Forensic and reliability analyses of fixed dental prostheses.

This article describes the protocol for determining the cause of failure for retrieved failed implant supported fixed dental prostheses (FDPs) in a clinical study of three-unit bridges. The results of loading of flexure bars of different veneer compositions at different stress rates were presented for two veneer materials (leucite reinforced and fluorapatite glass-ceramic veneers) and a Y-TZP core zirconia ceramic used in the clinical study. From these results, the strengths of the fast loading conditions were used to determine the fracture toughness of these materials. Fractal dimension measurements of the flexure bars and selected FDPs of the same materials demonstrated that the values were the same for both the bars and the FDPs. This allowed the use of fracture toughness values from the flexure bars to determine the strengths of the FDPs. The failure analysis of clinically obtained FDP replicates to determine the size of the fracture initiating cracks was then performed. Using the information from the flexure bars and the size of the fracture initiating cracks for the failed FDPs, the strengths of the FDPs were determined. The clinical failures were determined to be most likely the result of repeated crack growth due to initial overload and continuous use after initial cracking.

Novel Coatings to Minimize Corrosion of Titanium in Oral Biofilm.

The aim of this work is to investigate the effects produced by polymicrobial biofilm (Porphyromonas gingivalis, Streptococcus mutans, Streptococcus sanguinis, and Streptococcus salivarius) on the corrosion behavior of titanium dental implants. Pure titanium disks were polished and coated with titanium nitride (TiN) and silicon carbide (SiC) along with their quarternized versions. Next, the disks were cultivated in culture medium (BHI) with P. gingivalis, S. mutans, S. sanguinis, and S. salivarius and incubated anaerobically at 37 °C for 30 days. Titanium corrosion was evaluated through surface observation using Scanning Electron Microscope (SEM) and Atomic Force Microscopy (AFM). Furthermore, the Ti release in the medium was evaluated by Inductively Coupled Plasma Mass Spectrometry (ICP-MS). SEM images showed that coated Ti disks exhibited lower corrosion compared to non-coated disks, except for the quartenized TiN. This was confirmed by AFM, where the roughness was higher in non-coated Ti disks. ICP showed that Ti levels were low in all coating disks. These results indicate that these SiC and TiN-based coatings could be a useful tool to reduce surface corrosion on titanium implant surfaces.

Titanium Corrosion in Peri-Implantitis.

Titanium (Ti) corrodes clinically in the presence of bacteria. We investigated this phenomenon as a function of Ti particles found in biopsied tissues around peri-implantitis sites and surface roughness of failed Ti implants. Tissue biopsies were surgically collected from peri-implantitis sites, processed, and embedded in resin. The resin-embedded samples were hand trimmed to the region of interest and semi-thick (500 nm) sections were collected onto coverslips. One section was toluidine blue post-stained as a reference. The remainder sections were left unstained for energy-dispersive X-ray spectroscopy (EDX) analysis. Processed samples were examined under scanning electron microscopy (SEM) and EDX. Corresponding failed implants were also removed and examined under SEM and EDX. Five out of eight biopsied samples demonstrated the presence of Ti particles in the soft tissue, suggesting the true rate among all failures was between 24.5% and 91.5% (the lower bound of a 95% confidence interval for the true rate of Ti presence). SEM analysis of failed implant bodies also indicated changes in surface morphology and appeared less detailed with decreased weight percent of Ti on the surface of the failed implants. In conclusion, Ti particles were noted in 5/8 biopsied samples. Surface morphologies were smoother in failed implants compared with the reference implant.

Effect of pH Cycling Frequency on Glass-Ceramic Corrosion.

