Cell viability assessment and ion release profiles of GICs modified with TiO2- and Mg-doped hydroxyapatite nanoparticles.

OBJECTIVES: To assess and compare the cell viability and ion release profiles of two conventional glass ionomer cements (GICs), Fuji IX and Ketac Molar EasyMix, modified with TiO2 and Mg-doped-HAp nanoparticles (NPs). METHODS: TiO2 NPs, synthesized via a sol-gel method, and Mg-doped hydroxyapatite, synthesized via a hydrothermal process, were incorporated into GICs at a concentration of 5 wt.%. The biocompatibility of prepared materials was assessed by evaluating their effects on the viability of dental pulp stem cells (DPSCs), together with monitoring ion release profiles. Statistical analysis was performed using One-way analysis of variance, with significance level p < 0.05. RESULTS: The addition of NPs did not significantly affect the biocompatibility of GICs, as evidenced by comparable decreased levels in cell viability to their original formulations. Distinct variations in cell viability were observed among Fuji IX and Ketac Molar, including their respective modifications. FUJI IX and its modification with TiO2 exhibited moderate decrease in cell viability, while other groups exhibited severe negative effects. While slight differences in ion release profiles were observed among the groups, significant variations compared to original cements were not achieved. Fluoride release exhibited an initial "burst release" within the initial 24 h in all samples, stabilizing over subsequent days. CONCLUSIONS: The addition of NPs did not compromise biocompatibility, nor anticariogenic potential of tested GICs. However, observed differences among FUJI IX and Ketac Molar, including their respective modifications, as well as induced low viability of DPSC by all tested groups, suggest the need for careful consideration of cement composition in their biological assessments. CLINICAL SIGNIFICANCE: The findings contribute to understanding the complex interaction between NPs and GIC matrices. However, the results should be interpreted recognizing the inherent limitations associated with in vitro studies. Further research avenues could explore long-term effects, in vivo performance, and potential clinical applications.

Antibiotic Prescribing Practices in Endodontic Infections: A Survey of Dentists in Serbia.

The study goal was to provide an overview of antibiotic prescribing practices of Serbian dentists when treating endodontic infections and to disseminate the current ESE (European Society of Endodontology) recommendations to the study participants. A link to an online questionnaire was sent to 628 Serbian dentists whose email addresses were publicly available on the Internet, 158 of whom responded to the survey, resulting in a 25.16% response rate. The significance of possible associations was assessed via the Chi-squared test and Cramer's V measure of association, with p < 0.05 considered as statistically significant. According to the study findings, 55.7% of respondents prescribed a 5-day antibiotic course. Moreover, Amoxicillin 500 mg was the first-choice antibiotic for 55.1% of the respondents, followed by Clindamycin 600 mg (18.4%). For patients allergic to penicillin, 61.4% of respondents prescribed Clindamycin. Statistically significant differences emerged only in relation to acute apical abscess with systemic involvement, whereby dentists aged 46-55 were least likely to prescribe antibiotics in these clinical situations (p = 0.04). Analyses further revealed that recommendations for safe antibiotic prescribing practices were not always followed, as in certain cases, patients were given antibiotics even when this was not indicated. These findings highlight the need for additional education on responsible antibiotic use to prevent bacterial resistance.

Application of Scanning Electron Microscopy in the observation of dentin-adhesive interface.

The objective of this study was observation of the adhesive interface on original tooth samples, as well as their epoxy replicas, under SEM. A light-cure flowable composite was incrementally placed and light-polymerized in previously prepared cylindrical dentinal cavities on the buccal surfaces of extracted human third molars. After finishing procedures, impressions of the composite/dentin margin were made using polyvinylsiloxane in order to obtain accurate epoxy replicas for SEM analysis. Ultrastructural morphology of the adhesive surface was observed at high magnifications (≥1,000×) on original tooth samples, which were previously prepared to expose the part of the dentin surface, which participates in the formation of adhesive bond. SEM micrographs showed that marginal adaptation was mostly of acceptable quality. In some of the SEM micrographs of original tooth samples, marginal gap formation, and resin tag breakdown were noted, which were ascribed to polymerization shrinkage. Profound understanding of ultrastructural morphology is necessary for achieving more predictable and durable margin between composite restorations and surrounding tooth structures, and SEM analysis can serve that purpose.