparticles. Four different volume concentrations (0.01%, 0.025%, 0.050% and 0.075%) of TiO2 nanoparticles in the base lubricating oil are used for the analysis. The tribological tests were performed at ambient temperature as well as at 75 °C using a four ball tribometer. Scanning electron microscope (SEM) and Alicona Inginite Focus G5 microscope were used to analyze the worn surface. The results show that the surface-modified TiO2 nanoparticles can remarkably improve the load-carrying capacity, the friction reducing, and anti-wear abilities of the additive oil. The diameter of the wear trace and the coefficient of friction are the tribological properties analyzed for the nano-lubricant prepared at different volume concentration (VC). It was found that the diameter of the wear scar and the coefficient of friction increase with increasing VC of TiO2 nanoparticles in the lubricating oil. The main objective of the paper is to present the recent progress and, consequently, to develop a comprehensive understanding of the tribological behavior of engine oil mixed with TiO2 nanoparticles.