The effect of pH changes on the chemical durability of dental glass-ceramic materials was evaluated using weight loss and ion release levels. The hypothesis that increased pH changes will exhibit greater corrosion was investigated. The ion concentration was analyzed using inductively coupled plasma atomic emission spectrometer (ICP). The surface compositions were investigated using X-ray photoelectron spectroscopy (XPS). The surface morphologies were examined using scanning electron microscopy (SEM). Dental glass-ceramics were tested in constant immersion, 3-day cycling, and 1-day cycling with pH 10, pH 2, and pH 7 for 3, 15, and 30 days. The 1-d cycling group demonstrated the highest levels of weight loss compared with 3-d cycling and constant immersion. For the ion release, Si4+ and Ca2+ had the highest rates of release in 1-d cycling, whereas the Al3+ release rate with constant pH 2 was highest. The alteration/passivation layer that was formed on the surface of disks possibly prevented further dissolution of pH 10 corroded disks. XPS analysis demonstrated different surface compositions of corroded disks in pH 10 and pH 2. Si4+, K+, Na+, Al3+, and Ca2+ were detected on the surface of corroded pH 10 disks, whereas a Si4+ and P5+-rich surface formed on corroded pH 2 disks. SEM results demonstrated rougher surfaces for corroded disks in cycling conditions and pH 2 constant immersion. In conclusion, increased pH changes significantly promote the corrosion of dental glass-ceramic materials.

Novel Coatings to Minimize Bacterial Adhesion and Promote Osteoblast Activity for Titanium Implants.

Titanium nitride (TiN) and silicon carbide (SiC) adhesion properties to biofilm and the proliferation of human osteoblasts were studied. Quaternized titanium nitride (QTiN) was produced by converting the surface nitrogen on TiN to a positive charge through a quaternization process to further improve the antibacterial efficiency. The SiC required a nitridation within the plasma chamber of the surface layer before quaternization could be carried out to produce quaternized SiC (QSiC). The antimicrobial activity was evaluated on the reference strains of Porphyromonas gingivalis for 4 h by fluorescence microscopy using a live/dead viability kit. All the coatings exhibited a lower biofilm coverage compared to the uncoated samples (Ti-85.2%; TiN-24.22%; QTiN-11.4%; SiC-9.1%; QSiC-9.74%). Scanning Electron Microscope (SEM) images confirmed the reduction in P. gingivalis bacteria on the SiC and TiN-coated groups. After 24 h of osteoblast cultivation on the samples, the cell adhesion was observed on all the coated and uncoated groups. Fluorescence images demonstrated that the osteoblast cells adhered and proliferated on the surfaces. TiN and SiC coatings can inhibit the attachment of Porphyromonas gingivalis and promote osteoblast adhesion on the titanium used for implants. These coatings may possess the ability to prevent the development of peri-implantitis and stimulate osteointegration.

Anti-Bacterial Properties and Biocompatibility of Novel SiC Coating for Dental Ceramic.

A 200 nm plasma-enhanced chemical vapor-deposited SiC was used as a coating on dental ceramics to improve anti-bacterial properties for the applications of dental prosthesis. A thin SiO2 (20 nm) in the same system was deposited first, prior to SiC deposition, to improve the adhesion between SiC to dental ceramic. Silane and methane were the precursors for SiC deposition, and the SiO2 deposition employed silane and nitrous oxide as the precursors. SiC antimicrobial activity was evaluated on the proliferation of biofilm, Streptococcus sanguinis, and Streptococcus mutans on SiC-coated and uncoated dental ceramics for 24 h. The ceramic coating with SiC exhibited a biofilm coverage of 16.9%, whereas uncoated samples demonstrated a significantly higher biofilm coverage of 91.8%, measured with fluorescence and scanning electron microscopic images. The cytotoxicity of the SiC coating was evaluated using human periodontal ligament fibroblasts (HPdLF) by CellTiter-BlueCell viability assay. After 24 h of HPdLF cultivation, no obvious cytotoxicity was observed on the SiC coating and control group; both sets of samples exhibited similar cell adhesion and proliferation. SiC coating on a ceramic demonstrated antimicrobial activity without inducing cytotoxic effects.

Novel Coating to Minimize Corrosion of Glass-Ceramics for Dental Applications.

