RESUMO
This study aimed to evaluate the antibacterial effect of three final irrigation protocols and to compare their ability to remove the smear layer and debris from the root canal. Methods: Sixty-three single-rooted human teeth were inoculated with Enterococcus faecalis for 14 days. The teeth were divided into a positive control group (N = 3) and three treatment groups (N = 20) as follows: final irrigation with saline solution (control group), irrigation with 5.25% NaOCl ultrasonically activated with EndoUltra (EU), standard needle irrigation with Qmix 2in1 (Qx) and irrigation with 5.25% NaOCl activated using SiroLaser Blue (SB). The bacterial load was evaluated by analyzing the colony-forming units (CFU/mL). Selected specimens were split longitudinally and examined using scanning electron microscopy in order to determine the presence of a smear layer and debris. Statistical analyses were performed using one-way ANOVA and the Kruskal−Wallis rank-sum test. Results: Activation of NaOCl with EndoUltra or SiroLaser Blue was superior at reducing intracanal bacteria relative to standard needle irrigation with Qmix 2in1 solution (p < 0.05). Even though SiroLaser Blue showed the best results for removing the smear layer and debris, no significant differences were detected between the groups (p > 0.05). Conclusions: Final irrigation with 5.25% NaOCl ultrasonically activated using EndoUltra or SiroLaser Blue demonstrated a higher efficacy in bacterial reduction than standard needle irrigation with Qmix 2in1.
RESUMO
The aim of the present work was to prepare a series of novel restorative giomers and investigate the morphology, the physico-chemical properties (residual monomer, fluoride release), and the cytotoxicity of the new materials. The experimental giomers were prepared as light-cured pastes by blending different resin matrices comprising aromatic/aliphatic/urethane (di) methacrylates, with hybrid fillers containing pre-reacted glasses (PRGs), a radiopaque glass, and nano fluorhydroxyapatite. Polyalkenoic acids based on acrylic acid/itaconic acid/N-acryloyl -L-leucine modified or not with methacrylic groups, together with a superficially active glass, were used to prepare the PRGs. The fluoride ion release of the experimental giomers was investigated within a period of 60 days of storage in bidistilled water while using a fluoride ion selective electrode. Beautifil II commercial product was used as a reference. Cell cytotoxicity tests were done in vitro, in accordance with ISO 10993-122012 proceedings. Human dermal fibroblasts and umbilical endothelial vein cultures were used. The values that were obtained for cumulative fluoride release for all experimental giomers were higher than for the Beautifil II product, being more than twice the ones that were obtained for the commercial product after 60 days of storage in bidistilled water. The experimental biomaterials showed similar and/or better results when compared to the commercial one; this effect was maintained in all tested conditions.