The machinability of materials is highly affected by their hardness, and it affects power consumption, cutting tool life as well as surface quality while machining the component. This work deals with machining of annealed AISI 4340 alloy steel using a coated carbide tool under a dry environment. The microhardness of annealed and non-annealed workpieces was compared and a significant reduction was found in the microhardness of annealed samples. Microstructure examination of the annealed sample revealed the formation of coarse pearlite which indicated a reduction of hardness and improved ductility. A commercially CVD multilayer (TiN/TiCN/Al2O3/ZrCN) coated cemented carbide cutting tool was employed for turning quenched and tempered structural AISI 4340 alloy steel by varying machining speed, rate of feed, and depth of cut to evaluate the surface quality, machining forces, flank wear, and chip morphology. According to the findings of experiments, the feed rate possesses a high impact on surface finish, followed by cutting speed. The prominent shape of the serrated saw tooth chip was noticed at a higher cutting speed. Machined surface finish and cutting forces during turning is a function of the wear profile of the coated carbide insert. This study proves that annealing is a low-cost and economical process to enhance the machinability of alloy steel.
RESUMO
The machining of nickel-based super alloys is challenging, owing to the generation of high cutting temperatures, as well as difficulty in maintaining dimensional accuracy and minimizing surface roughness, which compels the use of cutting fluids for reducing these issues due to efficient cooling/lubrication strategies. The present work investigates the comparative performance of four cooling/lubrication techniques: dry cutting, wet, minimum quantity lubricant (MQL) and compressed-air modes in turning Nitronic 60 steel using a new-generation SiAlON ceramic inserts. Several machinability parameters were analyzed for performance evaluation. For this purpose, 16 cycles of turning trials were performed based on Taguchi's L16 orthogonal array experimental design by varying cutting conditions and lubrication modes. MQL exhibits beneficial effects as compared to the other lubrication conditions concerning low cutting force, improved surface finish, decreased cutting temperature, longer tool life, and lower white layer thickness on machined surface. Burr formation on the saw-tooth chip surface, as well as friction, greatly influenced the tool flank wear due to improper cooling and poor lubrication approach in dry, wet, and compressed-air-cooled machining environments in comparison to MQL-machining. From an economical perspective, the tool life in MQL machining improved by 11%, 72%, and 138% in the comparison with flooded, compressed-air, and dry conditions, respectively. The results of the study demonstrate that using the MQL system can help with heat extraction capability, and provide some promising outcomes.