The effect of a novel silicon carbide (SiC) coating on the chemical durability of a fluorapatite glass-ceramic veneer was investigated by examining weight loss and ion release levels. The hypothesis that this novel coating will exhibit significant corrosion resistance was tested. Inductively coupled plasma atomic emission spectrometer (ICP) was used for ion concentration determination and scanning electron microscopy (SEM) for surface morphology analyses. Samples were immersed in pH 10 and pH 2 buffer solutions to represent extreme conditions in the oral cavity. Analyses were done at 15 and 30 days. The SiC coated group demonstrated significant reduction in weight loss across all solutions and time points (p < 0.0001). Ion release analyses demonstrated either a marginally lower or a significantly lower release of ions for the SiC-coated disks. SEM analysis reveals planarization of surfaces by the SiC-coated group. The surfaces of coated samples were not as corroded as the non-coated samples, which is indicative of the protective nature of these coatings. In conclusion, SiC is a novel coating that holds promise for improving the performance of ceramic materials used for dental applications.

Retrospective analysis of survival rates of post-and-cores in a dental school setting.

STATEMENT OF PROBLEM: The clinical survival of different types of post-and-core systems requires assessment. PURPOSE: The purpose of this retrospective clinical study was to evaluate the clinical survival rate (CSR) of custom-fabricated cast metal and prefabricated (both metal- and fiber-reinforced composite resin post) post-and-cores as a function of patient- and restoration-related variables. MATERIAL AND METHODS: A retrospective analysis was conducted on electronic charts indicating that these patients had received some type of post-and-core between January 2003 and January 2018. A total of 754 records were included in the analysis based on the inclusion criteria. Data were analyzed by using the Kaplan-Meier and Cox proportional hazards analysis. RESULTS: Kaplan-Meier analysis demonstrated the mean survival time for each group to be 12.0 years for fiber-reinforced composite resin posts, 11.8 years for cast metal post-and-cores, and 10.2 years for prefabricated metal posts. Although the mean survival time differed by 1.8 years among groups, with prefabricated metal posts having a slightly higher risk of failure, this effect was not statistically significant (P=.067). The effect of post type also failed to reach significance when controlling for patient demographics and post position in a Cox proportional hazards analysis (P=.106). However, the Cox model did show that survival was associated with tooth position (P=.003), cement (P=.021), and type of restoration (P<.001). CONCLUSIONS: Analysis showed no evidence that post-and-core survival was significantly associated with 3 types of post-and-cores (custom-fabricated metal, prefabricated metal, and prefabricated fiber-reinforced composite resin). The percentage of root in the bone, tooth position, cement, and type of restoration, however, were significantly associated with survival.

Demonstration of SiO2/SiC based protective coating for dental ceramic prostheses.

SiO2/SiC coatings were deposited onto ceramics disks using plasma enhanced chemical vapor deposition. The effects of deposition pressure and gas-flow ratio on the refractive index, extinction coefficient, and SiC composition were studied. For the highest studied SiH4 to CH4 gas-flow ratio of 1.5, the refractive index increased by 17% from 2.53 (at the wavelength of 845 nm) to 2.96 (at the wavelength of 400 nm). For the lowest studied SiH4 to CH4 gas-flow ratio of 0.5, the refractive index only increased by 4% from 2.11 (at the wavelength of 845 nm) to 2.20 (at the wavelength of 400 nm). At higher deposition pressures, the variation in refractive index of the SiC coatings was significantly lower showing a slight increase from 1.93 (at a wavelength of 845 nm) to 1.96 at a wavelength of 400 nm. Except for the case of a low SiH4 to CH4 gas-flow ratio of 0.5, for light with wavelengths ≤ 650 nm, the extinction coefficient of the SiC coatings increased significantly. Light with a wavelength > 650 nm had an extinction coefficient near 0 in all cases. After annealing the sample at 400°C for 4 hours, hydrogen-related bonds broke and the stress of the film was reduced from -245 to -71 MPa. By utilizing different thicknesses of SiC, the full standard dental shade guide was matched with the ΔE of each coated disk being less than 3.3 compared to the shade guide.

Antibacterial Properties of Charged TiN Surfaces for Dental Implant Application.

The formation and characterization of positively surface charged TiN surfaces were investigated for improving dental implant survival. Surface nitrogen atoms of a traditional TiN implant were converted to a positive charge by a quaternization reaction which greatly increased the antibacterial efficiency. Ti, TiN, and quaternized TiN samples were incubated with human patient subgingival bacteria for 4 hours at 37°C in an anaerobic environment with an approximate 40% reduction in counts on the quaternized surface over traditional Ti and TiN. The samples were challenged with Streptococcus Mutans and fluorescent imaging confirmed significant reduction in the quaternized TiN over the traditional Ti and TiN. Contact angle measurement and X-Ray Photoelectron Spectroscopy (XPS) were utilized to confirm the surface chemistry changes. The XPS results found the charged quaternized nitrogen peak at 399.75 eV that is unique to the quaternized sample.

Fracture analysis of randomized implant-supported fixed dental prostheses.

OBJECTIVE: Fractures of posterior fixed dental all-ceramic prostheses can be caused by one or more factors including prosthesis design, flaw distribution, direction and magnitude of occlusal loading, nature of supporting infrastructure (tooth root/implant), and presence of adjacent teeth. This clinical study of implant-supported, all-ceramic fixed dental prostheses, determined the effects of (1) presence of a tooth distal to the most distal retainer; (2) prosthesis loading either along the non-load bearing or load bearing areas; (3) presence of excursive contacts or maximum intercuspation contacts in the prosthesis; and (4) magnitude of bite force on the occurrence of veneer ceramic fracture. METHODS: 89 implant-supported FDPs were randomized as either a three-unit posterior metal-ceramic (Au-Pd-Ag alloy and InLine POM, Ivoclar, Vivadent) FDP or a ceramic-ceramic (ZirCAD and ZirPress, Ivoclar, Vivadent) FDP. Two implants (Osseospeed, Dentsply) and custom abutments (Atlantis, Dentsply) supported these FDPs, which were cemented with resin cement (RelyX Universal Cement). Baseline photographs were made with markings of teeth from maximum intercuspation (MI) and excursive function. Patients were recalled at 6 months and 1-3 years. Fractures were observed, their locations recorded, and images compared with baseline photographs of occlusal contacts. CONCLUSION: No significant relationship existed between the occurrence of fracture and: (1) the magnitude of bite force; (2) a tooth distal to the most distal retainer; and (3) contacts in load-bearing or non-load-bearing areas. However, there was a significantly higher likelihood of fracture in areas with MI contacts only. CLINICAL SIGNIFICANCE: Because of the absence of a periodontal ligament, this clinical study demonstrates that there is a need to evaluate occlusion differently with implant-supported prostheses than with natural tooth supported prostheses. Implant supported prostheses should have minimal occlusion and lighter contacts than those supported by natural dentition. CLINICAL TRIALSGOV NO: K23 D2007-46.

Randomized clinical trial of implant-supported ceramic-ceramic and metal-ceramic fixed dental prostheses: preliminary results.

PURPOSE: The aim of this study was to determine the survival rates over time of implant-supported ceramic-ceramic and metal-ceramic prostheses as a function of core-veneer thickness ratio, gingival connector embrasure design, and connector height. MATERIALS AND METHODS: An IRB-approved, randomized, controlled clinical trial was conducted as a single-blind pilot study involving 55 patients missing three teeth in either one or two posterior areas. These patients (34 women; 21 men; age range 52-75 years) were recruited for the study to receive a three-unit implant-supported fixed dental prosthesis (FDP). Two implants were placed for each of the 72 FDPs in the study. The implants (Osseospeed, Astra Tech), which were made of titanium, were grit blasted. A gold-shaded, custom-milled titanium abutment (Atlantis, Astra Tech), was secured to each implant body. Each of the 72 FDPs in 55 patients were randomly assigned based on one of the following options: (1) A. MATERIAL: ceramic-ceramic (Yttria-stabilized zirconia core, pressable fluorapatite glass-ceramic, IPS e.max ZirCAD, and ZirPress, Ivoclar Vivadent) B. metal-ceramic (palladium-based noble alloy, Capricorn, Ivoclar Vivadent, with press-on leucite-reinforced glass-ceramic veneer, IPS InLine POM, Ivoclar Vivadent); (2) occlusal veneer thickness (0.5, 1.0, and 1.5 mm); (3) curvature of gingival embrasure (0.25, 0.5, and 0.75 mm diameter); and (4) connector height (3, 4, and 5 mm). FDPs were fabricated and cemented with dual-cure resin cement (RelyX, Universal Cement, 3M ESPE). Patients were recalled at 6 months, 1 year, and 2 years. FDPs were examined for cracks, fracture, and general surface quality. RESULTS: Recall exams of 72 prostheses revealed 10 chipping fractures. No fractures occurred within the connector or embrasure areas. Two-sided Fisher's exact tests showed no significant correlation between fractures and type of material system (p = 0.51), veneer thickness (p = 0.75), radius of curvature of gingival embrasure (p = 0.68), and connector height (p = 0.91). CONCLUSIONS: Although there were no significant associations between connector height, curvature of gingival embrasure, core/veneer thickness ratio, and material system and the survival probability of implant-supported FDPs with zirconia as a core material, the small number of fractures precludes a definitive conclusion on the dominant controlling factor.

Randomized, controlled clinical trial of bilayer ceramic and metal-ceramic crown performance.

PURPOSE: Analyzing the clinical performance of restorative materials is important, as there is an expectation that these materials and procedures will restore teeth and do no harm. The objective of this research study was to characterize the clinical performance of metal-ceramic crowns, core ceramic crowns, and core ceramic/veneer ceramic crowns based on 11 clinical criteria. MATERIALS AND METHODS: An IRB-approved, randomized, controlled clinical trial was conducted as a single-blind pilot study. The following three types of full crowns were fabricated: (1) metal-ceramic crown (MC) made from a Pd-Au-Ag-Sn-In alloy (Argedent 62) and a glass-ceramic veneer (IPS d.SIGN veneer); (2) non-veneered (glazed) lithium disilicate glass-ceramic crown (LDC) (IPS e.max Press core and e.max Ceram Glaze); and (3) veneered lithia disilicate glass-ceramic crown (LDC/V) with glass-ceramic veneer (IPS Empress 2 core and IPS Eris). Single-unit crowns were randomly assigned. Patients were recalled for each of 3 years and were evaluated by two calibrated clinicians. Thirty-six crowns were placed in 31 patients. A total of 12 crowns of each of the three crown types were studied. Eleven criteria were evaluated: tissue health, marginal integrity, secondary caries, proximal contact, anatomic contour, occlusion, surface texture, cracks/chips (fractures), color match, tooth sensitivity, and wear (of crowns and opposing enamel). Numerical rankings ranged from 1 to 4, with 4 being excellent, and 1 indicating a need for immediate replacement. Statistical analysis of the numerical rankings was performed using a Fisher's exact test. RESULTS: There was no statistically significant difference between performance of the core ceramic crowns and the two veneered crowns at year 1 and year 2 (p > 0.05). All crowns were rated either as excellent or good for each of the clinical criteria; however, between years 2 and 3, gradual roughening of the occlusal surface occurred in some of the ceramic-ceramic crowns, possibly caused by dissolution and wear of the glaze. Statistically significant differences in surface texture (p= 0.0013) and crown wear (p= 0.0078) were found at year 3 between the metal-ceramic crowns and the lithium-disilicate-based crowns. CONCLUSION: Based on the 11 criteria, the clinical performance of ceramic-ceramic crowns was comparable to that of the metal-ceramic crowns after 2 years; however, gradual roughening occurred between years 2 and 3, which resulted in differences in surface texture and wear.

Three years in vivo wear: core-ceramic, veneers, and enamel antagonists.

OBJECTIVES: Test the hypotheses that there are equivalent wear rates for enamel-versus-enamel and ceramic-versus-enamel, analyzing the in vivo wear of crown ceramics, their natural enamel antagonists, and the corresponding two contralateral teeth; and, that bite force does not correlate with the wear. METHODS: A controlled, clinical trial was conducted involving patients needing full coverage crowns opposing enamel antagonists. Bite forces were measured using a bilateral gnathodynamometer. Single-unit restorations of metal/ceramic (Argedent 62, Argen Corp/IPS d.SIGN veneer); or, core-ceramic/veneer from either, Empress2/Eris, or e.max Press core/e.max Ceram glaze (ceramics: Ivoclar Vivadent, USA) were randomly assigned, fabricated and cemented. Impressions were made of the ceramic crowns, as well as each maxillary and mandibular quadrant at one week (baseline) and one, two and three years. Resulting models were scanned (3D laser scanner). Maximum wear was calculated by superimposing baseline with annual images. RESULTS: There were a total of thirty-six crowns required for thirty-one patients. Each restoration had three associated enamel teeth: crown, (1) antagonist, (2) contralateral and (3) contralateral-antagonist. SAS PROC MIXED (α=0.05) indicated no statistical significance for mean maximum wear among crown ceramics, enamel antagonists and contralaterals. However, enamel wear was statistically significant in relation to intraoral location (p=0.04) and among years (p<0.02). Analyzed alone, the enamel contralateral-antagonist exhibited significantly greater wear (p<0.001). Considering all wear sites, there was no correlation with bite force (p=0.15). SIGNIFICANCE: The ceramics and their antagonists exhibited in vivo wear rates within the range of normal enamel. Future studies should examine the wear implications of the contralateral-antagonist enamel.

Anti-gingivitis effect of a dentifrice containing bioactive glass (NovaMin) particulate.

BACKGROUND: The objective of this pilot clinical trial was to evaluate the anti-gingivitis and anti-plaque effects of a dentifrice containing bioactive glass (NovaMin) compared with a placebo control dentifrice in a 6 weeks clinical study. METHODS: The study design was a randomized, double-blinded, controlled clinical trial. One hundred volunteers took part in the study and were matched for plaque index (PLI), gingival bleeding index (GBI), age and gender. The protocol was reviewed and approved by the Ethical Committee of the University. The subjects received a supragingival prophylaxis to remove all plaque, calculus and extrinsic stain. Following the baseline examination, subjects were instructed to brush with their assigned dentifrice and toothbrush. The PLI and GBI were determined for the baseline and 6 weeks. The data were analysed using a repeated-measures anova conducted on the two dependent measures to compare the effect between the test and control group. RESULTS: Ninety-five subjects finished the study. The results showed that the PLI (baseline=1.54, 6 weeks=1.29) and GBI (baseline=1.14, 6 weeks=0.47) were significantly reduced, respectively, over the 6 weeks period in the test group (p<0.001 for each measure). There was a 58.8% reduction in gingival bleeding and a 16.4% reduction in plaque growth. There was no difference of the PLI (baseline=1.60, 6 weeks=1.57) and GBI (baseline=1.18, 6-week=1.02) over the 6 week period in the control group. CONCLUSION: This study demonstrated that a dentifrice containing NovaMin significantly improves oral health as measured by a reduction in gingival bleeding and reduction in supragingival plaque compared with a negative dentifrice over the 6 weeks study period.

Surface treatments to improve bond strength in removable partial dentures.

The metal and resin interface of removable partial dentures is weakened by the poor bond strength between the two materials. This study was designed to test the hypothesis that surface treatments--consisting of air abrasion, with aluminum oxide, tin plating and oxidation, and silanation, either alone or in combination--will improve the bond strength of acrylic resin to metal. Statistical analysis revealed that air abrasion, tin plating/oxidation, and silanation all showed significantly higher bond strength than either abrasion and tin plating, abrasion and silanation, or abrasion alone. Air abrasion demonstrated the greatest effect on improving bond strength. The mean bond strength of samples subjected to a combination of air abrasion, tin plating and oxidation, and silanation was significantly greater than any other combination treatment.